Effect of bleaching agent on dental ceramics roughness

The aim of this study was to assess the effect of bleaching agents (10% and 16% carbamide peroxide) on the roughness of two dental ceramics in vitro, and to analyze the surface by scanning electronic microscopy (SEM). Two bleaching agents (10% and 16% / Whiteness, FGM Gel) and two microparticle feldspathic ceramics (Vita VM7 and Vita VM13) were used. Forty disks of Vita VM7 and Vita VM13 ceramic were manufactured, measuring 4mm in diameter and 4mm high, in accordance with the manufacturers’ recommendations, and were divided into 4 groups (n=10): (1) VM7 + Whiteness 10%; (2) VM7 + Whiteness 16%; (3) VM13 + Whiteness 10%; (4) VM13 + Whiteness 16%. The bleaching agent was applied for 8 hours a day for 15 days and during the intervals the test specimens were stored in distilled water at 37°C. The roughness (Ra) of the test specimens was evaluated before and after exposure to the bleaching agents using a laser roughness meter and the topographic description was analyzed by SEM. The statistical analysis of roughness data showed significant differences in the VM7 groups, using paired t-test, p=0.05 (VM7 + Whiteness 10%: p=0.002; VM7 + Whiteness 16%: p=0.001) and two-sample t-test (VM7 p=0,047), and no significant difference was found among VM13 groups. The qualitative SEM analysis showed different degrees of surface changes. The results suggest that the roughness of the tested ceramic surfaces increased after exposure to the bleaching agents.

O objetivo do estudo foi avaliar o efeito de agente clareador (10% e 16% de peroxido de carbamida) na rugosidade de duas ceramicas dentais in vitro e analisar a superficie atraves da microscopia eletronica de varredura (SEM). Foram utilizados dois agentes clareadores (10% e 16% / Whiteness, FGM Gel) e duas ceramicas feldspaticas microparticuladas (Vita VM7 e Vita VM13). Foram confeccionados quarenta discos de ceramica Vita VM7 e Vita VM13, com 4mm de diametro e 4mm de altura, de acordo com as recomendacoes do fabricante, sendo divididos em 4 grupos (n=10): G1- VM7 + Whiteness 10%, G2- VM7 + Whiteness 16%, G3- VM13 + Whiteness 10% e G4- VM13 + Whiteness 16%. O agente clareador foi aplicado por 8 horas durante 15 dias e durante os intervalos os corpos de prova (cp) ficavam armazenados em agua destilada a 37°C. A rugosidade (Ra) dos cp foi avaliada antes e apos a exposicao aos agentes clareadores utilizando o rugosimetro a laser Perthomether S8P, e a descricao topografica foi analisada no MEV. A analise estatistica na rugosidade mostrou diferenca significante entre os grupos da VM7, usando o teste pareado, p=0.05 (VM7 + Whiteness 10%: p=0.002; VM7 + Whiteness 16%: p=0.001) e nao foi encontrado diferenca estatistica para os grupos da VM13. A descricao qualitativa no SEM evidenciou alteracao nas superficies em diferentes graus. Os resultados sugeriram que as superficies das ceramicas testadas aumentaram a rugosidade apos a exposicao ao agente clareador.

Effect of different polymerization devices on the degree of conversion and the physical properties of an indirect resin composite

Polymerization of indirect resin composites (IRC) is carried out in the laboratories using special photo-polymerization devices to achieve a higher degree of conversion (DC). Such devices present variation in chambers and light output which may have consequences on the chemical and physical properties of IRCs. This study evaluated the effect of different polymerization devices on the flexural strength, Vickers microhardness and DC of an IRC. Specimens were prepared from an IRC material, Sinfony (3M ESPE), using special molds for flexural strength test (N=30) (25x2x2 mm, ISO 4049), Vickers microhardness test (N=30) (5x4 mm) and for DC (N=30) utilizing Micro-raman Spectroscopy. All specimens were submitted to initial polymerization with a Visio Alpha unit (3M ESPE) and then randomly divided into three groups (n=10/ group). Specimens in Group 1 (control) received additional polymerizations using a Visio Beta Vario device (3M ESPE), and those in Group 2 and Group 3 using Powerlux (EDG) and Strobolux (EDG) devices, respectively. DC and mechanical tests were then conducted. For the mechanical tests, the data were analyzed using ANOVA and Tukey's tests (p<0.05) and for DC, one-way ANOVA was used. Polymerization in Strobolux (Group 3) resulted in significantly lower flexural strength (MPa) values (134±27) compared to Visio Beta Vario (165±20) (Group 1) (p<0.05). The lowest microhardness values (Kg/mm2) were obtained in Group 3 (30±1) (p<0.05). DC was similar in all groups (75±1, 91±5, 85±7 % for Visio Beta Vario, Powerlux and Strobolux, respectively) (p=0.1205). The type of polymerization device may affect the flexural strength and Vickers hardness of the IRC tested. DC also seems to be affected by the type of polymerization device but the results were not significant.

As polimerizacoes de resinas compostas indiretas (RCI) sao realizadas em Laboratorio em dispositivos fotopolimerizadores especiais para que seja alcancado um maior grau de conversao (GC). Estes dispositivos apresentam variacoes nas cameras e nas lampadas polimerizadoras as quais podem gerar consequencias nas propriedades fisicas e quimicas das RCIs. Este estudo avaliou o efeito de diferentes unidades polimerizadoras na resistencia a flexao, dureza Vickers e GC de uma RCI. Amostras da RCI Sinfony (3M ESPE) foram preparadas, utilizando matrizes especiais para o teste de resistencia a flexao (N=30) (25x2x2 mm, ISO 4049), teste de microdureza Vickers (N=30) (5x4 mm) e para o GC (N=30), utilizando a espectroscopia Micro-raman. Todas as amostras foram submetidas a polimerizacao inicial na unidade Visio Alpha (3M ESPE) e em seguida elas foram divididas aleatoriamente em tres grupos (n=10/por grupo). As amostras do Gr1 (controle) tiveram sua polimerizacao final realizada na unidade Visio Beta Vario (3M ESPE), e as do Gr2 e Gr3 nas unidades Powerlux (EDG) e Strobolux (EDG), respectivamente e entao os testes mecanicos e do GC foram conduzidos. Para os testes mecanicos, os dados foram analisados utilizando a analise de Variancia (ANOVA) e o teste de Tukey (p<0.05) e ANOVA 1-fator para o GC. A polimerizacao na unidade Strobolux (Gr3) gerou valores de resistencia a flexao (MPa) significativamente inferiores (134±27) comparado a unidade Visio Beta Vario (165±20) (Gr1) (p<0.05). Os menores valores de microdureza (Kg/mm2) foram obtidos para o Gr3 (30±1) (p<0.05). O GC em todas as unidades polimerizadoras (75±1, 91±5, 85±7 % para Visio Beta Vario, Powerlux e Strobolux, respectivamente) foi semelhante entre os grupos (p=0.1205). O tipo de unidade polimerizadora afetou a resistencia a flexao e a dureza Vickers da RCI testada. O GC tambem foi afetado pelo tipo de unidade polimerizadora, mas a diferenca nao foi significativa.

Surface degradation of glass ceramics after exposure to acidulated phosphate fluoride

OBJECTIVE: This study evaluated the surface degradation effect of acidulated phosphate fluoride (APF) gel exposure on the glassy matrix ceramics as a function of time. MATERIAL AND METHODS: Disc-shaped ceramic specimens (N = 120, 10/per ceramic material) were prepared in stainless steel molds (inner diameter: 5 mm, height: 2 mm) using 6 dental ceramics: 3 indicated for ceramic-fused-to-metal (Vita Omega 900, Carmen and Vita Titankeramik), 2 for all-ceramic (Vitadur Alpha and Finesse® Low Fusing) and 1 for both types of restorations (IPS d.SIGN). The specimens were wet ground finished, ultrasonically cleaned and auto-glazed. All specimens were subjected to calculation of percentage of mass loss, surface roughness analysis and topographical description by scanning electron microscopy (SEM) before (0 min) and after exposure to 1.23 percent APF gel for 4 min and 60 min representing short- and long-term etching effect, respectively. The data were analyzed using two-way ANOVA with repeated measures and Tukey's test (a=0.05). RESULTS: Significant effect of the type of the ceramics (p=0.0000, p=0.0031) and exposure time (p=0.0000) was observed in both surface roughness and percentage of mass loss values, respectively. The interaction factor between both parameters was also significant for both parameters (p=0.0904, p=0.0258). Both 4 min (0.44±0.1 - 0.81±0.2 mm) and 60 min (0.66±0.1 - 1.04±0.3 mm) APF gel exposure created significantly more surface roughness for all groups when compared to the control groups (0.33±0.2 - 0.68±0.2 mm) (p<0.05). There were no significant differences in percentage of mass loss between the ceramics at 4 min (p>0.05) but at 60 min exposure, IPS d.SIGN showed the highest percentage of mass loss (0.1151±0.11). The mean surface roughness for Vita Titankeramik (0.84±0.2 mm) and Finesse® Low Fusing (0.74.±0.2 mm) was significantly higher than those of the other ...

Shear bond strenght between metal alloy and a ceramic system, submitted to different thermocycling immersion times

El objetivo de este estudio fue evaluar la resistencia a cizallamiento de aleaciones metálicas de Co-Cr y Ni-Cr; con un mismo tipo de cerámica, sometidos a diferentes tiempos de inmersión en el termociclaje. Sesenta especímenes fueron confeccionados de forma standarden formato cilindrico. Tres condiciones de termociclaje fueron evaluadas: sin termociclaje, 3000 ciclos (5ºC/55ºC±1) con 30s y 3.000 ciclos (5ºC/55ºC±1) con 60s de tiempo de inmersión. El ensayo de cizallamiento fue realizado en una máquina universal usando un dispositivo para concentrar la tensión en la interfase metalocerámica durante el test. La carga fue aplicada hasta que ocurra la fractura de los especimenes. La información fue estadísticamente analizada por ANOVA(two-way) y el test de Tukey (p<0,05). Los resultados no mostraron diferencia estadísticamente significante entre las combinaciones metal-porcelana. Sin embargo, ambas combinaciones metalocerámicas sometidas a 60s de tiempo de inmersión mostraron valores más bajos en comparación con los especimenes del grupo sin termociclaje. Fue concluido que el tiempo de inmersión de termociclaje de 1 minuto afectó los valores de resistencia de cizallamiento en los grupos de Ni-Cr/porcelana y Cr-Co/porcelana.

Carga imediata e restauração protética definitiva com pilares protéticos personalizados / Immediate functional loading and definitive prosthetic restoration with personal abutments

O objetivo deste caso clínico é um tratamento com reposição dos dentes 11 e 21, com fixações convencionais sob carga imediata, e restaurações protéticas definitivas com pilares personalizados com coroas do sistema Procera All Ceram, desta maneira promovendo estética, integração social e conforto.

Reabilitaçäo vestibular na criança: estudo preliminar / Vestibular rehabilitation in children: preliminary study

Forma de estudo: Clínico prospectivo. Objetivo: O estudo analisa prospectivamente os resultados da Reabilitaçäo Vestibular pelo método de Cawtorne & Cooksey em 22 crianças, portadoras de vestibulopatia periférica, associada ou näo a sintomas centrais, com idade média de 8,6 anos. Material e método: Os exames quantitativos da funçäo vestibular utilizados para quantificar a vestibulopatia foram a eletronistagmografia e a prova rotatória pendular decrescente (PRPD), mas a história clínica altamente sugestiva de processo vestibular foi considerada diagnóstica mesmo na presença de exames normais. Resultado: Os resultados apontam a Reabilitaçäo Vestibular como uma opçäo válida no tratamento das vestibulopatias na infância, uma vez que näo houve casos näo responsivos ao tratamento

Restauraçäo oclusal efetiva das próteses parafusadas sobre implantes osseointegrados / Clinical case report: effective occlusal restoration for screw retained osseointegrated implant prostheses

O objetivo deste caso clínico foi apresentar uma técnica alternativa de obturaçäo do conduto oclusal de acesso ao parafuso de retençäo das próteses parafusdas sobre implantes como também preservar a estética e a funçäo mastigatória

Nistagmo de privaçäo vértebro-basilar e doppler no diagnóstico de insuficiência vértebro-basilar / Nistagmus of vertebrobasilar privation and doppler in the diagnosis of vertebrobasilar insufficiency

Introduçäo: A insuficiência vértebro-basilar (IVB) é causa freqüente de vertigem, especialmente em idosos, que comumente sofrem de aterosclerose e espondiloartrose cervical. Nos últimos 10 anos, temos utilizado o nistagmo de privaçäo vértebro-basilar (NPVB) para diagnosticar IVB. O objetivo do nosso estudo é avaliar a utilidade do método duplex scan para detectar compressäo da artéria vertebral em pacientes com sintomas de IVB e NPVB positivo. Material e método: Um total de 21 pacientes com sintomas de IVB e NyPVB positivo foi avaliado. Exames com duplex scan (7,5 MHz, SD 800 Philips) foram realizados para avaliar as artérias vertebrais (21 pacientes) e artérias carótidas (15 pacientes). Resultados: Compressäo de artéria vertebral foi encontrada em quatro (19 por cento) pacientes: três compressöes extrínsicas e uma intrínseca. O diagnóstico foi baseado na diminuiçäo ou ausência de fluxo evidenciada pelo duplex scan após uma rotaçäo de cabeça do paciente. Conclusäo: O NPVB e relativamente freqüente em pacientes com sintomas de IVB. Apesar da história e do exame físico, o método: duplex scan mostrou poucos casos de IVB (19 por cento), o que pode ser explicado pela limitaçäo dele em avaliar regiöes anatômicas de difícil acesso, como as artérias vertebrais. Concluímos que o NPVB é mais útil que o duplex scan no diagnóstico de IVB