ABSTRACT
Analyzes of samples of stem and fiber Boehmeria nivea var. Murakami were performed to increase information on the plant and disseminate its multiple possibilities of use. The histochemical analyzes with dyes and reagents showed the presence of lignified, suberous and cutinized cell walls with Safranin in the xylem region. The presence of pectin-cellulose with Astra Blue was confirmed in the regions of fiber bundles (cortex). In all regions of the stem were identified substances such as fat and mucilage with Methylene Blue evidencing high concentrations in the regions of fiber bundles and bark (violet blue). By means of Lugol (dark brown) starches were identified in several parts of the stem with concentrations in the xylem and epidermal regions. Through analyzes by EDS it was possible to identify F, Mg, Al, Si, K and Ca with predominance of K. In the chemical analyzes of the fibers were found 71.75 of cellulose, 12.11 of hemicelluloses, 1.06 of lignin and 1.70% of ashes. The percentages of extractives soluble in hot and cold water were 5.28 and 3.12% respectively, for Ethanol-Toluene was 8.55 and NaOH (1%) 27.27%. Histochemical analyzes revealed important characteristics of the fiber and stem contributing with better knowledge of the species.
Análises de amostras de caule e de fibras Boehmeria nivea var. Murakami foram realizadas para aumentar o conhecimento da planta e difundir suas múltiplas possibilidades de uso. As análises histoquímicas com corantes e reagentes mostraram paredes celulares lignificadas, suberosas e cutinizadas com Safranina na região do xilema. Confirmou-se a presença de pectocelulose com Azul de Astra nas regiões de feixes de fibras (córtex). Em todas as regiões do caule, foram identificadas substâncias como gordura e mucilagem com Azul de Metileno, evidenciando elevadas concentrações nas regiões dos feixes de fibras e da casca (azul violeta). Por meio de Lugol (marrom escuro), foram identificados amidos em várias partes do caule com concentrações nas regiões do xilema e da epiderme. Por meio de análises de EDS, foram identificados F, Mg, Al, Si, K e Ca, com predominância do K. Nas análises químicas das fibras, foram encontrados 71,09 de celulose, 12,11 de hemiceluloses, 1,06 de lignina e 1,70% de cinzas. As porcentagens de extrativos solúveis em água quente e fria foram de 5,28 e 3,12%, respectivamente. Para o Etanol-Tolueno, foi 8,55 e para o NaOH (1%), 27,27%. As análises histoquímicas revelaram importantes características das fibras e do caule, contribuindo com melhores conhecimentos da espécie
ABSTRACT
As propriedades mecânicas por flexão estática da madeira resinada de Pinus elliottii foram avaliadas por meio de testes destrutivos e não destrutivos. Para tanto, foram confeccionados corpos de prova de 10x10x200mm3 (radial, tangencial e longitudinal), levando em consideração dois fatores: lenho (juvenil, próximo à medula e adulto, próximo à casca) e resina, isto é, corpos de prova oriundos de toras com e sem estrias de resinagem. Para a avaliação não destrutiva, utilizou-se um aparelho de ultrassom com transdutores do tipo ponto seco, em que se pode calcular a velocidade da onda ultrassônica e consequentemente o módulo de elasticidade dinâmico (ED). Para obtenção do módulo de elasticidade (MOE) e do módulo de ruptura (MOR), realizou-se o ensaio destrutivo de flexão estática de três pontos. De posse das curvas de força x deformação, calculou-se a fragilidade do material. Os resultados confirmaram que o fator lenho foi significativo para as propriedades analisadas e o fator resina, em especial, para aumento do MOR e da massa específica. A fragilidade aumentou quando analisada a madeira juvenil e o fator resina quando incluso tendeu a aumentar a fragilidade no lenho adulto. O modelo de regressão múltiplo com variáveis Dummies, proposto para estimar o MOE pelo ED, foi significativo em 1% de probabilidade de erro (r2=0,75). Os resultados apresentados no presente trabalho mostraram que os fatores lenho e resina não afetaram negativamente as propriedades mecânicas da madeira de Pinus elliottii, em que, para o segundo fator, conclui-se, de maneira geral, que a madeira serrada oriunda de toras resinadas pode não representar danos significativos quando em serviço estrutural.
The mechanical properties for static bending of Pinus elliottii tapped wood were evaluated by nondestructive and destructive tests. To achieve this, samples measuring 10x10x200mm3 (thickness, width and length) were prepared considering two factors: wood (juvenile, near to pith and mature, near to bark) and rosin, i.e., samples from logs with and without tapping grooves. The nondestructive evaluation were performed using an ultrasound equipment with dry-point transducers in order to measure the ultrasonic velocity and, consequently, the dynamic modulus of elasticity (ED). The modulus of elasticity (MOE) and the modulus of rupture (MOR) were measured through static bending tests. The wood brittleness were determined through the analysis of force x deformation plots. The results confirmed the significance of wood factor for the properties analyzed and the factor rosin, especially for MOR and density. The brittleness increased for the juvenile wood and, when included the factor rosin, this property tends to increase for the mature wood. The multiple regression model with Dummies variables proposed to estimate MOE as a function of ED was significant at 1% of probability of error (r2=0.75). Moreover, the results showed that factor wood and factor rosin did not negatively affect the mechanical properties of Pinus elliotti wood. In general, the timber from tapped logs could not represent significant damages when in structural service.
ABSTRACT
Foram avaliadas as propriedades físico-mecânicas de painéis aglomerados produzidos com diferentes proporções de madeira (Eucalyptus grandis) e bambu (Bambusa vulgaris). Os painéis foram produzidos utilizando o adesivo ureia-formaldeído com a adição de 0, 25, 50, 75 e 100% de bambu. Para cada tratamento, determinaram-se as propriedades físicas (massa específica; teor de umidade; absorção de água e inchamento em espessura após 2 e 24 horas de imersão em água) e mecânicas (flexão estática; ligação interna; e arrancamento de parafusos). Os resultados obtidos indicaram que o acréscimo das partículas de bambu proporcionou uma redução significativa na qualidade dos painéis para os parâmetros avaliados, apresentando uma maior absorção de água e uma menor resistência à flexão estática e ao arrancamento de parafuso.
It was evaluated the physical and mechanical properties of particleboard produced with different proportions of wood (Eucalyptus grandis) and bamboo (Bambusa vulgaris). The boards were produced using urea-formaldehyde adhesive with the addition of 0, 25, 50, 75 and 100% of bamboo. For each treatment were determined physical properties (specific gravity, moisture content, water absorption and thickness swelling after 2 and 24 hours water immersion) and mechanical properties (static bending, internal bond and screw withdrawal). The results indicated that the addition of particles of bamboo provided a significant reduction in the quality of panels for most parameters, showing higher water absorption and a lower resistance to static bending and screw withdrawal.