Active and Passive Application of the Phosphoric Acid on the Bond Strength of Lithium Disilicate

Abstract The objective of this study was to evaluate the effect of passive or active phosphoric acid (PA) application after hydrofluoric acid (HA) treatment on the microshear bond strength of lithium disilicate. Thirty ceramic discs were made with IPS Emax 2 (10 mm thick and 10 mm diameter). The specimens were divided into 3 groups, A: 9.6% HA application; AF: 9.6% HA application + cleaning with 37% PA in passive mode and AFF: 9.6% HA application + cleaning with 37% PA in active mode. For the microshear test, four tygons (0.9 mm diameter and 0.2 mm high) were filled with resin cement (RelyX Ultimate) and placed on the ceramic disks. After testing, the fracture modes were examined under scanning electron microscopy. Data were analyzed by one-way ANOVA and Tukey's post test (α=0.05). The bond strength values were significantly higher in Group AFF (11.0±2.5 MPa) compared with group A (8.1±2.6 MPa) (p<0.002). AF group was not statistically different (9.4±2.5 MPa) from Group A. It was concluded that the active application of 37% PA after 9.6% HA increases the microshear bond strength values between the resin cement and lithium disilicate ceramic.

Resumo O objetivo desse estudo foi avaliar o efeito da aplicação passiva ou ativa do ácido fosfórico após o tratamento com ácido hidrofluorídrico na resistência de união ao microcisalhamento entre cimento resinoso e dissilicato de lítio. Trinta discos foram confeccionados com IPS Emax 2 (10 mm de espessura e 10 mm de diâmetro). Os espécimes foram divididos em três grupos (A: aplicação do ácido hidrofluorídrico 9,6%; AF: aplicação do ácido hidrofluorídrico 9,6% + limpeza com ácido fosfórico 37% em modo passivo; AFF: aplicação do ácido hidrofluorídrico 9,6% + limpeza com ácido fosfórico 37% no modo ativo). Para o teste de microcisalhamento, quatro tygons (0,9 de diâmetro e 0,2 mm de altura) foram preenchidos com cimento resinoso (RelyX Ultimate) e dispostos sobre os discos de cerâmica. Após o teste, os modos de fratura foram examinados por microscopia eletrônica de varredura. Os dados foram analisados estatisticamente por ANOVA e pós-teste de Tukey (α=0,05). Os valores de resistência de união foram significativamente superiores para o grupo AFF (11,0±2,5 MPa), comparado ao grupo A (8,1±2,6 MPa) (p<0,002), mas este não estatisticamente diferente do grupo AF (9,4±2,5 MPa). Concluiu-se que a aplicação ativa do ácido fosfórico 37% após o uso do ácido hidrofluorídrico 9,6% aumenta a resistência de união entre o cimento resinoso e a cerâmica de dissilicato de lítio.

Influence of sandblasting distance on enamel and ceramic structure bond strength / Influência do jateamento na estrutura cerâmica e esmalte, alterando a distância na resistência de união

Objetive: The purpose of this study was to evaluate the influence of sandblasting distance on ceramic and enamelbond strength. Material & Methods: Sixtythird molars were selected, enamel surfaces were ground flat with wet 600 - 2000 grit aluminum oxide abrasive papers and polished with three, one, and one-fourth micrometer-grit diamond pastes. On hundred and twentylithium disilicate-based core ceramic discs (2 mm diameter; 1 mm thickness) were also obtained and further divided into 7 groups [Group C, no sandblasting, Group SB-E(5-10) enamel sandblasting - 5 and 10 mm of distance, Group SBC(5-10) ceramic sandblasting 5 mm and 10 mm of distance, Group SB-EC(5-10) enamel and ceramic sandblasting 5 mm and 10 mm of distance]. After treatments,shear and Atomic Force Microscopy (AFM) tests were performed.Data were analyzed by Statistic Tests of normality, one-way ANOVA and Tukey post-test (α: 0.05). Results: Group C presented the highestbond strength values(59.2 ±12.5), while group SB-E 5 mm showed the lowest values (21.7 ± 08.8) (p < 0.005). Conclusion: The use of sandblasting treatment of enamel surface at 5mm distance decreases the bonding strength to shear.

Objetivo: o objetivo do estudo foi avaliar influência do jateamento na estrutura cerâmica e esmalte sob resistência de união, mudando a distância. Materiais e Métodos: 60 terceiros molares, foram selecionados, superfícies de esmalte foram planificadas com lixa com grão 600 - 2000 lixas e polido com pastas de diamante de um grão -micrômetro. Obtidos 120 discos cerâmica em dissilicato de lítio de (2 mm de diâmetro e 1 mm de espessura), dividido em sete grupos [Grupo C, não jateamento, Grupo SB-E (5-10) esmalte jateamento 5 e 10 mm, Grupo SB -C (5-10) de jacto de areia cerâmica 5 mm e 10 mm, Grupo SB-CE (5-10) e esmalte cerâmico areação 5 milímetros e 10 mm], depois foi realizado o microcisalhamento e a microscopia de forca atômica (AFM), estatística como Teste de Normalidade , após análise de variância one-way e teste de Tukey (α: 0,05). Resultados: A força do grupo C apresentou maiores valores de resistência de união (59,2 ± 12,5), o grupo SB-E 5 mm (21,7 ± 08,8) (p < 0,005), o grupo SB-E10 (53,6 ± 14,3). Conclusão: o uso de jateamento tratamento da superfície do esmalte de 5 mm, de 20 s diminui a força de ligação de microcisalhamento.