Effect of Finish Line Design and Cement Space Thickness on the Marginal Accuracy of Monolithic Zirconia Crowns / Efeito do desenho da linha de término e da espessura do espaço de cimento na precisão marginal de coroas monolíticas de zircônia

Objective: The purpose of this study was to evaluate the effect of finish line design and cement space thickness on the marginal accuracy of monolithic zirconia crowns. Materials and methods: Thirty crowns were fabricated from translucent zirconia (inCoris TZI) using Cerec in-Lab system and divided into three main groups (10 each) according to the finish line type of the die (knife-edge, chamfer, and shoulder). Every group was divided into two subgroups (5 each) according to cement space thickness (20 and50µm). Optical impressions were taken for the dies using the Cerec scanner and cement space was set twice for every finish line design; 20 and 50 µm. The completed crowns were cemented to the dies and the marginal gap was evaluated. The collected data was statistically analyzed using Mann-Whitney U test and Kruskal-Wallis test and the significance level was set at P ≤ 0.05. Results: Regarding the marginal gap; there was no statistically significant difference between different finish line designs or between different cement space thicknesses. Conclusion: Neither finish line design nor cement space thickness has an effect on the marginal gap of inCoris TZI crowns. (AU)

Declaração do problema: A necessidade de um método minimamente invasivo de preparação de coroa única é inevitável, principalmente com dentes enfraquecidos e com alta probabilidade de irritação pulpar. Portanto, é necessária uma restauração durável e adaptada, com preparação menos invasiva da linha de término. Objetivo: O objetivo deste estudo foi avaliar o efeito do design da linha de término e da espessura do espaço de cimento na precisão marginal das coroas monolíticas de zircônia. Material e Métodos: Trinta coroas foram fabricadas a partir de zircônia translúcida (inCoris TZI) usando o sistema Cerec em laboratório, e divididas em três grupos principais (n = 10), de acordo com o tipo de linha de término da matriz (lâmina, chanfro e ombro). Cada grupo foi dividido em dois subgrupos (5 cada), de acordo com a espessura do espaço do cimento (20 e 50 µm). Impressões ópticas foram obtidas para as matrizes usando o scanner Cerec e o espaço de cimento foi definido duas vezes para cada projeto de linha de chegada: 20 e 50 µm. As coroas confeccionadas foram cimentadas nos moldes e a diferença marginal foi avaliada. Os dados coletados foram analisados estatisticamente pelo teste U de Mann-Whitney e Kruskal-Wallis e o nível de significância foi estabelecido em P ≤ 0,05. Resultados: Em relação ao gap marginal não houve diferença estatisticamente significante entre diferentes projetos de linha de acabamento ou entre diferentes espessuras de espaço de cimento. Conclusão: nem o design da linha de término, nem a espessura do espaço de cimento afetam a folga marginal das coroas inCoris TZI. (AU)

Effect of diode laser irradiation of bonding agents before curing versus standard bonding protocol on the shear bond strength between resin cement and dentin / Efeito da irradiação com laser de diodo sobre sistemas adesivos antes da cura versus protocolo de adesão padrão na resistência ao cisalhamento entre o cimento resinoso e a dentina

Objective: This study aimed to evaluate the effect of diode laser irradiation (970 nm) of a one-step self-etch adhesive (Clearfil S3 Bond/CS3B) and of the bonding agent of a two-step self-etch adhesive (Clearfil Liner Bond F/CLBF) placed on dentin before polymerization on the shear bond strength. Material and methods: Forty sound premolars were sectioned buccally to obtain flat dentin surfaces. The specimens were divided into 4 groups (n = 10): Group (OS) ­ CS3B + polymerization. Group (OS-L) ­ CS3B + laser + polymerization. Group (TS) ­ CLBF (bonding agent only) + polymerization. Group (TS-L) ­ CLBF (bonding agent only) + laser + polymerization. The diode laser was irradiated through an 8 mm bleaching tip for 10 seconds, (0.4 W, 10 Hz, 4 J). All samples were cemented to composite blocks and submitted to 4000 thermal cycles. The samples were tested for shear bond strength in a universal testing machine. Data obtained was analyzed using Twoway (ANOVA) (p < 0.05) and the Bonferroni posthoc test. Representative samples from each group were analyzed using scanning electron microscopy (SEM). Results: Group TS-L ­ (7.43 MPa) displayed statistically significant higher shear bond strength in comparison to that of group TS ­ (5.13 MPa). No statistically significant difference was found between group OS-L ­ (6.49 MPa) and group OS ­ (7.28 MPa). Group TS-L exhibited the highest resin penetration beyond the hybrid layer under SEM. Conclusions: Diode laser irradiation of a bonding agent placed on dentin without prior priming increased the bond strength to dentin and is promising as a new dentin adhesion protocol. (AU)

Objetivo: Este estudo teve como objetivo avaliar o efeito da irradiação com laser de diodo (970 nm) sobre um adesivo autocondicionante de um passo (Clearfil S3 Bond / CS3B) e de um outro adesivo autocondicionante de dois passos (Clearfil Liner Bond F / CLBF) aplicado na dentina, antes de sua polimerização, na resistência ao cisalhamento. Material e métodos: Quarenta pré-molares hígidos foram seccionados vestibularmente para obtenção de superfícies dentinárias planas. Os espécimes foram divididos em 4 grupos (n = 10): Grupo (OS) - polimerização de CS3B +. Grupo (OS-L) - laser + CS3 + polimerização. Grupo (TS) - CLBF (apenas agente de adesão) + polimerização. Grupo (TS-L) - CLBF (somente agente de adesão) + laser + polimerização. O laser de diodo foi irradiado através de uma ponta de branqueamento de 8 mm durante 10 segundos (0,4 W, 10 Hz, 4 J). Todas as amostras foram cimentadas a blocos de compósitos, submetidos a 4.000 ciclos térmicos. As amostras foram testadas quanto à resistência ao cisalhamento em uma máquina universal de ensaios. Os dados obtidos foram analisados utilizandose Two-way (ANOVA) (p < 0,05) e o teste post-hoc de Bonferroni. Amostras representativas de cada grupo foram analisadas por microscopia eletrônica de varredura (MEV). Resultados: O grupo TS-L - (7,43 MPa) apresentou resistência ao cisalhamento estatisticamente significativa maior em relação ao grupo TS (5,13 MPa). Não houve diferença estatisticamente significativa entre o grupo OS-L - (6,49 MPa) e grupo OS - (7,28 MPa). O grupo TS-L exibiu a maior penetração de resina além da camada híbrida em MEV. Conclusões: A irradiação com laser de diodo de um agente adesivo colocado sobre a dentina sem o uso prévio de primers aumentou a força de adesão à dentina e é promissora como um novo protocolo de adesão dentinária. (AU)