Desajuste vertical entre implante de hexágono interno e pilares Ucla totalmente calcináveis e com base de CoCr após a fundição pelo processo convencional / Vertical misfit between internal hexagon implants and Ucla burnout and CoCr prefabricated base abutments after conventional casting procedures

Objetivo: avaliar, por meio de um microdurômetro, o grau de desajuste na adaptação de pilares Ucla em implantes. Material e métodos: foram utilizados dez implantes de hexágono interno de plataforma regular, e seus respectivos componentes protéticos do tipo Ucla com antirrotacional, como seguem: dez pilares Ucla totalmente calcináveis e dez pilares Ucla com base de CoCr. Todos os pilares Ucla foram fundidos pelo mesmo laboratório de prótese e pelo mesmo processo laboratorial. Cada implante recebeu apenas dois pilares, que foram anexados por meio de um parafuso de titânio quadrado utilizando-se torque de 30 Ncm com torquímetro manual. Cada conjunto implante/pilar recebeu quatro marcações aleatórias em torno da circunferência, na qual foram feitas as medições do espaço existente entre as peças utilizando uma lupa estereoscópica de 100 vezes de aumento. Resultados: os resultados obtidos mostraram diferenças significativas entre os grupos submetidos ao teste Mann-Whitney (p < 0,05). Conclusão: o pilar Ucla com base de CoCr apresentou menor desajuste marginal vertical, quando comparado ao pilar Ucla totalmente calcinável, após o processo de fundição nos implantes de hexágono interno.

Objective: to evaluate, using a microhardness device, the misfit between Ucla abutments and internal hex implants. Material and methods: 10 internal hex implants received 10 Ucla burnout and 10 Ucla abutments with CoCr collar. All the abutments were cast in the same laboratory and under the same protocol. A square-head titanium screw was tightened to a 30 Ncm using a manual wrench. Each abutment/implant set receive four random markings around its perimeter. A stereoscopic lens was used to investigate the misfi t at 100 magnification. Results: there was a statistically significant difference between tested abutments (Mann-Whitney p < 0.05). Conclusion: the Ucla abutment with the CoCr collar presented less vertica misfit values after casting for internal hex dental implants.

Surface roughness of a resin composite / Rugosidade superficial de resina composta

ABSTRACT Objective: The aim of the present study was to evaluate the surface roughness (Ra) of the Z-350 resin composite following immersion in different media (distilled water, coca-cola, coffee, black tea and red wine). Methods: Fifty specimens of resin composite measuring 10 mm x 2 mm were prepared. Polymerization was performed using the conventional method (40 s). Each specimen was immersed for one hour per day. Evaluations were performed at baseline as well as after three, six, nine and 12 months. Three Ra readings were taken in opposite directions at each evaluation using a roughness meter. Mean Ra values were subjected to analysis of variance (ANOVA) followed by Tukey's test (p < 0.05). Results: A significant increase in Ra was found in the specimens submitted to coffee, coca-cola(r) and black tea between baseline and the three-month evaluation. Variance was also found among the remaining evaluation times (3 months to 12 months), but the differences did not achieve statistical significance. No statistically significant differences in Ra were found among evaluation times in the specimens submitted to red wine or distilled water. Conclusion: Based on the present findings, coca-cola, coffee and black tea exert an influence on the surface roughness of resin composites.

RESUMO Objetivo: Avaliar a rugosidade da superfície (Ra) do Z-350 resina composta após imersão em diferentes meios (água destilada, coca-cola, café, chá preto e vinho tinto). Métodos: Foram preparados cinquenta espécimes de resina composta medindo 10 mm x 2 mm. A polimerização foi realizada através do método convencional (40 s). Cada espécime foi imerso durante uma hora por dia. As avaliações foram realizadas na linha de base, bem como após três, seis, nove e 12 meses. Três leituras Ra foram levados em direções opostas em cada avaliação, utilizando um medidor de rugosidade. Os valores médios de Ra foram submetidos a análise de variância (ANOVA) seguido pelo teste de Tukey (p <0,05). Resultados: Um aumento significativo na Ra foi encontrada nas amostras submetidas ao café, coca-Cola(r) e chá preto entre o início e a avaliação de três meses. Variância também foi encontrado entre as épocas de avaliação restantes (3 meses a 12 meses), mas as diferenças não atingiram significância estatística. Não houve diferenças estatisticamente significativas na Ra encontrados entre os momentos de avaliação nos casos submetidos ao vinho tinto ou água destilada. Conclusão: Com base nos achados, coca-cola, café e chá preto exercem uma influência sobre a rugosidade superficial de resinas compostas.