ABSTRACT
OBJECTIVE@#This study aimed to compare the effects of water storage treatment and thermal cycling on the shear bond strength (SBS) of three self-adhesive dual-cure resin cements.@*METHODS@#Six cubic zirconia specimens with side length of 2 cm were obtained by cutting and sintering. Three self-adhering dual-cure resin cements (i.e., Clearfil SAC, RelyX U200, and Multilink Speed) were selected. According to their bonding modes, they were divided into three groups: direct bonding group (direct coating with resin cement), adhesive group (applying universal adhesives and then coating with resin cement), and primer group (applying Z-Prime Plus and then coating with resin cement). According to experimental conditions, each group was divided into two subgroups: subgroup a (water storage at 37 ℃ for 24 h) and subgroup b (thermalcycling for 5 000 times). SBS data were analyzed by one-way ANOVA by using SPSS 19.0 software (P0.05). After thermalcycling, the SBS of the three types of resin cements decreased (P<0.05); the SBS of the adhesive group was higher than that of the direct adhesive group and the primer group (P<0.05). Fracture mode analysis revealed that the type Ⅲ fracture mode evidently increased after the thermalcycling treatment compared with the water storage treatment.@*CONCLUSIONS@#The universal adhesives and the primer can improve the SBS of self-adhesive dual-cure resin cement in water storage at 37 ℃ for 24 h. The universal adhesives had a better bonding durability than the zirconia primer.