ABSTRACT
Abstract The purpose of this study was to evaluate the effect of dentin moisture (moist and dry) on the bonding of fiber posts to root dentin with different adhesive strategies (etch-and-rinse, self-etch, and self-adhesive). Seventy-two extracted single-rooted human teeth were endodontically treated and divided into six groups (n = 12) according to the moisture of dentin surface and adhesive systems as follows: a) etch-and-rinse/moist, b) etch-and-rinse/dry, c) self-etch/moist, d) self-etch/dry, e) self-adhesive/moist, and 6) self-adhesive/dry. The specimens were sectioned into six slices for push-out bond strength (BS), nanoleakage (NL) by SEM, and Vickers microhardness (VHN) of the resin cement. A universal testing machine (AG-I, Shimadzu Autograph) was used at a crosshead speed of 0.5 mm/min until post extrusion, with a load cell of 50 kg for evaluation of the push-out strength. Data on BS, NL, and VHN were evaluated by two-way ANOVA and Tukey's test (α = 0.05). Dentin moisture as the main factor was not significantly different for the push-out test. However, higher BS values can be observed for the etch-and-rinse group. A lower percentage of NL was found in the dry dentin groups. The moisture pattern was not significant in the hardness values for the pre-etching groups. Additional moisture did not increase the evaluated properties.
ABSTRACT
Abstract The purpose of this study was to analyze the effect of the application of different concentrations of EDTA on the adhesion of fiber posts to root dentin using self-adhesive resin cements. After endodontic treatment, 78 single roots were randomly divided into six groups (n = 13) according to the combination of the following factors: surface dentin treatment - control (distilled water), 17% EDTA and 24% EDTA; and self-adhesive resin cement - RelyX U200 (RX); and Multilink Speed (ML). After fiber post cementation, six slices were obtained for each root. Ten roots of each group were used for bond strength (BS) and three for microhardness (MH) evaluations. Data obtained from BS and MH tests for each resin cement were subjected to two-way ANOVA (surface treatment vs. root region) and to a post-hoc Tukey's test (α = 0.05). The lowest BS value was observed in the 24% EDTA group for RX cement, whereas the highest values for ML cement were observed for the control group in the middle and apical regions. In the MH test, the lowest value for RX was observed for 24% EDTA in the cervical region, whereas and the highest value for the ML cement was observed in the control group. Regarding both self-adhesive resin cements tested, the application of 24% EDTA was not able to improve the adhesion of fiber posts to root canal.