ABSTRACT
Objective@#To analyze the effect of ceramic materials thickness and resin cement shades on the final color of ceramic veneers in the discolored teeth, and to investigate the color agreement of try-in pastes to the corresponding resin cements. @*Methods@#Sixty artificial maxillary central incisor teeth (C2 shade) were used to simulate the natural discolored teeth and prepared according to veneer tooth preparation protocol. Veneers of different thickness in the body region (0.50 and 0.75 mm) were fabricated using ceramic materials (LT A2 shade, IPS e.max Press). The ceramic veneer specimens were bonded to the artificial teeth using the 6 shades of resin cements (Variolink Veneer: shades of LV-3, LV-2, HV+3; RelyX™ Veneer: shades of TR, A3, WO) (n=5). A clinical spectrophotometer was used to measure the color parameters of ceramic veneers at the cervical, body and incisal regions. Color changes of veneers before and after cementation were calculated and registered as ΔE1, and the changes between try-in paste and the corresponding resin cements were registered as ΔE2. @*Results@#Three-way ANOVA indicated that ΔE1 and ΔE2 values were significantly affected by the ceramic thickness, resin cement shades and measuring regions (P<0.05). The ΔE1 values of six shades ranged from 0.59-8.27. The ΔE1 values were more than 2.72 when the ceramic veneers were cemented with resin cements in shades of HV+3 and WO. The ΔE2 values of six shades ranged from 0.60-2.56. The shades of HV+3, WO and A3 resin cements were more than 1.60. @*Conclusions@#Different thickness of ceramic materials, resin cement shades and measuring regions could affect the final color of ceramic veneers. The color differences of some resin cements and corresponding try-in pastes might be observed in clinical practice.
ABSTRACT
<p><b>OBJECTIVE</b>To evaluate the influence of various shades of resin cements on the final color of an improved lithium-disilicate pressed glass ceramic veneers and analyze the agreement of resin cements and corresponding try-in pastes.</p><p><b>METHODS</b>Forty-eight artificial maxillary central incisor teeth were sequenced according to the measured color parameters and divided at random into 8 groups (n = 6). These artificial teeth were prepared following veneer preparation protocol. An improved lithium- disilicate pressed glass ceramic materials (IPS e.max Press, Ivoclar Vivadent) were selected as the veneer material. The shape and curvature of each veneer wax pattern were duplicated with the same impression to guarantee the similarity. The ceramic veneer specimens were delivered on the artificial teeth using the corresponding try-in pastes of 8 shades (Variolink Veneer, shades of LV-3, LV-2, MV, HV+2, HV+3; and 3M RelyXTM Veneer, shades of WO, TR, A3) and bonded with the resin cements. A clinical spectrophotometer was used to measure the color parameters of the ceramic veneers before the try-in, during the try-in procedure, and after cementation. ΔE values and C*ab values were calculated.</p><p><b>RESULTS</b>The result of one-way ANOVA indicated that the color changes of ceramic veneer cementation with resin cements were statistically significantly different in the shades of resin cements (P < 0.001). The ΔE values of ceramic veneer after cementation ranged from 0.93 to 6.79. The color changes of ceramic veneer specimens using the shades of LV-3, HV+3, WO were 3.31, 4.90 and 6.79, respectively (ΔE>3.3). The ΔE values of the ceramic veneer specimens between the resin cements and corresponding try-in pastes were from 0.72 to 1.79 (except the shade of HV+3).</p><p><b>CONCLUSIONS</b>The LV-3, HV+3, WO shades were able to change the final color of a ceramic veneer. The color of resin cements and corresponding try-in pastes achieved high agreement (except the shade of HV+3).</p>