ABSTRACT
Abstract The purpose of this study was to evaluate the color adaptation of single-shade resin composites applied to different tooth shades. A total of 108 class III preparations (n=6) were performed on the acrylic denture maxillary incisors (2mm depth and 2mm height). 5 single-shade resin composites (Vittra APS Unique, Omnichroma, ZenChroma, Clearfil Majesty ES-2 Universal, Charisma Topaz One) and 1 multishade resin composite (Estelite Asteria) were placed in the cavities and polished. I performed visual and instrumental color analyses. The CIEDE2000 formula was used to assess the shade differences (ΔE) between teeth and restorations. The obtained ΔE values were recorded and statistically analyzed. For the instrumental analysis, ZenChroma in A1 shade groups showed statistically significant higher differences (p<0.05). Among all tested materials, A3 shade groups showed lower ΔE values (p<0.05). For the visual analysis, there were no significant differences between materials and scores in A1 and A3 shade groups (p>0.05). There were statistically significant differences between the materials and the scores in A2 shade groups (p<0.05). As a result of this study, it was concluded that, making esthetic restorations with single-shade resin composites promises proper color adaptation, but their properties still need improvement. Single-shade resin composites can reduce chair-time and technical sensitivity with good color matching.
Resumen El objetivo de este estudio fue evaluar la adaptación del color de resinas compuestas omnicromáticas. Se realizaron un total de 108 preparaciones de clase III (n=6) en los incisivos superiores de prótesis acrílicas (2mm de profundidad y 2mm de altura). Se colocaron cinco resinas compuestas omnicromáticas (Vittra APS Unique, Omnichroma, ZenChroma, Clearfil Majesty ES-2 Universal, Charisma Topaz One), además de una resina multitono (Estelite Asteria) en las cavidades y se pulieron. Se realizó el análisis de color visual e instrumental. Se utilizó la fórmula CIEDE2000 para evaluar las diferencias de tono (ΔE) entre dientes y restauraciones. Los valores de ΔE obtenidos se registraron y analizaron estadísticamente. Para el análisis instrumental, ZenChroma en los grupos de color A1 mostró diferencias mayores estadísticamente significativas (p<0,05). Entre todos los materiales probados, los grupos de tonos A3 mostraron valores de ΔE más bajos (p<0.05). Para el análisis visual, no hubo diferencias significativas entre materiales y puntuaciones en los grupos de color A1 y A3 (p>0,05). Hubo diferencias estadísticamente significativas entre los materiales y las puntuaciones en los grupos de color A2 (p<0,05). Como resultado de este estudio, se concluyó que la realización de restauraciones estéticas con resinas compuestas omnicromáticas promueve una adecuada adaptación del color, pero aún necesitan mejorar sus propiedades. Las resinas compuetas omnicromáticas pueden reducir el tiempo de atención clínica y la sensibilidad técnica con una adecuada combinación de colores.
ABSTRACT
Abstract The purpose of this study was to examine the effect of different decontamination agents on the bond strength of saliva-contaminated CAD/CAM blocks and repair composite materials. Two hunderd eighty 3-mm-thick specimens were prepared from four different CAD/CAM materials: Katana Zirconia UTML disc, IPS e.max CAD block, Shofu block, and Vita Enamic block. Each material was divided into seven different subgroups (N=70). Group 1 had a clean surface. The other groups were comprised of the samples, which were contaminated with human saliva: group 2: negative control (non-cleaned); group 3: cleaned with water spray; group 4: cleaned with 70% ethanol; group 5: cleaned with Ivoclean; group 6: cleaned with Katana Cleaner; and group 7: cleaned with phosphoric acid. After the decontamination protocols, the resin composite cylinders were bonded to the CAD/CAM surfaces with a thin layer of dual-cured resin cement. The samples were stored for 24 hours at 37°C in distilled water. Then, they were subjected to a shear bond strength test (SBS). The values were recorded, and fracture types were evaluated using a microscope. Data were analyzed using two-way ANOVA and Tukey's post-hoc test. Generally, all decontaminating agents improved the SBS of composites to Katana Zirconia UTML, IPS e.max, and Vita Enamic materials (p<0.05). However, for Shofu materials, group 6 samples exhibited significantly higher bond strength values as compared with group 2 samples (p=0.026). The highest SBS values were seen in the phosphoric acid-treated group in Katana zirconia materials (26.45 ± 9.38 MPa), whereas the lowest values were seen in group 2 samples in Shofu materials (13.17±3.40 MPa). Each decontaminant agent improved the bond strength of composites to the contaminated CAD/CAM materials. If saliva is not cleaned before adhesive procedure, SBS values may decrease. All decontamination agents can be used safely on zirconia, lithium-disilicate glass-ceramic, hybrid ceramic, and polymer-infiltrated ceramic surfaces.
Resumen El propósito de este estudio fue examinar el efecto de diferentes agentes descontaminantes sobre la fuerza de unión de bloques CAD/CAM contaminados con saliva y materiales compuestos de reparación. Se prepararon doscientas ochenta muestras de 3 mm de espesor a partir de cuatro materiales CAD/CAM diferentes: disco Katana Zirconia UTML, bloque IPS e.max CAD, bloque Shofu y bloque Vita Enamic. Cada material se dividió en siete subgrupos diferentes (N=70). El grupo 1 tenía una superficie limpia. Los otros grupos estaban compuestos por muestras que estaban contaminadas con saliva humana: grupo 2: control negativo (no limpio); grupo 3: limpiado con agua pulverizada; grupo 4: limpiado con etanol al 70%; grupo 5: limpiado con Ivoclean; grupo 6: limpiado con Katana Cleaner; y grupo 7: limpiado con ácido fosfórico. Después de los protocolos de descontaminación, los cilindros de composite de resina se adhirieron a las superficies CAD/CAM con una fina capa de cemento de resina de curado dual. Las muestras se almacenaron durante 24 horas a 37°C en agua destilada. Luego, fueron sometidos a una prueba de resistencia al corte (SBS). Se registraron los valores y se evaluaron los tipos de fracturas utilizando un microscopio. Los datos se analizaron mediante ANOVA de dos factores y la prueba post-hoc de Tukey. En general, todos los agentes descontaminantes mejoraron el SBS de los composites con los materiales Katana Zirconia UTML, IPS e.max y Vita Enamic (p<0,05). Sin embargo, para los materiales Shofu, las muestras del grupo 6 exhibieron valores de fuerza de unión significativamente más altos en comparación con las muestras del grupo 2 (p=0,026). Los valores más altos de SBS se observaron en el grupo tratado con ácido fosfórico en materiales de circonio Katana (26,45 ± 9,38 MPa), mientras que los valores más bajos se observaron en las muestras del grupo 2 en materiales Shofu (13,17 ± 3,40 MPa). Cada agente descontaminante mejoró la fuerza de unión de los composites a los materiales CAD/CAM contaminados. Si no se limpia la saliva antes del procedimiento adhesivo, los valores de SBS pueden disminuir. Todos los agentes descontaminantes se pueden utilizar de forma segura en superficies de circonio, cerámica de vidrio de disilicato de litio, cerámica híbrida y cerámica con infiltraciones de polímeros.