ABSTRACT
Objective: This study evaluated the effect of root perforations on the bond strength of fiberglass posts cemented to the root canal with two adhesive systems and resin cement. Material and Methods: Forty single-rooted human teeth received endodontic treatment and were prepared for the cementation of fiberglass posts (Exacto Mini, Angelus). The teeth were divided into four experimental groups (n = 10) according to the root condition (with or without perforation) and the adhesive system used: G1: without perforation + Adper Single Bond 2 (3M ESPE), G2: without perforation + Clearfil SE Bond (Kuraray), G3: with perforation + Adper Single Bond 2, G4: with perforation + Clearfil SE Bond. The perforation was executed on the root surface with a diamond bur and sealed with white mineral trioxide aggregate (MTA). The specimens were sectioned and a push-out test was carried out (1 mm/min speed and 50 kgf). The data were statistically analyzed by ANOVA and Tukey Test (5%). Results: Adper Single Bond 2 promoted the greatest values of bond strength to the roots without root perforation. The presence of root perforation led to the reduction in bond strength values regardless of the bonding system used (p < 0.05). Conclusion: The root perforations caused a direct effect on the bond strength of the fiberglass posts cemented by reducing the bond strength values to the root dentin regardless of the adhesive system used.
Objetivo: O objetivo deste estudo foi avaliar o efeito das perfurações radiculares na resistência de união de pinos de fibra de vidro cimentados com dois sistemas adesivos e um cimento resinoso. Material e Métodos: Quarenta dentes humanos unirradiculares receberam tratamento endodôntico e foram preparados para cimentação de pinos de fibra de vidro (Exacto Mini, Angelus). Os dentes foram divididos em quatro grupos experimentais (n = 10) de acordo com a condição radicular (com ou sem perfuração) e o sistema adesivo utilizado: G1: sem perfuração + Adper Single Bond 2; G2: sem perfuração + Clearfil SE Bond; G3: com perfuração + Adper Single Bond 2; G4: com perfuração + Clearfil SE Bond. A perfuração foi realizada na superfície radicular com uma ponta diamantada e selada com agregado de trióxido mineral branco (MTA). Os espécimes foram seccionados para realização do teste de extrusão por cisalhamento (Push-out) com velocidade de 1 mm/ min e célula de carga de 50 Kgf. Os dados obtidos foram submetidos à Análise de Variância (ANOVA) e Teste de Tukey a 5%. Resultados: O sistema adesivo Adper Single Bond 2 promoveu os maiores valores de resistência de união nas raízes sem perfuração radicular. A presença de perfuração promoveu redução nos valores de resistência de união, independentemente do sistema adesivo utilizado (p < 0,05). Conclusão: As perfurações radiculares causaram efeito direto sobre a resistência de união dos pinos de fibra de vidro, promovendo redução nos valores da resistência de união independentemente do tipo de sistema adesivo utilizado.
Subject(s)
Humans , Cementation , Dental Cements , Dentin-Bonding AgentsABSTRACT
O objetivo deste estudo foi avaliar o conhecimento e comportamento dos pacientes em atendimento nas clínicas de Endodontia e Dentística da Faculdade de Odontologia de São José dos Campos sobre cárie, doença periodontal e higiene bucal, por meio de um questionário específico e, após avaliação, orientar os participantes da pesquisa. Foram avaliados 430 pacientes adultos com idade entre 18 e 80 anos e os dados obtidos submetidos à análise estatística descritiva. Os resultados mostraram que 72% dos pacientes eram do gênero feminino, sendo predominante a faixa etária entre 41 a 50 anos. Verificou-se que os participantes com maior nível de escolaridade apresentaram mais conhecimento sobre cárie e doença periodontal. Escova e dentifrício foram os recursos mais utilizados para higienização bucal por 56,05% dos entrevistados. A presença de dor (53,03%) foi o fator que motivou a procura pelo atendimento odontológico, enquanto 46,97% foram motivados por atitude preventiva (consulta de rotina). O fio dental é utilizado por 43,95% dos entrevistados, sendo que 46,05% não o utilizamalegando que o mesmo provoca sangramento gengival. Pôde-se concluir que os pacientes avaliadosapresentaram nível de conhecimento desigual sobre cárie, doença periodontal e higiene bucal. O nível de escolaridade teve influência direta sobre o conhecimento e o comportamento dos pacientes em relação às principais doenças da boca. Existe a necessidade contínua de orientação sobre as medidas preventivas para cárie e doença periodontal, ressaltando o papel da dieta e da utilização do fio dental nos programas educativos.
Subject(s)
Humans , Male , Female , Adult , Middle Aged , Behavior , Dental Caries , Knowledge , Oral Health , Oral Hygiene , Periodontics , Social Class , ToothbrushingABSTRACT
O objetivo deste estudo foi avaliar o efeito das perfurações radiculares na resistência adesiva de pinos de fibra de vidro cimentados com dois cimentos resinosos à dentina intra-radicular. Quarenta dentes humanos unirradiculares hígidos receberam tratamento endodôntico e foram preparados para a cimentação de pinos de fibra de vidro (Exacto Mini, Angelus). Os dentes foram divididos em 4 grupos experimentais (n=10) de acordo com a condição radicular (perfuração presente ou ausente) e o cimento resinoso utilizado: G1: perfuração ausente + cimento Rely X U100 (3M ESPE); G2: perfuração ausente + Panavia F2.0 (Kuraray); G3: perfuração presente + Rely X U100 (3M ESPE); G4: perfuração presente + Panavia F2.0 (Kuraray). A perfuração foi realizada na superfície radicular com ponta diamantada e selada com agregado de trióxido mineral branco (MTA). Os espécimes foram seccionados para a realização do teste de extrusão por cisalhamento (Push-out) com velocidade de 1mm/min. e célula de carga de 50kgf. Os dados obtidos foram submetidos à Análise de Variância e ao Teste de Tukey (5%). Pôde-se verificar que o cimento resinoso Rely X U100 promoveu os maiores valores de resistência adesiva, independentemente da presença ou não de perfuração radicular; e, ainda, que a presença de perfuração promoveu redução nos valores de resistência adesiva dos cimentos resinosos. Concluiu-se que a presença de perfuração radicular teve efeito direto sobre a resistência adesiva dos pinos de fibra de vidro e dos cimentos resinosos, promovendo redução nos valores de resistência adesiva à dentina intra-radicular
The objective of this paper is to present evaluation of the effect of root perforations on the adhesive resistance (or bond strength) of fiberglass pins bonded by two resin cements over the intra-root dentin.. Forty human and sound one--root teeth were subject to endodontic treatment and prepared for having fiberglass pins cemented to them (Exacto Mini, Angelus). The teeth were divided into four experimental groups (n=10), according to the root condition (with or without perforations) and to the resin cement: G1, no perforation, cement Rely X U100 (3M ESPE); G2: no perforation+ Panavia F2.0 (Kuraray); G3,: existing perforation + Rely X U100 (3M ESPE); G4: existing perforation+ Panavia F2.0 (Kuraray). Perforation was performed on the root surface with diamond tip and sealed with white mineral trioxide aggregate (MTA). The samples were sectioned and a push out test was performed (1mm/minute speed, 50 kgf). The obtained data was submitted to statistical analysis and Tukey test (5%).It was found that the resin cement Rely X U100 caused the highest levels of adhesive resistance regardless of the root perforation and also that perforation produced a reduction of the adhesive resistance of resin cement. The conclusion was that root perforation had a direct effect over the adhesive resistance of fiberglass pins and of resin cement and also produced a reduction in the values of adhesive resistance to the intra-root dentin
Subject(s)
Humans , Cementation , Dental Cements , Dentin-Bonding AgentsABSTRACT
Introdução: A população brasileira apresenta alta prevalência de hipertensão arterial (HA), porém a ausência de sintomas muitas vezes leva ao diagnóstico tardio e ao surgimento de comorbidades. Objetivo: Determinar a prevalência de hipertensão arterial e de seus fatores de risco na clínica de cirurgia odontológica da Universidade Federal de Juiz de Fora. Métodos: A amostra foi constituída de 146 pacientes que foram submetidos a uma anamnese para análise dos fatores de risco e a três mensurações de pressão arterial (PA), com intervalos de dois minutos entre elas. Posteriormente, calcularam-se as médias da PA sistólica (PAS) e PA distólica (PAD) destas medidas. O paciente com valor médio da PAS≥140mmHg e/ou PAD≥90mmHg foi avaliado em mais duas sessões com intervalo de uma semana entre elas; o paciente com PAS<140mmHg e PAD<90mmHg, foi considerado com valores aceitáveis de PA. Resultados: Dos 146 pacientes, 36,3% eram hipertensos, 13,7% não diagnosticados e 22,6% faziam uso de medicação, destes apenas 5% estavam controlados. Dentre os fatores de risco avaliados, os mais prevalentes foram história familiar de hipertensão arterial (78%), sedentarismo (75%) e tabagismo (32%). Conclusão: Na amostra estudada, foi observada alta prevalência de hipertensão arterial e de alguns de seus fatores de risco. Este estudo demonstra a importância da avaliação da PA previamente ao procedimento odontológico.
Introduction: The Brazilian population has a high prevalence of hypertension (HA), but the absence of symptoms often leads to late diagnosis and the emergence of comorbidities. Objective: The objective of this study was to determine the prevalence of hypertension in patients who were under treatment at the Surgery dentistry clinic at the Juiz de Fora Federal University. Methods: The sample consisted of 146 patients that were submitted an interview and three measures of the blood pressure with two minutes interval between them. The mean value of systolic blood pressure and diastolic blood pressure of these three measures were calculated. The patients who presented a mean value of sistolic blood pressure ≥ 140 mmHg and/or the diastolic blood pressure ≥ 90 mmHg were evaluated in more two sessions with an interval of one week between them. Results: From the 146 patients evaluated, 36,3% were hypertensive, 13,7% patients whom presented alterations in blood pressure were not aware about their condition, 22,6% took medication, and just 5% of them presented the blood pressure under control. From the risk factors evaluated, the most prevalent were history family of hypertension (78%), sedentarily (75%), smokers (32%). Conclusions: In the sample studied was observed high prevalence of hypertension and of some of its risk factors. This study shows the importance of the evaluation of the blood pressure before the dental procedure.
Subject(s)
Humans , Oral Surgical Procedures , Hypertension/diagnosis , Hypertension/epidemiology , Brazil , Blood Pressure Monitors , Prevalence , Risk FactorsABSTRACT
o objetivo deste estudo foi avaliar in vitro os valores de pH do meio externo após a realização do clareamento interno utilizando o peróxido de hidrogênio a 30% e diferentes associações de perborato de sódio. Foram utilizados 50 prémolares humanos, distribuídos aleatoriamente em cinco grupos, de acordo com o agente clareador utilizado para o clareamento interno desses dentes: a) água destilada; b) perborato de sódio com água destilada (2g/ml); c) perborato de sódio com peróxido de carbamida 10% (2g/ml); d) perborato de sódio com peróxido de hidrogênio 30% (2g/ml); e) peróxido de hidrogênio 30%. Foi realizada a abertura coronária, obturação do canal radicular, confecção de um tampão cervical com cimento de ionômero de vidro modificado por resina (Vitremer-3M/ESPE), e, posteriormente, a inserção do agente clareador. Os dentes foram armazenados em potes plásticos com água destilada, utilizando um dispositivo mecânico. A mensuração do pH do meio (água destilada) foi realizada imediatamente e 7 dias após a inserção dos agentes clareadores. Os dados obtidos foram submetidos a ANOVA dois fatores e Teste de Tukey a 5%. Os resultados deste estudo confirmaram a alcalinidade das associações de perborato de sódio e a acidez do peróxido de hidrogênio a 30% no período inicial. Considerando os resultados obtidos, pode-se concluir que os agentes clareadores utilizados modificaram o pH do meio externo em um período de 7 dias.
The present in vitro study evaluated the pH values of extraradicular medium after intracoronal bleaching with 30%hydrogen peroxide or 10% carbamide peroxide and different associations of sodium perborate. The study was composed of 50 extracted human premolars, randomly divided into five groups, according to the bleaching agent employed for intracoronal bleaching of these teeth: a) distilled water; b) sodium perborate with distilled water (2g/ml); c) sodium perborate with 10% carbamide peroxide (2g/ml); d) sodium perborate with 30% hydrogen peroxide (2g/ml); e) 30% hydrogen peroxide. Coronal access was performed, followed by root canal filling, confection of a cervical intermediate base with resin-modified glass ionomer cement (Vitremer-3M/ESPE) and application of the bleaching agents. The teeth were stored in plastic flasks containing distilled water, using a mechanical device. Measurement of pH of the extraradicular medium (distilled water) was performed immediately and 7 days after insertion of the bleaching agents. The pH values were analysed using the two-way ANOVA and Tukey,s test at significance level of 5%. The results of the present study confirmed the alkalinity of associations of sodium perborate and the acidity of 30% hydrogen peroxide at the immediateperiod. Considering the results achieved, it can be concluded that the bleaching agents employed changed the pH of theextraradicular medium at 7-day period.
Subject(s)
Humans , Hydrogen Peroxide , Tooth Bleaching , Hydrogen-Ion Concentration , Tooth, NonvitalABSTRACT
The present in vitro study evaluated the pH values of extraradicular medium after intracoronal bleaching with 30% hydrogen peroxide or 10% carbamide peroxide and different associations of sodium perborate. The study was composed of 50 extracted human premolars, randomly divided into five groups, according to the bleaching agent employed for intracoronal bleaching of these teeth: a) distilled water; b) sodium perborate with distilled water (2g/ml); c) sodium perborate with 10% carbamide peroxide (2g/ml); d) sodium perborate with 30% hydrogen peroxide (2g/ml); e) 30% hydrogen peroxide. Coronal access was performed, followed by root canal filling, confection of a cervical intermediate base with resin-modified glass ionomer cement (Vitremer-3M/ESPE) and application of the bleaching agents. The teeth were stored in plastic flasks containing distilled water, using a mechanical device. Measurement of pH of the extraradicular medium (distilled water) was performed immediately and 7 days after insertion of the bleaching agents. The pH values were analysed using the two-way ANOVA and Tukey's test at significance level of 5%. The results of the present study confirmed the alkalinity of associations of sodium perborate and the acidity of 30% hydrogen peroxide at the immediateperiod. Considering the results achieved, it can be concluded that the bleaching agents employed changed the pH of the extraradicular medium at 7-day period.
O objetivo deste estudo foi avaliar in vitro os valores de pH do meio externo após a realização do clareamento interno utilizando o peróxido de hidrogênio a 30% e diferentes associações de perborato de sódio. Foram utilizados 50 prémolares humanos, distribuídos aleatoriamente em cinco grupos, de acordo com o agente clareador utilizado para o clareamento interno desses dentes: a) água destilada; b) perborato de sódio com água destilada (2g/ml); c) perborato de sódio com peróxido de carbamida 10% (2g/ml); d) perborato de sódio com peróxido de hidrogênio 30% (2g/ml); e) peróxido de hidrogênio 30%. Foi realizada a abertura coronária, obturação do canal radicular, confecção de um tampão cervical com cimento de ionômero de vidro modificado por resina (Vitremer-3M/ESPE), e, posteriormente, a inserção do agente clareador. Os dentes foram armazenados em potes plásticos com água destilada, utilizando um dispositivo mecânico. A mensuração do pH do meio (água destilada) foi realizada imediatamente e 7 dias após a inserção dos agentes clareadores. Os dados obtidos foram submetidos a ANOVA dois fatores e Teste de Tukey a 5%. Os resultados deste estudo confirmaram a alcalinidade das associações de perborato de sódio e a acidez do peróxido de hidrogênio a 30% no período inicial. Considerando os resultados obtidos, pode-se concluir que os agentes clareadores utilizados modificaram o pH do meio externo em um período de 7 dias.
Subject(s)
Humans , Hydrogen Peroxide , Tooth Bleaching , Hydrogen-Ion Concentration , Tooth, NonvitalABSTRACT
The aim of this study was to determine the effect of the exposure of different endodontic materials to different dye solutions by evaluating the optical density of the dye solutions. Seventy-five plastic tubes were filled with one of the following materials: AH Plus, Sealapex, Portland cement, MTA (Angelus and Pro Root) and fifteen control plastic tubes were not. Each specimen of material and control was immersed in a container with 1 ml of each dye solution. A 0.1 ml-dye solution aliquote was removed before immersion and after 12, 24, 48 and 72 hours of each specimen immersion to record its optical density (OD) in a spectrophotometer. Statistical analysis was performed with ANOVA and Tukey tests (5 percent). No significant difference was found among any of the solution OD values for AH Plus cement. Portland cement promoted different OD values after 12 hours of immersion. MTA-Angelus cement presented different OD values only for 2 percent rhodamine B and the MTA-Pro Root cement presented different OD values in all 2 percent rhodamine B samples. Sealapex cement promoted a reduction in the India Ink OD values. Dye evaluation through OD seems to be an interesting method to select the best dye solution to use in a given marginal leakage study.
Subject(s)
Coloring Agents/chemistry , Dental Leakage/diagnosis , Methylene Blue/chemistry , Root Canal Filling Materials/chemistry , Analysis of Variance , Dental Cements , Hydrogen-Ion Concentration , Materials Testing , Spectrophotometry/methods , Time FactorsABSTRACT
O objetivo deste trabalho foi avaliar a densidade óptica das soluções corantes azul de metileno 2% tamponada e nãotamponada, rodamina B 2% tamponada e não tamponada, antes e após a imersão de dois materiais retrobturadores por diferentes períodos de tempo. As soluções corantes, sem a imersão dos espécimes, foram analisadas nos períodos de 0,12, 24, 48 e 72 horas. Foram preparados oitenta espécimes de cimento Sealer 26 e oitenta de cimento de Portland, os quais foram imersos em 0,7 ml de cada uma das soluções corantes e avaliados nos períodos de tempo de 12, 24, 48 e 72 horas. A densidade óptica foi avaliada em espectrofotômetro ajustado em 596nm para o azul de metileno e 566nmpara a rodamina B. Os dados obtidos foram analisados através dos testes ANOVA (3 fatores) e Tukey 5%. Os resultados mostraram que houve diferença estatisticamente significativa nos valores da densidade óptica do azul de metileno 2% tamponado após a imersão do Sealer 26 nos períodos de 24, 48 e 72 horas em relação ao tempo de 12 horas. Houve diferença estatisticamente significativa nos valores da densidade óptica da rodamina B 2% tamponada após a imersão do cimento de Portland nos períodos de 12, 24 e 48 horas em relação ao tempo de 72 horas. Pôde-se verificar que as soluções corantes não tamponadas apresentaram valores menores de densidade óptica. Dentre as soluções corantes analisadas,a rodamina B 2% tamponada apresentou comportamento mais estável quanto aos valores de densidade ópticaaté o período de avaliação de 48 horas.
Subject(s)
Coloring Agents , Dental Materials , Root Canal Filling Materials , Analysis of Variance , Methylene Blue , RhodaminesABSTRACT
O objetivo deste estudo foi avaliar o selamento de ápices radiculares tratados com diferentes agentes desmineralizantes e retrobturados com agregado de trióxido mineral (MTA), mediante infiltração marginal por corante. Cinqüenta e seis dentes unirradiculares humanos extraídos foram instrumentados, obturados e seccionados apicalmente. Os preparos cavitários apicais foram confeccionados com pontas ultra-sônicas e os agentes desmineralizantes foram aplicados previamente à retrobturação com Pro Root MTA. Os espécimes foram divididos aleatoriamente em 4 grupos (n=14): grupo 1 (sem agente desmineralizante); grupo 2 (ácido fosfórico 35% durante 15 s); grupo 3 (solução de EDTA 17%, pH 7, durante 3 min); grupo 4 (gel de EDTA 24%, pH 7, durante 4 min). A extensão da infiltração de corante (rodamina B 2% a 37°C, por 24 h) foi avaliada em milímetros utilizando-se um estereomicroscópio. Os resultados foram analisados estatisticamente por meio de análise de variância a um critério e do teste Tukey com nível de significância de 5%. Dentre os grupos experimentais, a menor extensão de infiltração do corante foi verificada no grupo 1 (1,89 mm), seguido pelos grupos 2 (2,18 mm), 4 (2,54 mm) e 3 (2,64 mm). Não houve diferenças estatisticamente significante (p>0.05) na infiltração marginal pelo corante entre os grupos 1, 2 e 4 e os grupos 2, 3 e 4. Com base nos resultados obtidos, pode-se concluir que a aplicação de agentes desmineralizantes não pode ser recomendada quando da utilização do MTA em cirurgias parendodônticas.
Subject(s)
In Vitro Techniques , Tooth Apex , Tooth, Nonvital , Analysis of Variance , Root Canal Filling Materials , Tooth DemineralizationABSTRACT
O objetivo deste trabalho foi avaliar in vitro a influência de três associações de agentes clareadores sobre o tampão cervical utilizando infiltração marginal por corante. Foram utilizados 48 molares humanos íntegros, recém-extraídos, tratados endodonticamente pela técnica da condensação lateral ativa com cones de guta-percha e cimento obturador Sealapex. O cimento de ionômero de vidro modificado por resina - Vitremer (3M) foi utilizado como tampão cervical com espessura de 3mm. Os espécimes foram divididos em quatro grupos conforme a utilização dos materiais clareadores: 1 (controle, sem material clareador), 2 (perborato de sódio + água), 3 (perborato de sódio + peróxido de carbamida a 10%) e 4 (perborato de sódio + peróxido de carbamida a 35%). A troca dos agentes clareadores foi realizada após 7 e 14 dias. Após 21 dias, os agentes clareadores foram removidos e os dentes foram impermeabilizados com 2 camadas de esmalte para unhas e uma camada de cera pegajosa, sendo imersos em corante Rodamina B a 2% durante 48 horas e posteriormente lavados em água corrente e secos. A avaliação da infiltração na interface dentina-tampão cervical em direção apical foi realizada em estereomicroscópio. Os dados obtidos foram submetidos aos testes de Kruskal-Wallis e Dunnett com nível de significância de 5%. Este estudo mostrou que não houve diferença estatística entre o grupo controle e as associações de agentes clareadores. Concluiu-se que as associações de agentes clareadores tiveram o mesmo grau de infiltração quando comparados ao grupo controle, e não houve diferença estatística quando comparou-se os materiais clareadores entre si.
Subject(s)
Humans , In Vitro Techniques , Tooth Bleaching , Tooth, Nonvital , Analysis of Variance , Glass Ionomer Cements , SodiumABSTRACT
O objetivo deste trabalho foi avaliar o pH e a densidade óptica da solução corante de azul de metileno 2% tamponada e não tamponada, rodamina B 2% tamponada e não tamponada, antes e após a imersão de materiais endodônticos por diferentes tempos. As soluções corantes, sem a imersão dos espécimes foram analisadas nos tempos de 0, 12, 24, 48 e 72 horas. Foram preparados oitenta cilindros de MTA branco e oitenta de MTA cinza, que foram imersos em 0,7 mL de cada uma das soluções corantes, após os tempos de 12, 24, 48 e 72 horas. Foram realizadas avaliações do pH e da densidade óptica através de espectrofotômetro, ajustado em 596 nm para azul de metileno e 566 nm para rodamina B. Os dados de pH foram analisados através de estatística descritiva. Os dados da densidade óptica após a imersão dos espécimes foram analisados através dos testes ANOVA (3 fatores) e Tukey 5%. Os resultados mostraram que a imersão dos espécimes de MTA branco por 12, 24, 48 ou 72h, nas soluções corantes tamponadas não promoveu alterações significativas nos valores da densidade optica. A estabilidade dos valores da densidade óptica, após a imersão dos espécimes de MTA cinza por 12, 24, 48 e 72h nas soluções de azul de metileno e rodamina B 2% não tamponadas, pode ser verificada. Concluiu-se que as imersões dos materiais endodonticos promoveram o aumento de pH das soluções corantes nos diferentes tempos de analise, sendo que as soluções não tamponadas apresentaram maior variação. O comportamento das quatro soluções corantes, após a imersão dos materiais endodonticos por 12,24,48 ou 72h não foram iguais. A variabilidade dos valores da densidade óptica apos imersão dos espécimes de MTA cinza na solução de azul de metileno 2% tamponada foi maior que a verificada após a imersão de espécimes de MTA branco. Dentre as soluções corantes analisadas, a rodamina B 2% tamponada apresentou comportamento mais estável de pH e de densidade ópt¡ca quando os materiais endodônticos foram imersos por 24 horas.
Subject(s)
Coloring Agents , Dental Leakage , Dye Dilution Technique , Methylene Blue , Root Canal Filling Materials , Hydrogen-Ion ConcentrationABSTRACT
O objetivo deste trabalho foi avaliar o selamento de ápices radiculares preparados com ultra-som e brocas convencionais e retrobturados com Super EBA e MTA mediante infiltração marginal por corante. Foram utilizados 56 dentes unirradiculados humanos extraídos, divididos em quatro grupos de 14:A1 (BEBA) - preparo convencional com brocas e retrobturação com super EBA; A2 (BMTA) - preparo convencional com brocas e retrobturação com MTA; B1 (UEBA) - preparo com ultra-som e retrobturação com Super EBA e B2 (UMTA) - preparo com ultra-som e retrobturação com MTA. Após impermeabilização, os espécimes foram imersos em tinta nanquim por 48h. As infiltrações ocorridas foram avaliadas com auxílio de estereomicroscópio e os resultados foram submetidos à análise estatística (ANOVA). As medidas das infiltrações foram 0,5071 mm para o grupo BEBA, 0,4714 mm para o grupo BMTA, 0,3357 mm para o grupo UEBA e 0,3035 mm para o grupo UMTA. Ocorreram diferenças estatisticamente significativas entre os métodos de preparo cavitário apical, sendo que, os melhores resultados foram obtidos com o ultra-som. os materiais utilizados (Super EBA ou MTA) apresentaram selamento marginal semelhante, independente do método de preparo cavitário apical
Subject(s)
Dental Marginal Adaptation , CeramicsABSTRACT
O objetivo deste trabalho foi avaliar o preparo cavitário apical com ultra-som sobre a infiltraçäo marginal por corante empregando três materiais retrobturadores. Foram utilizados 72 dentes unirradiculados humanos extraídos, divididos em seis grupos de 12. Os dentes receberam apicectomia, preparo cavitário com ultra-som ou brocas convencionais e retrobturaçäo com cimento de ionômero de vidro (Grupos 1 e 4), Super EBA (Grupos 2 e 5) e Sealapex associado ao óxido de zinco (Grupos 3 e 6). Os espécimes foram imersos em corante durante 48 horas a 37ºC, e as infiltraçöes ocorridas foram avaliadas com o auxílio de um estereomicroscópio. Pôde-se concluir que os métodos de preparo cavitário apical (com ultra-som ou brocas) näo influenciaram os resultados da infiltraçäo marginal apresentada pelos três materiais retrobturadores. Os materiais retrobturadores influenciaram os valores da infiltraçäo marginal. Os melhores resultados em termos de infiltraçäo foram obtidos com o cimento de ionômero de vidro e Super EBA
Subject(s)
Apicoectomy , Root Canal Filling Materials , Ultrasonics , Dental Cavity Preparation/methodsABSTRACT
A Odontologia comprova vantagens na utilizaçäo do amálgama de prata nas restauraçöes dos dentes posteriores. Contudo as propriedades físicas do material o contraindicam para cavidades muito extensas, devido à sua falta de adesäo à estrutura dental. A técnica de utilizaçäo conjunta de adesivos dentinários e amálgama reúne as qualidades favoráveis dos primeiros, como a adesäo e a diminuiçäo da microinfiltraçäo, com a possibilidade da realizaçäo de preparos mais conservadores, dada a comprovada eficiência dos amálgamas. Baseado nesses princípios, o objetivo deste artigo é apresentar algumas técnicas de restauraçäo com amálgama adesivo de forma que o leitor seja capaz de aproveitar o potencial das mesmas
Subject(s)
Dental Amalgam , Dentin-Bonding Agents , Dental Restoration, PermanentABSTRACT
Este trabalho teve como objetivo avaliar a influência dos métodos de esterilizaçäo sobre a capacidade e velocidade de absorçäo de cones de papel absorvente empregados em Endodontia. Foram analisados 320 cones de papel número 40, dos quais dez cones de cada marca comercial receberam zero, um, cinco ou dez ciclos de esterilizaçäo em estufa (170ºC/1 hora) ou em autoclave (134ºC/15psi/15 minutos). Após cada ciclo de esterilizaçäo, os cones foram avaliados quanto à capacidade e velocidade de absorçäo à soluçäo de hipoclorito de sódio a 1 por cento. Os dados foram submetidos à análise estatística por meio dos testes ANOVA (três e dois critérios) e Tukey (5 por cento). Pôde-se concluir que a capacidade e velocidade de absorçäo sofreram influência dos métodos de esterilizaçäo, do número de ciclos de esterilizaçäo, bem como da marca comercial dos cones avaliados. Näo houve relaçäo de proporcionalidade direta entre a capacidade e velocidade de absorçäo à soluçäo irrigadora empregada. A autoclavaçäo mostrou-se um procedimento viável, em até 10 ciclos, para a esterilizaçäo de cones de papel absorvente da marca Tanari
Subject(s)
Endodontics , Sterilization/methodsABSTRACT
A presença de umidade no interior do sistema de canais radiculares, após o preparo biomecânico e sua desinfecçäo, pode influenciar no selamento apical e no êxito da obturaçäo endodôntica. O objetivo deste trabalho foi avaliar a influência do número de esterilizaçöes em autoclave, sobre a capacidade e velocidade de absorçäo dos cones de papel empregados em Endodontia. Foram analisados 440 cones de papel número 40, dos quais dez cones de cada marca comercial receberam de zero à dez ciclos de esterilizaçäo em autoclave (134ºC/15 psi/15 minutos). Após cada ciclo de esterilizaçäo, os cones foram avaliados quanto a capacidade e velocidade de absorçäo de soluçäo de hipoclorito de sódio a 1 por cento. Os dados foram submetidos à análise estatística por meio dos testes da ANOVA (dois critérios) e Tukey (5 por cento). Pôde-se concluir que, quanto à capacidade de absorçäo, os cones que sofreram menor influência dos diversos ciclos de esterilizaçäo em autoclave foram, em ordem decrescente: Tanari, Tanari "cell pack", Conne e Diadent "cell pack". Quanto à velocidade de absorçäo, os cones que obtiveram os melhores resultados foram: Tanari "cell pack", Tanari, Conne Diadent "cell pack". A autoclavaçäo mostrou-se um procedimento viável, em até 10 ciclos, apenas para a esterilizaçäo de cones de papel absorvente da marca Tanari utilizados em Endodontia
Subject(s)
Endodontics , SterilizationABSTRACT
Neste trabalho é apresentado um caso clínico de tratamento endodôntico e protético de um incisivo central superior direito com dois canais radiculares
Subject(s)
Male , Adult , Endodontics , Incisor/anatomy & histology , Root Canal Therapy , Dental Prosthesis Repair , Incisor , Tooth Preparation, ProsthodonticABSTRACT
As leveduras säo freqüentes na cavidade bucal de indivíduos saudáveis, representando 60 a 70 por cento dos isolamentos, e seu estudo é importante, já que infecçöes causadas por esses microorganismos têm aumentado, principalmente com o advento da AIDS. O presente trabalho visa isolar leveduras do gênero Candida em dentes com comprometimento pulpar e/ou periapical e analisar in vitro a resistência desses microorganismos a medicamentos utilizados na terapia endodôntica. Foram estudados 100 dentes com comprometimento pulpar e/ou periapical, dos quais se coletou material do canal radicular 8 por cento de C. albicans. A verificaçäo da açäo in vitro de substâncias medicamentosas utilizadas na rotina do tratamento endodôntico sobre Candida demonstrou, nas condiçöes experimentais do presente trabalho, que atuaram efetivamente frente as amostras de Candida apenas o Cresophene, o Tricresol Formalina e a Clorexidine a 2 por cento