Surface topography, gloss and flexural strength of pressable ceramic after finishing-polishing protocols

Abstract This study evaluated the effect of different finishing-polishing protocols on surface roughness, gloss, morphology and biaxial flexural strength of pressable fluorapatite glass ceramic. Thirty ceramic discs (12x1 mm) were produced and divided into five groups (n=6): CT: control (glaze); DA: fine grit diamond bur; DG: DA + new glaze layer; DP: DA + felt disk with fine grit diamond paste; DK: DA+ sequential polishing with silicon abrasive instruments, goat hair brush and cotton wheel. The specimens were analyzed for surface roughness (Ra) under profilometry and atomic force microscopy (AFM). Gloss was measured with spectrophotometry and micromorphology with scanning electron microscopy (SEM). Flexural strength was assessed by biaxial flexural strength test. Data were analyzed using one-way ANOVA and Tukey's post hoc test (a=0.05). DK showed the lowest surface roughness values and DA presented the highest in the perfilometer analysis. No significant differences were observed in the AFM for the CT, DG and DK groups, which presented the lower surface roughness; DA and DP had the higher Ra values. The DA, DP and CT showed the lowest surface gloss values, and the reflectance was significantly different from those observed for DK and DG groups. SEM analysis revealed the smoothest surface for DK group, followed by DG and CT groups; DA and DP groups exhibited variable degrees of surface irregularities. No significant differences were observed among groups for the biaxial flexural strength. The polishing protocol used in DK group can be a good alternative for chairside finishing of adjusted pressable fluorapatite glass ceramic surfaces.

Resumo O objetivo deste estudo foi avaliar o efeito de diferentes protocolos de acabamento e polimento na rugosidade da superfície, brilho, resistência à flexão biaxial e morfologia de cerâmica prensada. Trinta discos de cerâmica (12x1 mm) foram produzidos e divididos em cinco grupos (n=6): CT- controle (glaze); DA- ponta diamantada de granulação fina; DG: DA + nova camada de glaze; DP: DA + disco de feltro com pasta de diamante de granulo fino; DK: DA + polimento sequencial com instrumentos abrasivos de silício, escova de cabra e roda de algodão. Os espécimes foram analisados quanto à rugosidade da superfície (Ra) sob profilometria e microscopia de força atômica (AFM). O brilho foi medido com espectrofotometria e a micromorfologia com microscopia eletrônica de varredura (SEM). A resistência à flexão foi avaliada pelo teste de resistência à flexão biaxial. Os dados foram analisados ​​usando ANOVA um fator e teste post hoc de Tukey (a=0,05). DK mostrou mais baixos valores de rugosidade da superfície e DA apresentou o maior na análise do perfilômetro. Não foram observadas diferenças significativas no AFM para os grupos CT, DG e DK, que apresentaram a menor rugosidade de superfície; DA e DP apresentaram os maiores valores Ra. O DA, DP e CT mostraram valores de brilho superficial mais baixos, e a reflectância foi significativamente diferente da observada para os grupos DK e DG. A análise de SEM revelou a superfície mais homogênea para o grupo DK, seguido de grupos DG e CT; Os grupos DA e DP exibiram graus variáveis de irregularidades da superfície. Não foram observadas diferenças significativas entre os grupos quanto à resistência à flexão biaxial. O protocolo de polimento utilizado no grupo DK pode ser uma boa alternativa para o acabamento em consultório das superfícies de cerâmicas prensadas após ajustes.

Reabilitação estética do sorriso por meio de procedimento restaurador direto com resina composta nanoparticulada: relato de caso / Esthetic smile rehabilitation throught direct restorative procedure with nanoparticulate composite resin: a case report

Pacientes acometidos por traumas em dentes anteriores são comumente encontrados na prática clínica. Estes traumas ocasionam diversas complicações, que podem prejudicar a função como fonética, estética e em casos mais graves, até resultar em perda do elemento dentário. Na ocorrência de fraturas dentárias, uma das alternativas de reabilitação é o procedimento restaurador por meio de técnica direta, com utilização de resina composta. Tais materiais possuem facilidade na execução da técnica, apresentam baixo custo, quando comparado às restaurações indiretas e ainda possuem propriedades físicas e mecânicas que são semelhantes à estrutura dentinária, funcionando de forma a biomimetizar a estrutura perdida do elemento dentário. O presente caso clínico relata reabilitação funcional e estética do sorriso de um paciente jovem, por meio de procedimento restaurador direto, o qual foi possível devolver aspecto de naturalidade aos dentes e harmonia do sorriso.

Patients affected by injuries in anterior teeth are commonly encountered in clinical practice. These cause a variety of complications, which may impair the function as phonetics, esthetics and in more severe cases, even result in dental element loss. On dental fractures occurrence, one of the rehabilitation alternatives is the restorative procedure through direct technique, using composite resin. Such materials have ease in execution of the technique, feature low cost, when compared to the indirect restorations and still possess physical and mechanical properties, which are similar to dentin structure, working in order to resemble the lost dental element structure. The present clinical case reports functional and esthetic smile rehabilitation of a young patient, through direct restorative procedure, which was possible return aspect of naturalness to the teeth and the smile harmony.

Reabilitação estética do sorriso com laminados cerâmicos: Relato de caso clínico / Aesthetic Restabilishment with laminates venners: Case report

Resumo: A busca por um sorriso harmônico eleva o nível de exigência e a expectativa dos pacientes. Esse fato propicia o desenvolvimento de novos materiais e técnicas odontológicas que visam procedimentos conservadores e resultados mais previsíveis. As cerâmicas têm se tornado alternativa para essas reabilitações de alta exigência estética, uma vez que possuem propriedades como biocompatibilidade, estabilidade de cor, longevidade e resistência, ou seja, apresentam biomimetismo com esmalte. Dessa forma, esse relato de caso tem como objetivo descrever a sequência clínica de uma reabilitação estética dos dentes 11, 12, 21 e 22 empregando laminados de cerâmica vítrea a reforçadas de dissilicato de lítio, proporcionando a reprodução das características naturais dos dentes. Os laminados cerâmicos promoveram excelentes resultados estéticos, sendo que o conhecimento da técnica operatória e dos materiais restauradores e qualidade do trabalho protético são essenciais parao planejamento e execução de restaurações estéticas.

The search for a harmonious smile raises the level of demand and the expectations of patients. This fact enables the development of new dental materials and techniques to conservative procedures and more predictable results. The ceramic has become an alternative to these highly demanding aesthetic restorations since they possess properties such as biocompatibility, color stability, durability and resilience, ie with the present biomimetism tooth structure. Thus, this case report aims to describe the clinical sequence of an aesthetic rehabilitation of the teeth 11, 12, 21 and 22 using laminated glass-ceramic reinforced of lithium di-silicate, providing playback of the natural characteristics of the teeth. The ceramic laminates promoted excellent aesthetic results, and the knowledge of the surgical technique and restorative materials and quality of the prosthetic work areessential for planning and execution of esthetic restorations.

Acabamento e polimento em resina composta: reprodução do natural / Polishing composite resin: reproduction of natural

As restaurações diretas em resina composta em dentes anterioresconstituem tratamento estético, entretanto, dependendo da composição e do uso inadequado destes compósitos resinosos, podem resultar em restaurações insatisfatórias provenientes da inadequada rugosidade superficial, porosidade, ausência de brilho e alteração de cor. Estas características podem ser evitadas ao se realizar adequado acabamento e polimento. Diante deste quadro, este artigo tem como objetivo apresentar uma técnica de acabamento e polimento para restaurações em resina composta. O acabamento e polimento é uma etapa imprescindível para a harmonia do sorriso e sucesso das reabilitações com resina composta.

Direct composite resin restorations in anterior teeth are aesthetic treatment, however, the some composition and the inappropriate use of these resin composites can be result in unsatisfactory restorations from inadequate surface roughness, porosity, lack luster and color change. These characteristics can avoid when management correct finishing and polishing. The aim of this article was to describe finishing and polishing techniques in composite resin restorations. The finishing and polishing is essential to smile harmony and success of restorations with composite resin step.