Influence of activation mode, fatigue, and ceramic interposition on resin cements' diametral tensile strength

Abstract This study evaluated the influence of activation modes, on Diametral Tensile Strength (DTS) of dual cured resin cements subjected to a Mechanical Fatigue test (MF). Four dual-cured resin cements (RelyX UNICEM [U], RelyX ARC [A], ENFORCE [E] and Nexus 2 [N]) were activated by three different curing modes as follows: Self-Curing (SC), Dual Cure activation with photoactivation executed directly (DC) and Dual Cure activation with Photoactivation Through Porcelain (DCTP). After 24 hours, half of the sample was subjected to 30.000 fatigue cycles at 1 Hz frequency and 12 N load. Then, all specimens were subjected to DTS test in Instron Universal Testing Machine and data were analyzed by three-way ANOVA and Tukey's Test (5%). The results of DTS test means (MPa) and standard deviation, for each cement factor activated by SC, DC and DCTP was respectively: U (28.12 ± 5.29; 37.44 ± 6.49 and 40.10 ± 4.39), A (49.68 ± 8.42; 55.12 ± 5.16 and 63.43 ± 6.92), E (49.12 ± 3.89; 56.42 ± 8.88 and 56.96 ± 6.45) and N (61.89 ± 11.21; 59.26 ± 9.47 and 62.56 ± 10.93). Turkey's test indicated that DC is related to the highest DTS values; Nexus 2 DTS remained the same independently of activation mode and that the Porcelain disk interposition enhanced DTS only for RelyX ARC the ANOVA statistical test indicated that MF didn't alter the DTS values for all experimental groups. MF results clinical implication is that all cements tested exhibited, in an immediate loading, good cross linked bonds quality.

Estudo in vitro da lisura superficial em resinas compostas, após imersão em café e Coca-Cola® / An in vitro evaluation of surface roughness resin composite restorative materials after immersion in coffee and Coke®

O objetivo deste trabalho foi analisar a diferença na rugosidade superficial de três resinas compostas submetidas a ciclos de imersão em três soluções pigmentantes. A amostra foi dividida em 4 grupos, de acordo com o tipo de solução de imersão: no Grupo I, saliva artificial (controle); no Grupo II, café; no Grupo III, Coca-Cola®; e, no Grupo IV, café seguido de Coca-Cola®. Cada grupo foi dividido em 3 subgrupos (N=9) de cada tipo de resina. Os corpos-de-prova foram levados à estufa a 37ºC (±1ºC), mergulhados em saliva artificial e estocados por uma semana. Após esse procedimento, todas as amostras sofreram três ciclos diários de imersão durante um período de 30 dias, após o qual tiveram sua lisura superficial avaliada no rugosímetro (Ra). Após a análise dos resultados pôde-se concluir que as imersões em Coca-Cola® e em Café e Coca-Cola® diminuem significativamente a rugosidade em todos os materiais, e a imersão em Café aumentou a rugosidade na Durafil® e na Esthet X®. A corrosão pode ter sido o processo responsável pelo aumento na sua lisura superficial, conferido aos materiais após a imersão em Coca-Cola®.