ABSTRACT
ABSTRACT Objective: The aim of the present study was to evaluate the surface roughness (Ra) of the Z-350 resin composite following immersion in different media (distilled water, coca-cola, coffee, black tea and red wine). Methods: Fifty specimens of resin composite measuring 10 mm x 2 mm were prepared. Polymerization was performed using the conventional method (40 s). Each specimen was immersed for one hour per day. Evaluations were performed at baseline as well as after three, six, nine and 12 months. Three Ra readings were taken in opposite directions at each evaluation using a roughness meter. Mean Ra values were subjected to analysis of variance (ANOVA) followed by Tukey's test (p < 0.05). Results: A significant increase in Ra was found in the specimens submitted to coffee, coca-cola(r) and black tea between baseline and the three-month evaluation. Variance was also found among the remaining evaluation times (3 months to 12 months), but the differences did not achieve statistical significance. No statistically significant differences in Ra were found among evaluation times in the specimens submitted to red wine or distilled water. Conclusion: Based on the present findings, coca-cola, coffee and black tea exert an influence on the surface roughness of resin composites.
RESUMO Objetivo: Avaliar a rugosidade da superfície (Ra) do Z-350 resina composta após imersão em diferentes meios (água destilada, coca-cola, café, chá preto e vinho tinto). Métodos: Foram preparados cinquenta espécimes de resina composta medindo 10 mm x 2 mm. A polimerização foi realizada através do método convencional (40 s). Cada espécime foi imerso durante uma hora por dia. As avaliações foram realizadas na linha de base, bem como após três, seis, nove e 12 meses. Três leituras Ra foram levados em direções opostas em cada avaliação, utilizando um medidor de rugosidade. Os valores médios de Ra foram submetidos a análise de variância (ANOVA) seguido pelo teste de Tukey (p <0,05). Resultados: Um aumento significativo na Ra foi encontrada nas amostras submetidas ao café, coca-Cola(r) e chá preto entre o início e a avaliação de três meses. Variância também foi encontrado entre as épocas de avaliação restantes (3 meses a 12 meses), mas as diferenças não atingiram significância estatística. Não houve diferenças estatisticamente significativas na Ra encontrados entre os momentos de avaliação nos casos submetidos ao vinho tinto ou água destilada. Conclusão: Com base nos achados, coca-cola, café e chá preto exercem uma influência sobre a rugosidade superficial de resinas compostas.
ABSTRACT
The purpose of the present study was to assess the bond strength of composite resin repairs subjected to different surface treatments and accelerated artificial aging. 192 cylindrical samples (CSs) were prepared and divided into 24 groups (n = 8). Half of the CSs were stored in water for 24 h, and the other half were subjected to C-UV accelerated aging for non-metallic specimens. The treatments were phosphoric acid + silane + adhesive (PSA); phosphoric acid + adhesive (PA); diamond bur + phosphoric acid + silane + adhesive (DPSA); diamond bur + phosphoric acid + adhesive (DPA); air abrasion + phosphoric acid + silane + adhesive (APSA); and air abrasion + phosphoric acid + adhesive (APA). The repair was performed and the specimens were again aged as described above. A control group (n = 8) was established and did not receive any type of aging or surface treatment. The specimens were loaded to failure in shear mode with a crosshead speed of 0.5 mm/min until fracture. Data were analyzed by one-way ANOVA/Tukey's test (p < 0.05). No statistically significant differences were found among DPSA, DPA, APSA, APA, and the control group. The aged PSA and PA achieved low bonding values and were statistically different from the control group, whereas the non-aged PSA and PA presented no statistically significant difference from the control group. Repairs with the proposed surface treatments were viable on both recent and aged restorations; however, phosphoric acid + adhesive alone were effective only on recent restorations.
Subject(s)
Composite Resins/chemistry , Dental Bonding/methods , Dental Restoration Repair/methods , Analysis of Variance , Dental Cements/chemistry , Materials Testing , Phosphoric Acids/chemistry , Shear Strength , Surface Properties , Time FactorsABSTRACT
Este estudo avaliou o comportamento mecânico de uma resina de poliuretano Quartz-die (Zermack - Itália) empregada na modelagem odontológica comparando-a com o gesso tipo IV Durone (Dentsply - Brasil). Uma matriz metálica moldada com silicona de condensação Speedex (Coltène - Suiça) proporcionou corpos de prova com 12mm de altura por 6mm de diâmetro. Oito corpos de prova em resina de poliuretano e oito em gesso tipo IV (Durone) foram submetidos a ensaio de compressão na máquina de ensaios universal EMIC DL 2000, com célula de carga de 2000Kgf e velocidade de 0,05mm/min. Oito corpos de prova em resina de poliuretano e oito em gesso tipo IV obtidos a partir de uma matriz metálica hexagonal foram ensaiados noDurômetro Sussen Wolpert tipo Testor HTl, empregando penetrador esférico de 12,7mm, estabelecendo valores para dureza Rockwell. Os valores obtidos foram submetidos ao teste não-paramétrico de Kruskall-Walliscom p<0,05. Dentro dos parâmetros adotados neste estudo pôde-se concluir que a resina de poliuretano Quartz-die apresentou menor resistência à compressão e menor dureza superficial que o gesso tipo IV Durone.
Subject(s)
Dental Impression Materials/analysis , Resins, Synthetic/analysis , Calcium Sulfate/administration & dosage , Hardness Tests/methodsABSTRACT
El termocondicionador es un aparato de construcción simple y costo reducido, que tiene por objetivo el de facilitar al Cirujano Dentista la manipulación de resina acrílica para realizar trabajos clínicos en los que su uso es necesario. Con este artículo se pretende mostrar la técnica de confección de un termocondicionador así como sus aplicaciones clínicas
The termoconditioning is a piece of equipment of simple construction and reduced cost, which provides comfort to the dentist when he performs clinical functions when the use of acrylic resin is necessary. The objective of this article is to demonstrate the making technique of one termoconditioning and its clinical applications
Subject(s)
Female , Acrylic Resins , Equipment and SuppliesABSTRACT
El objetivo de este trabajo fue verificar la influencia del Envejecimiento Artificial Acelerado sobre la resistencia a compresión de tres resinas compuestas. Los especimenes fueron confeccionados con auxilio de una matriz de nylon utilizando la técnica incremental, en cuanto a la manipulación se siguieron las instrucciones del fabricante , en total fueron confeccionados 48 especimenes utilizando las resina compuestas Filtek Supreme (3M-ESPE), Charisma (Heraeus-Kulzer) e Filtek Z-250 (3M-ESPE). Transcurridas 24 horas, 24 especimenes, 8 de cada material, fueron sometidos a ensayos mecánicos de compresión en la Máquina Universal de Ensayos (EMIC DL-2000) con una célula de carga de 2000Kgf y velocidad de 0,05mm/min. Los otros 24 cuerpos de prueba fueron sometidos a envejecimiento artificial acelerado en la máquina de C-UV Sistema Acelerado de Envejecimiento para no metálicos - ASTM-G-53 por 192 horas, lo que equivale a aproximadamente 5 años de envejecimiento en condiciones clínicas normales, posteriormente sometidas a ensayos mecánicos de compresión. Se realizo el análisis estadístico comparativo entre los resultados obtenidos utilizando el test de ANOVA/Tukey (P<0,05) y fue verificado que no hubo diferencia estadística en la resistencia a compresión entre las resinas Z-250 y Filtek Supreme envejecidas y no envejecidas. Entretanto se presento diferencia estadística entre las muestras confeccionadas con la resina Charisma envejecida y no envejecida
The objective of this work was to verify the influence of the Sped up Artificial Aging in the compressive strength of 3 composed resins. It was used a matrix of nylon for confection of 48 bodies of test with 8,0mm of height and 4,0mm of width, having been 16 with the Filtek resin Supreme(3M), 16 with Charisma (Heraeus Kulzer) and 16 with Filtek Z-250(3M). For the confection of the test bodies the incremental technique was used respecting the time of curing indicated for the manufacturers. Passed 24 hours, half of the bodies of test of each material was submitted to the compressive assay in the Universal Machine of Assays (EMIC DL-2000) with load cell of 2000Kgf and speed of 0,05mm/min. To another half it was submitted to the artificial aging sped up in the C-UV machine Sped up System of Aging for not metallic - ASTM-G-53 for 192 hours that is equivalent approximately the 5 years of aging and later submitted to the compressive assay. Analysis was become fullfilled comparative statistics between the gotten results using ANOVA/Tukey (P<0.05). It was verified that it did not have difference statistics in the compressive strength between the resins aged and not aged Z-250 and Filtek Supreme. However difference occurred statistics between aged and not aged the Charisma resin
Subject(s)
Female , Composite Resins , DentistryABSTRACT
Este estudo objetivou avaliar a capacidade de reprodução de detalhes presentes no molde por materiais de modelagem à base de gipsita Gesso pedra tipo IV, Durone, (Dentsply); Gesso pedra tipo IV, Fuji Rock EP,(GC); Gesso pedra tipo IV, Resinado Rock Plus, (Polidental); Gesso pedra tipo V, Durone, (Dentsply) epolímeros: resinas epóxicas Epoxiglass 1504, (Epoxiglass), resina epóxica Epoxiglass 1504 modificada com diatomita pura e silanizada. A resina e seu endurecedor foram carregados com diatomita numa relação de30%. A diatomita foi tratada com Silano Silquest A 187, (Crompton S/A). A resina modificada foi manipuladaem uma relação de 35%. Empregando-se silicona de adição Presidente (Kit de silicona leve e pesada, Coltène) realizaram-se três moldagens de uma matriz metálica com quatro hastes contendo sulcos dimensionados. Os corpos de prova foram analisados em microscópio óptico com aumento de 40 vezes (Measurescope Nikon, procedência Nippon Kogaru K. K.). Os resultados expressos por gessos e resinas foram analisados com o teste Variância e Tukey (p<0,05). Verificou-se que não há diferenças estatisticamente significantes entre os gessos e resinas analisadas. Concluiu-se que o carregamento da resina epóxica com diatomita ou com diatomita silanizada não reduz a sua capacidade em reproduzir detalhes presentes no molde. Com a metodologia empregada, não houve diferença entre gessos tipo IV e V e resina epóxica pura ou modificada com diatomita na capacidadede reprodução de detalhes presentes no molde.
Subject(s)
Dental Impression Materials/analysis , Epoxy Resins/analysis , Calcium Sulfate/analysis , Analysis of Variance , Data Interpretation, StatisticalABSTRACT
The objective of this study was to verify the biocompatibility of three different dental adhesives (Single Bond, Clearfil SE Bond and Prime & Bond NT). Thirty-six male rats (Rattus norvegicus, Holtzman) received two subcutaneous implants in the region of their backs. Artificial sponges containing the adhesive material were placed in the cavities and they were polymerized before the surgical site was sutured. As a control, one group was implanted with sponges containing water. Each rat received two implants containing the same adhesive; consequently each group consisted of 9 rats with two implants, resulting in 18 samples per group. After 7, 15 and 30 days, 3 animals of each group were killed and the tissues containing the sponges were analyzed by microscopy. The results showed a great similarity between the control group and the Single Bond implanted tissues, followed by the Clearfil SE Bond and Prime & Bond NT. The Prime & Bond NT adhesive system appeared to show less biocompatibility when compared with the other two tested materials.
Subject(s)
Animals , Male , Rats , Biocompatible Materials , Dental Materials , Dentin-Bonding Agents , Materials Testing , Subcutaneous TissueABSTRACT
The aim of the present study was to analyze the impact fracture strength using plaster and resin modeling materials. The analysis was made using nine dies having plaster III bases and internal portion of laboratory-type addition silicone. Nine test specimens were produced of each following material: typeIV Durone plaster, type IV Fuji Rock plaster, type IV Rock Plus plaster, type V Durone plaster, Epoxiglass 1504 epoxy resin, epoxy resin modified with diatomite and epoxy resin modified with diatomite. The tests were performed in a Ceast testing machine. At the moment of fracture, the machine recorded avalue (Energy), using a formula to obtain the impact strength value in joules per meter. Statistical and variance analyses and Student's t test revealed that pure or silanized diatomite increased the impact fracture strength of models made of Epoxiglass 1504 epoxy resin and that silanizing the filler led toa further gain in impact fracture strength. The models made of Epoxiglass 1504 displayed greater impact fracture strength than those made of plaster types IV and V. No statistically significant differences were found among the analyzed plasters. Models prepared with epoxy resin displayed in general greater impact fracture strength than models made of plasters.
Subject(s)
Dental Impression Materials , Dental Materials , Epoxy Resins , Physical PhenomenaABSTRACT
El objetivo de este trabajo fue el de realizar una revisión de literatura con el fin de identificar las alteraciones de posturales consecuentes de la Disfunción Temporomandibular y el tratamiento fisioterapéutico con entrenamiento postural. La metodología empleada fue una revisión bibliográfica por intermedio del sistema Medline y Lilacs, entre los años de 1993 y 2003, además de otros artículos y textos considerados importantes para este trabajo. Después de la lectura crítica fueron identificados dos temas: Las Disfunciones Temporomandibulares y su relación con la postura; las Disfunciones Temporomandibulares y el tratamiento fisioterapéutico por ejercicios y entrenamiento de postura. Conclusión: las alteraciones posturales pueden estar relacionadas a la Disfunción Temporomandibular y el uso de tratamiento fisioterapéutico con entrenamiento postural puede obtener resultados positivos.
O objetivo deste trabalho foi realizar uma revisão da literatura a fim de se obter um levantamento sobre quais alterações posturais sao decorrentes da Disfunção Temporomadibular e sua correlação com o tratamento fisioterapêutico e treino de postura. A metodologia empregada foi um levantamento bibliográfico realizado pelo sistema Medline e Lilacs, entre 1993 e 2003, além de outros artigos e textos considerados importantes para este trabalho. Após leitura crítica foram identificados dois temas: As Disfunções Temporomandibulares e sua relação com a postura; as Disfunções Temporomandibulares e o tratamento fisioterapêutico por exercícios e treino de postura. Conclusão: as alterações posturais podem estar relacionadas à Disfunção Temporomandibular, e o tratamento fisioterapêutico com treino de postura pode-se obter resultados positivos.
The aim of this work is to present survey on posture alterations due to Temporomandibular Joint Dysfunction and the related Physiotherapy treatment using posture training. The employed methodology was based on a large survey from 1993 to 2003 over well known datbases like Medline and Lilacs. Two main issues are present in almost all articles: how Dysfunction Temporomandibular Joint and posture are related and the Dysfunction Temporomandibular Joint treatment using training and exercises. The was observed that physiotherapy treatment using training and exercises was help patients to decrease the symptoms and, as a consequence, their posture.
Subject(s)
Humans , Physical Education and Training/methods , Physical Therapy Modalities , Posture/physiology , Temporomandibular Joint Disorders/rehabilitation , Masticatory Muscles/physiopathology , Stomatognathic System/physiopathologyABSTRACT
El presente trabajo relata la solución de un caso clínico en el cual fue utilizada una resina compuesta submicrohíbrida; con el objetivo de devolver no solo la función sino también la estética, por medio de la técnica restauradora directa. Después de realizados el examen clínico y radiográfico, se observo que las cúspides linguales y la restauración del diente 36 estaban fracturadas. Inicialmente fueron verificados los contactos oclusales así como el registro del color, que fue A3, de acuerdo con la escala Vita. El sistema adhesivo seleccionado fue Excite, asociado a la resina compuesta InTen-S, además de los pigmentos Tetric color. Se puede concluir que el uso de resina compuesta de bajo escurrimiento demostró buenos resultados clínicos.
The present study report a case which was used sub-microhibrid composite resin as aim to get better function and esthetic by a restorative protocol. At the clinical trial and x - ray, it was observed a deficient restoration allied with lingual cusp crack. The initial color was evaluated as A3, according by the Vita shade guide. The adhesion system used was Excite, restorative composite In Ten-S and Tetric color stain. It was conclude that this composite provide a healthier clinical aspects due to its proprieties.
Subject(s)
Humans , Male , Adult , Esthetics, Dental , Composite Resins/chemistry , Composite Resins/therapeutic use , Dental Restoration, Permanent/methods , Brazil , Color , Dental Polishing , Dental Bonding/methodsABSTRACT
Este estudio pretendió evaluar el comportamiento de resistencia a la tensión de modelos odontológicos obtenidos a partir de una resina epóxica de uso industrial modificada con circonita. A la resina Epoxiglass 1504 y el endurecedor Epoxiglass 1603 les fue adicionada circonita en una proporción de 1 para 1 en peso; modificada de esta manera fue manipulada siguiendo las instrucciones del fabricante, el cual establece una proporción de 35 por ciento en peso entre la resina y el endurecedor. Fueron realizadas 15 impresiones de un modelo matriz, utilizando silicona de adición, siendo vaciados con Epoxiglass 1504, Epoxiglass 1504 modificada y Yeso Piedra tipo IV, obteniéndose 60 cuerpos de prueba en total. Las características de los mismos fueron: 12 mm. de altura y 6.0 mm. de diámetro. Los cuerpos de prueba fueron divididos en dos grupos de 30 cada uno, de estos uno de ellos fue sometido al ensayo mecánico de compresión y el otro al de tracción por compresión diametral, utilizando una máquina universal de ensayos DL2000 EMIC, con una célula de carga de 2000kgf y velocidad de 0,5mm/min. Los resultados fueron analizados con el análisis estadístico ANOVA y comprobación con el test de Tuckey con grado de exactitud de 5 por ciento verificando que: los modelos de resina epóxica Epoxiglass 1504 mostraron resistencia a compresión y resistencia a tracción por compresión diametral superior a los modelos de yeso tipo IV; la circonita aumenta la resistencia a tracción por compresión diametral de la resina Epoxiglass 1504. Frente a estos resultados, se puede concluir que la resina epoxica Epoxiglass 1504 se presenta como un material viable para la obtención de modelos odontológicos, así como también, que la circonita mejoró comportamiento mecánico del material en relación a las propiedades mecánicas estudiadas.
This study evaluated the tensil behavior of dental models obtained using an industrial epoxic resin modified with zirconita. The Epoxiglass resin 1504 and the hardener Epoxiglass 1603 were added with zirconita in a ratio of 1/1 in weight. The modified resin was manipulated in accordance with the manufacturer's specifications, which establishes a relation of 35% in weight between the resin and the hardener. Fifteen moldings of a matrix were conducted using addition silicone. Then, they were filled with epoxic resin Epoxiglass 1504, resin Epoxiglass 1504 modified or type IV Durone plaster, which provided 60 test specimens with 12mm of height and 6mm of diameter. Thirty specimens were submitted to the compression assay and thirty to the traction assay by diametrical compression, using the universal machine DL2000 (EMIC), with a load cell of 2000 Kgf and 0,5mm/mim speed. The results were analyzed by Variance analysis followed by Tukey test with significance level set at 5%. It was verified that models made of Epoxiglass 1504 presented superior tensile strenght for diametrical compression and also superior compressive strength than models made of plaster type IV. The zirconita increased the tensile strenght for diametrical compression of the epoxic resin Epoxiglass 1504. In accordance to the present results, it was verified that the epoxic resin Epoxiglass 1504 is a viable material for dental modeling and that the zirconita provides mechanical benefit for the epoxic resin.
Esse estudo avaliou o comportamento tensil de modelos odontológicos obtidos a partir de uma resina epóxica de uso industrial modificada com zirconita. A resina Epoxiglass 1504 e o endurecedor Epoxiglass 1603 foram carregados com zirconita numa proporção de 1/1 em peso. A resina modificada foi manipulada de acordo com as especificações do fabricante, que estabelece uma relação de 35% em peso entre a resina e o endurecedor. Foram realizadas quinze moldagens de uma matriz, os moldes foram obtidos com silicone de adição e preenchidos com resina epóxica Epoxiglass 1504, resina Epoxiglass 1504 modificada e gesso tipo IV Durone, o que proporcionou 60 corpos de prova com 12mm de altura e 6mm de diâmetro. Trinta corpos de prova foram submetidos ao ensaio de compressão e trinta ao ensaio de tração por compressão diametral, empregando-se a máquina universal de ensaios DL2000 da EMIC, com célula de carga de 2000Kgf e velocidade de 0,5mm/mim. Os resultados foram analisados com Teste de Variância e Tukey com significância de 5%, e verificou-se que: Modelos obtidos em resina epóxica Epoxiglass 1504 apresentam superior resistência à tração por compressão diametral que modelos obtidos em gesso tipo IV; Modelos obtidos em resina epóxica Epoxiglass 1504 apresentam superior resistência à compressão que modelos obtidos em gesso tipo IV; A zirconita aumenta a resistência à tração por compressão diametral da resina epóxica Epoxiglass 1504. Diante dos resultados encontrados, verificou-se que a resina epóxica Epoxiglass 1504 apresenta-se como material viável para a modelagem odontológica e que a zirconita proporciona ganho mecânico para a resina epóxica.
Subject(s)
Compressive Strength , Models, Dental , Polymers/chemistry , Epoxy Resins/chemistry , Tensile Strength , Analysis of Variance , Zirconium/chemistry , Materials Testing , Data Interpretation, Statistical , Calcium Sulfate/chemistryABSTRACT
El objetivo de este trabajo fue el de comparar la resistencia a compresión de tres diferentes marcas de resinas compuestas. Filtek Supreme (3M-ESPE), Charisma (Heraus-Kulzer), y Teric Ceram (Ivoclar-Vivadent), utilizando dos fuentes de fotopolimerización (Optilght,Gnathus y Ultraled (Dabi Atlante). En total fueron confeccionados 48 especímenes divididos en 6 grupos conteniendo 8 muestras cada uno. Para los grupos G1 (Filtek Supreme); G3 (Tetric Ceram) e G5 (Charisma) fue utilizada una lámpara de luz halógena; para los grupos G2 (Filtek Supreme); G4 (Tetric Ceram) e G6 (Charisma) fue utilizada una unidad de fotopolimerización por LEDs. El tiempo de polimerización fue el mismo recomendado por los propios fabricantes. Todas las muestras fueron almacenadas en recipientes plásticos negros herméticamente tapados durante 24 horas. Los ensayos mecánicos de compresión fueron realizados usando una Maquina Universal de Ensayos EMIC DL 2000, con célula de carga de 2000kgf con velocidad de acción de 0,5mm/minuto hasta producir la fractura. Los datos obtenidos fueron analizados usando los tests estadísticos ANOVA/Tukey (p<0,005). Las medias encontradas en MPa fueron: G1 248.37; G 2193.75; G3 222.00; G4 195.87; G5 280.37; G6 205.25. Se observó que las resinas compuestas Filtek Supreme y Charisma polimerizadas por luz halógena presentaron los valores de resistencia a compresión estadísticamente superiores a los mostrados por los grupos polimerizados con LEDs. El grupo de Tetric Ceram no mostró diferencia estadísticamente significante. El grupo 5 mostró valores superiores en relación a los otros grupos, siendo estadísticamente diferente de los grupos 2,3,4,6. El grupo 2 mostró los menores valores, siendo estadísticamente diferente de los grupos 1 y 5. Por los resultados obtenidos puede concluirse de que las resinas fotopolimerizadas por luz halógena presentaron los mejores resultados de resistencia a compresión con excepción de la resina compuesta Tetric Ceram.
This study main purpose was to evaluate the mechanical response of three different resin composite brands; Filtek Supreme, Charisma and Tetric Ceram cured by halogen or light emitting diode - LED (Optilght,Gnathus e Ultraled, Dabi Atlante). A nylon mold 4-mm in diameter and 8-mm in depth was used to obtain forty eight specimens dived in 6 groups of 8 varying the light-curing unit; G1 Filtek Supreme, G3 Tetric, G5 Charisma cured by halogen light-curing unit, and G2 Filtek Supreme, G4 Tetric, G6 Charisma cured by LED. The resin composites were inserted according to the incremental method. The resin composites were light cured according to the manufactures' instructions. The specimens were kept in plastic containers airtightly closed for 24 hours. In order to perform the evaluation, an EMIC DL 2000 was used at a crosshead speed of 0.5 mm/minute and a charge cell of 2000 Kg strength. The statistical analysis was performed using one-way analysis of variance (ANOVA) and Tukey test at a p<0.05 significance level. The mean were G1 248.37, G2 193.75, G3 222.00, G4 195.87, G5 280.37, G6 205.25. In conclusion, the resin composites light-cured by halogen scored higher in the compressive strength test. In the Tetric Ceram group there were no statistically relevant results.
Subject(s)
Compressive Strength , Dental Equipment , Composite Resins/chemistry , Analysis of Variance , Patent , Photochemistry , Data Interpretation, StatisticalABSTRACT
O objetivo deste trabalho foi avaliar o comportamento mecânico à compressão de sete diferentes resinas compostas fotopolimerizáveis: G1- Tetric Ceram (Ivoclar Vivadent); G2- Durafill VS (Heraeus Kulser); G3-Esthet X (Dentsply); G4- Charisma (Heraeus Kulser); G5- Filtek Supreme (3M ESPE); G6- Filtek Z250 (3M ESPE); G7- Filtek P60 (3M ESPE). Foram confeccionados oito corpos-de-prova de cada resina, utilizando matriz de nylon (4mm de diâmetro e 8mm de altura). As resinas foram inseridas em incrementos e fotopolimerizadas pelo tempo recomendado pelos fabricantes (Optilight 600 - Gnatus) com intensidade monitorada...
Subject(s)
Composite Resins/analysis , Materials Testing , Compressive StrengthABSTRACT
Para realização deste estudo vinte condutos artificiais foram construídos em blocos formados por esmaltee dentina, a partir de dentes bovinos. Dez pinos de fibra de vidro e dez de fibra de carbono foram cimentadosnos condutos com cimento resinoso C&B. Empregou-se matriz de policarbonato para confecção do coreem resina composta, perfazendo quatro grupos: Grupo (1) pino de fibra de vidro e core com resina compostaCharisma; Grupo (2) pino de fibra de carbono e core com resina composta Charisma; Grupo (3) pino defibra de vidro e core com resina composta reforçada Enforce-core; Grupo (4) pino de fibra de carbono ecore com resina composta reforçada Enforce-core. Os ensaios mecânicos de compressão foram realizadosna máquina universal de ensaios EMIC DL 2000, com célula de carga 2000kgf e velocidade 1mm/mim.Verificou-se diferença estatística (p<0,05) (ANOVA) somente do fator resina no que tange as medidas daresistência à fratura do core, além disso, não há uma influencia significativa do tipo de fibra e nem mesmoda interação entre os fatores (resina x fibra). A conclusão para um fator é a mesma independentemente donível do outro fator. Os resultados para os dentes com resina composta reforçada diferem significativamentedos dentes que utilizaram resina composta não reforçada, onde, os dentes com resina composta reforçadaapresentaram medidas de resistência significativamente superiores aos dentes que utilizaram resina compostanão reforçada, independentemente do tipo de fibra (Teste de DUNCAN). Portanto, a fibra não influencia noresultado de resistência.
Subject(s)
Cattle , Dental Pins , Composite Resins/therapeutic use , Resins/analysis , Resin Cements/therapeutic use , Data Interpretation, Statistical , Casts, SurgicalABSTRACT
O cimento de ionômero de vidro foi desenvolvido a partir da união de dois outros materiais, o cimento de silicato e o cimento policarboxilato de zinco. Mesmo com a evolução desses materiais, a propriedade solubilidade/desintegração ainda está pouco clara na literatura. O objetivo deste trabalho foi avaliar comparativamente a solubilidade e desintegração de cimentos de ionômero de vidro modificados por resina e de compômeros, bem como, a necessidade ou não de aplicação de agentes de proteção sobre suas superfícies. Os materiais utilizados foram: M1-Vitremer (3M Co.); M2-Fuji II LC (GCAmerica Inc.); M3-Dyract (Dentsply); e M4-Compoglass (Vivadent). Os agentes de proteção superficial utilizados foram: P1-Fluroshield (Dentsply) e P2-FinishingGloss (3M Co.). Estes materiais foram submetidos a testes de solubilidade e desintegração de acordo com a norma ISO 7489 de 1986. Aos resultados foram aplicadas transformações angulares e submetidos à análise de variância (p < 0,05) a dois critérios fixos e teste de homogeneidade. Os cimentos de ionômero de vidro modificados por resina e os compômeros apresentaram diferentes valores de solubilidade e desintegração. O menor valor foi obtido pelo Dyract, seguido pelo Fuji II LC e Compoglass com valores intermediários e Vitremer com o maior valor. Concluiu-se que os materiais submetidos à proteção superficial apresentaram menores valores de solubilidade e desintegração que os não protegidos; os agentes protetores, Finishing Gloss e Fluroshield mostraram-se eficazes para proteção superficial dos cimentos de ionômero de vidro modificados por resina e compômeros
The glass ionomer cement was developed from two other materials, the silicate cement and the zinc policarboxilate cement. Even though these materials have been enhanced since their creation, the solubility/disintegration properties are still not clear in the specific literature. This study main purpose was to evaluate the solubility and disintegration of resin modified glass ionomer cements as well as the necessity of using coating materials over their surface. M1-Vitremer (3M ESPE); M2-Fuji II LC (GCAmerica Inc.); M3-Dyract (Dentsply); and M4-Compoglass(Vivadent) were used in this study. The coating materials used were P1- Fluroshield (Dentsply) and P2-Finishing Gloss (3M ESPE). These materials underwent solubility and disintegration tests according to ISO 7489 policies from 1986. The results were submitted to angular transformations and variance analysis and homogeneity test suggesting: the resin modified glass ionomer cements and compomers showed different solubility and disintegration rates, Dyract < Fuji II LC = Compoglass < Vitremer; the resin modified glass ionomer cements and compomers submitted to the surface protection showed lower solubility and disintegration rates contrasted to the non-protected specimens; Finishing Gloss and Fluroshield demonstrated effective surface protection for resin modified glass ionomer cements and compomers
Subject(s)
Analysis of Variance , Glass Ionomer Cements , Resin Cements , Compomers , SolubilityABSTRACT
The objective of this study was to verify the biocompatibility of dental adhesives (Prime & Bond 2.1; Prime & Bond NT and Scotchbond MP). Thirty-six male rats (Rattus norvegicus) received artificial sponges containing the adhesive materials in their back, and they were polymerized before suture. As a control, one group had sponges containing water. Each group consisted of 9 rats with two implants, resulting in 18 samples per group. Three animals of each group were killed after 7, 15 and 30 days and the tissue was analyzed. At sevenday period, inflammation was acute and severe in all other groups, except water. After 15 days, Prime & Bond 2.1 and Prime & Bond NT groups showed a more severe inflammatory infiltrate with foci of neutrophils inside the cavity border when compared with the Scotchbond Primer. After 30 days, in the control group the cavity was shown to be filled by well organized granulomas next to the sponge samples. Prime & Bond 2.1 and Prime & Bond NT groups maintained intense inflammatory process when compared with the Scotchbond Primer MP group. The present results showed that Scotchbond MP Primer Group demonstrated better biocompatibility than the other two groups.
Subject(s)
Animals , Male , Rats , Biocompatible Materials , Dental Materials , Dentin-Bonding Agents , Dental ImplantsABSTRACT
O objetivo do trabalho foi estudar a biocompatibilidade de sistemas adesivos. Foram utilizados 36 ratos machos (Rattus norvegicus, Holtzman), divididos aleatoriamente em quatro grupos experimentais (controle: água destilada, Excite, Suprafill e magic Bond DE) que receberam 2 implantes cada no tecido conjuntivo subcutâneo na região dorsal. Esponjas artificiais contendo o material adesivo foram depositados nas cavidades e estes foram polimerizados antes da sultura. Realizou-se biópsia excisional em 3 animais por grupo após 7, 15 e 30 dias e os tecidos foram analisados por microscopia óptica. Aos 7 dias, os grupos Excite, Suprafill e Magic Bond DE, apresentaram intenso infiltrado inflamatório mono e polimorfonuclear, sem diferrenças entre os grupos: enquanto o grupo controle, revelou moderado infiltrado inflamatório mononuclear. Aos 15 dias ocorreu diminuição da intensidade dos fenômenos inflamatórios nos três grupos experimentais...
Subject(s)
Animals , Male , Rats , Dentin-Bonding Agents/analysis , Materials Testing , Distilled WaterABSTRACT
O objetivo deste estudo foi avaliar o pH de agentes clareadores a base de carbamida a 10 por cento e 16 por cento disponíveis comercialmente Whiteness Standard (FGM), Review (SSWhiate) e Whteness Perfect (FGM) e manipulados em farmácia de manipulação. A análise do pH foi conduzida utilizando um pHmetro Micronal B474, calibrado em 4,00 e 7,00 com solução tampão ácido cítrico/hidrogênio fosfato de sódio, empregando-se solução KCl 3 mol L. Três gramas de cada amostra foram depositadas em tubo de ensaio recobrindo todo bulbo do eletrodo. O processo foi repetido 8 vezes para cada agente clareador. O eletrodo era lavado entre cada amostra usando água corrente e ácido acético a 4 por cento para remoção completa do agente clareador. O eltrodo foi lavado com água destilada, seco com papel absorvente e a calibração conferida. Aguardava-se 3 minutos para cada leitura, em temperatura ambiente de 24±1ºC. O pH dos produtos clareadores variou de 4,060 (agente manipulado 10 por cento) a 6,212 (Whiteness Standard 10 por cento)...
Subject(s)
Tooth Bleaching/adverse effects , Peroxides/administration & dosage , Data Interpretation, Statistical , Hydrogen-Ion ConcentrationABSTRACT
No presente trabalho, avaliou-se, através de ensaios mecânicos de cisalhamento, a resistência de união à dentina de peças metálicas fundidas em liga de prata cimentadas com quatro tipos de cimentos odontológicos. Foram selecionados quarenta dentes molares humanos íntegros e fixados com resina acrílica em tubos plásticos de PVC. A seguir, cada coroa dental foi então seccionada na altura do terço oclusal deixando a dentina exposta. A liga de prata foi preparada em pastilhas com 3mm de espessura. Antes da cimentação, cada pastilha recebeu um jateamento de óxido de alumínio de 0,05µm de granulação, por 15 segundos e com pressão de 70/80 libras. O processo de cimentação, para cada tipo de cimento, foi realizado de acordo com as instruções dos fabricantes. Os ensaios mecânicos de cisalhamento foram realizados na máquina MTSû810 Material Test System utilizando uma carga de 100 Kgf e velocidade de pressão de 0,05 mm/min. Para verificar a diferença significativa entre os tratamentos, realizou-se a análise de variância e teste de Tuckey ao nível de significância de 5 %. Os resultados obtidos nos levaram a concluir que: 1) G2 (cimento resinoso RelyX Cement) apresentou, numericamente, a maior média dos valores de união, seguido em ordem decrescente por G1 (cimento de ionômero de vidro modificado com resina RelyX Luting), G4 (cimento de ionômero de vidro Ketac Cem) e G3 (fosfato de zinco); 2) As médias dos valores de união, de todos os grupos, foram diferentes estatisticamente entre si.
This work evaluated, through mechanical shearing assays, the strength of bonding to dentine of silver alloy metallic pieces, bonded with four types of dental cements. Fortywhole human molar teeth were selected and fixed, with acrylic resin, to û inch plastic PVC tubing segments. Following this, each dental crown was sectioned at the oclusal third, M-D direction, exposing the dentine. The silver alloy was prepared as 3mm-thick discs. Before cementation, each disc was blasted withaluminum oxyde (0.05mm grain), during 15 seconds, at a 70/80 pounds pressure. The cementation process, for each cement,followed the manufactureræs instructions. The mechanical shearing assays were performed with a MTS-810 Material TestSystem machine, at 100 Kgf load and 0.05 mm/min pressure speed. The results were statistically analysed with ANOVAand Tuckeyæs test at 5% significance level. The results allowed the following conclusions: 1) G2 (resin cement RelyX) offered,numerically, the greatest average bonding value, followed, in decrescent order, by G1 (glass ionomer modifyed with RelyXLuting resin), G4 (standard glass ionomer cement Ketac Cem) and G3 (zinc phosphate); 2) The average bonding values,in all groups, were statistically different.
Subject(s)
Dental Alloys , Dental Cements , Dentin , Shear StrengthABSTRACT
O objetivo desse trabalho foi avaliar a influência do prazo de validade de resinas compostas na resistência à compressão. As resinas foram divididas em 6 grupos: G1 Esthet X (Dentsply/Caulk), G3 Charisma (Heraeus Kulzer), G5 Durafil VS (Heraeus Kulzer), com prazo de validade vencido e G2 Esthet X, G4 Charisma, G6 Durafil VS, dentro do prazo de validade...