Chinese Journal of Tissue Engineering Research ; (53): 3720-3725, 2016.
Article in Chinese | WPRIM | ID: wpr-494080

ABSTRACT

BACKGROUND: In our previous studies, zinc-calcium-phosphate (Zn-Ca-P) coating has been successful y prepared on the surface of AZ31 magnesium al oy, which improves the corrosion resistance of the al oy. OBJECTIVE: To analyze the hemocompatibility of Zn-Ca-P coated AZ31 magnesium al oy in vitro. METHODS: Zn-Ca-P coating was prepared on the surface of AZ31 magnesium al oy using chemical transformation. Afterwards, the characteristics of the Zn-Ca-P coating were investigated using scanning electron microscope, and X-ray diffraction analyzed its components. Besides, hemocompatibility in vitro was evaluated by platelet adhesion assay, dynamic clotting time test and hemolysis test. RESULTS AND CONCLUSION: Under scanning electron microscope, a flower-like coating was formed ont surface of the AZ31 magnesium al oy, with the main chemical component of insoluble phosphates Zn3(PO4)2?4H2O. And some round distortionless blood platelets adhered to the surface of AZ31 magnesium al oy, with no pseudopodia. In dynamic clotting time test, the long curve of Zn-Ca-P coating tended to descend indicating better anticoagulant activity. And the hemolysis rate was below 5%. In conclusion, Zn-Ca-P coating has good hemocompatibility in vitro.

SELECTION OF CITATIONS
SEARCH DETAIL