Influence of Photoinitiator System on Physical-Chemical Properties of Experimental Self-Adhesive Composites

Abstract The aim of this study was to determine the influence of photoinitiator systems on physical-chemical properties of flowable composites. Conventional (CFC), composed by bisphenol-glycidyl dimethacrylate (BisGMA)+triethyleneglycol dimethacrylate (TEGDMA), and self-adhesive (SAFC), composed by BisGMA+TEDGMA+bis{2-(methacryloyloxy) ethyl} phosphate (2MP), flowable composites were developed. Five photoinitiator systems were tested: camphorquinone (CQ), ethyl-4-dimethylaminobenzoate (EDMAB), diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO), phenylbis (2,4,6-trimethylbenzoyl)phosphine oxide (BAPO), CQ+EDMAB+TPO and CQ+EDMAB+BAPO. A two-peak LED was used; degree of conversion (DC) and the maximum polymerization rate (RPmax) were determined by near infrared spectroscopy. For the yellowing degree a spectrophotometer was used. Water sorption (Wsp) was obtained after 30 days of water storage (n=5). Data were submitted to two-way analysis of variance and Tukey’s test (a=0.05). BAPO presented the highest DC and RPmax values for both series. SAFCs presented lower DC and RPmax for CQ+EDMAB-based materials. Greater yellowing was observed for SAFCs compared with CFCs, except for BAPO. Greater Wsp was observed for SAFCs compared with CFCs. The photoinitiator did not influence Wsp for CFCs, but TPO and BAPO presented the highest Wsp in SAFCs. The photoinitiator system affected differently the physical-chemical properties of CFCs and SAFCs.

Resumo O objetivo do estudo foi determinar a influência do sistema fotoiniciador sobre as propriedades físico-químicas de compósitos fluidos. Os compósitos convencionais foram compostos por bisfenol-glicidil dimetacrilato (BisGMA) + trietilenoglicol dimetacrilato (TEGDMA), e os autoadesivos, apresentavam BisGMA +TEGDMA+ Bis2(metacriloiloxi)etil fosfato (2 MP). Cinco sistemas fotoiniciadores foram testados: canforquinona + etil-4- dimetilamino benzoato (CQ+EDMAB), óxido mono-alquil fosfínico (TPO) e óxido bis-alquil fosfínico (BAPO), CQ+EDMAB+TPO e CQ+EDMAB+BAPO. LED de amplo espectro foi usado; o grau de conversão (GC) e a taxa de polimerização (TP) foram determinados por espectroscopia próximo ao infravermelho; o grau de amarelo foi mensurado por um espectrofotômetro e absorção de água foi obtida após 30 dias de armazenamento em água (n=5). Os dados foram submetidos a análise de variância de dois fatores e teste de Tukey (?=0,05). BAPO apresentou os maiores valores de GC e TP nos compósitos convencionais e autoadesivos. Compósitos autoadesivos apresentaram menor GC e TP quando CQ+EDMAB foi usado. Maior amarelecimento foi observado nos compósitos autoadesivos em relação aos convencionais, exceto para BAPO. Compósitos autoadesivos promoveram maior absorção de água. Não houve influência dos fotoiniciadores nos compósitos convencionais, no entanto TPO e BAPO apresentaram os maiores valores de absorção de água nos compósitos autoadesivos. Os sistemas fotoiniciadores influenciaram de maneira diferente as propriedades físico-químicas dos compósitos convencionais e autoadesivos.

Reabilitação oral estética com laminados cerâmicos ultrafinos / Aesthetic oral rehabilitation with ultrathin ceramic veneers

A utilização de laminados cerâmicos ultrafinos nas reabilitações orais estéticas tem-se tornado uma opção de tratamento cada vez mais popular. Entretanto não há elevado nível de evidência científica quanto à longevidade dessas restaurações. Com base nisso, o objetivo do presente artigo é relatar a instalação de laminados cerâmicos ultrafinos na bateria labial superior de uma paciente com queixa de insatisfação estética do sorriso após ter finalizado um tratamento ortodôntico, destacando aspectos relacionados ao diagnóstico, ao planejamento do caso e ao preparo dentário...

The use of ultrathin ceramic veneers for the aesthetic oral rehabilitation has become an increasingly popular treatment. However, there is few high-quality scientific evidence regarding the longevity of these restorations. Based on this fact, the purpose of this study is to report a clinical case of ultra-thin ceramic veneers in the maxillary teeth of a patient unsatisfied with her smile after the end of the orthodontic treatment, highlighting aspects related to diagnosis, treatment planning and tooth preparation...

Bulk and surface properties related to composite filler size

There are few studies that fully characterize the effect of the filler size on the surface, optical and mechanical properties of resin composites. AIM: To determine the influence of the filler size content on surface, optical and mechanical properties before and after accelerated aging. METHODS: Seven resin composites were investigated: Filtek Supreme® (3M/ESPE), Estelite Σ Quick® (Tokuyama), Evolu-X® (Dentsply), Esthet-X HD® (Dentsply), Opallis® (FGM), Herculite XRV Ultra® (Kerr) and Filtek Z250® (3M/ESPE). Elastic modulus (EM) and flexural strength (FS) were determined by three-point bending of specimens immersed or not in absolute ethanol for seven days. Roughness (Ra) and gloss (G.U.) analyses were determined before and after ethanol storage for seven days and CIELAB color change (ΔE*) was obtained with a spectrophotometer. Results were analyzed by two-way ANOVA (general linear model) for EM and FS, with repeated measures for roughness and gloss, and one-way ANOVA for ΔE*. All comparisons were performed by Tukey's test (5%). Pearsons' correlation test was performed to determine the correlation between EM, FS, roughness, gloss, and ΔE* with the mean filler sizes. RESULTS: Mechanical properties decreased for all materials when submitted to immersion in ethanol. Increasing filler size gradually increased EM, FS and roughness values; gloss values decreased and didn't significantly affects ΔE*. Nanofiller composites presented higher gloss values than the others. CONCLUSIONS: It was possible to determine that the average filler size is a good predictor just for FS and gloss retention.

Avaliação da abrasividade de escovas dentais com cerdas macias / Abrasion assessment of soft bristle toothbrushes

Uma ampla variedade de escovas dentais está disponível no mercado com diversas indicações clínicas. Entretanto, poucos estudos na literatura avaliam a abrasão de escovas de diferentes marcas sobre as restaurações de resina composta. Objetivo: o presente estudo buscou avaliar a abrasividade de três escovas dentais com cerdas macias: Oral B Indicator Plus®, Colgate Extra Clean® e Dr. Veit Soft® em um compósito restaurador. Materiais e método: discos do compósito (8 mm x 2 mm) Tetric Ceram® foram produzidos e fotoativados com uma fonte de luz LED por 40 segundos cada. Dezoito amostras foram confeccionadas e divididas em três grupos experimentais (n = 6). Foram avaliadas a rugosidade superficial (Ra) e a massa em gramas (g) de cada espécime. Em seguida, os espécimes e as escovas foram posicionados em uma máquina simuladora de escovação (ODEME®, Luzerna, SC, Brasil). Os grupos foram submetidos a ciclos que simularam o uso contínuo das escovas por 3 meses. Para cada amostra, foi preparada uma pasta contendo a proporção em massa 1:2 de água destilada e pasta dental. Após a abrasão, a rugosidade e massa foram novamente mensuradas. As extremidades das cerdas foram observadas em um estereomicroscópio com magnitude de 45x. Os resultados foram submetidos ao teste estatístico de Análise de Variância com medidas repetidas no tempo (5%). Resultados: Não houve diferença estatística em massa para nenhum grupo antes e após abrasão (p = 0,727). No entanto, as escovas Oral B Indicator Plus® e Colgate Extra Clean® produziram superfícies mais rugosas (p = 0,002) quando comparada com Dr. Veit Soft® após abrasão. Conclusão: os resultados mostraram que existe variação no potencial de abrasão de escovas dentais classificadas comercialmente como cerdas macias de diferentes fabricantes.

There is a wide variety of toothbrushes available in the market with various clinical indications. However, there are few studies in literature that assess the abrasion of toothbrushes of different brands on composite resin restorations. Objective: the present study assessed the abrasion of three brands of soft bristles toothbrushes: Oral B Indicator Plus™, Colgate Extra Clean™, and Dr. Veit Soft™ on a restorative composite material. Materials and method: discs of composite material (8 mm x 2 mm) Tetric Ceram™ were produced and light cured with an LED unit for 40 seconds each. A total of 18 samples were made and divided in three experimental groups (n = 6). Superficial roughness (Ra) and mass in grams (g) of each sample were assessed. Then, the samples and toothbrushes were placed in a toothbrushing simulating machine (ODEME™, Luzerna, SC - Brazil). The groups were submitted to cycles simulating the continuous use of toothbrushes for 3 months. A paste containing the proportion in mass 1:2 of distilled water and dental paste was prepared for each sample. After abrasion, roughness and mass were measured again. The ends of the bristles were observed with a stereomicroscope at 45x magnitude. The results were submitted to ANOVA test with repeated measures over time (5%). Results: there was no statistical difference in mass for any group before and after toothbrush abrasion (p = 0.727). However, Oral B Indicator Plus and Colgate Extra Clean toothbrushes produced rougher surfaces (p = 0.002) than Dr. Veit Soft after abrasion. Conclusion: the results showed that there are variations in the potential for abrasion of toothbrushes commercially classified as soft bristles from different manufacturers.

Associação de compostos fluoretados no tratamento de lesões incipentes de cárie / The association of fluoride in the treatment of incipient caries lesions

A doença cárie, quando diagnosticada em seu estágio inicial, é passível de ser tratada de forma não invasiva através de agentes remineralizadores, como os fluoretos. Dentre os compostos fluoretados, destaca-se o dentifrício, que é o que apresenta o melhor custo benefício, devido à praticidade, baixo custo e freqüência de aplicações. Porém, em pacientes de alto risco e/ou de atividade de cárie, a associação de produtos fluoretados pode trazer benefícios adicionais. Neste sentido, o objetivo do presente estudo foi realizar um levantamento da literatura sobre as vantagens e desvantagens da associação de produtos fluoretados no tratamento remineralizador de lesões incipientes de cáries.

Banco de dentes humanos na percepção dos acadêmicos da faculdade de odontologia da Universidade Federal Fluminense / Dentistry students' knowledge about the human tooth bank of Universidade Federal Fluminense

O objetivo desta pesquisa foi avaliar o nível de informação dos alunos dos 4º, 5º e 6º períodos da Faculdade de Odontologia da Universidade Federal Fluminense (FO-UFF) acerca da importância do Banco de Dentes Humanos (BDH) e sua funcionalidade. Foram entrevistados 95 alunos, utilizando questionário com perguntas fechadas. Os resultados indicaram que 100% dos alunos tem consciência da existência do BDH na FO-UFF e que 71,3% tem conhecimento de sua finalidade. Esse conhecimento é diferenciado em função do período que o aluno esteja cursando (x2), sendo a proporção de alunos do 4º período significativamente menor (p<0,05). Os autores concluíra, que há necessidade de um maior trabalho de divulgação na população de alunos estudada sobre a importância do BDH.

This research’s goal was to evaluate the level of information known by the 4th, 5th and 6th terms’ students from the Dental School at Universidade Federal Fluminense (FO-UFF) about the importance of the Human Teeth Bank (BDH) and its functionality. There were 95 students in the research, and it was used an objective assessment. The results indicated that 100% of the students know about UFF´s Dental School teeth bank, and that 71,3% knowm it’s purpose. This knowledge depends on the term the student’s on (x2), and the proportion of students who are on their 4th term is highly smaller (p<0,05). The authors concluded that there’s a need to inform more the 4th, 5th and 6th terms’ students about the importance of BDH.