ABSTRACT
OBJECTIVE: The purpose of this study was to investigate the viscoelastic properties related to handling characteristics of composite resins. METHODS: A custom designed vertical oscillation rheometer (VOR) was used for rheological measurements of composites. The VOR consists of three parts: (1) a measuring unit, (2) a deformation induction unit and (3) a force detecting unit. Two medium viscous composites, Z100 and Z250 and two packable composites, P60 and SureFil were tested. The viscoelastic material function, including complex modulus E* and phase angle delta, were measured. A dynamic oscillatory test was used to evaluate the storage modulus (E'), loss modulus (E") and loss tangent (tandelta) of the composites as a function of frequency (omega) from 0.1 to 20 Hz at 23degrees C. RESULTS: The E' and E" increased with increasing frequency and showed differences in magnitude between brands. The E*s of composites at omega = 2 Hz, normalized to that of Z100, were 2.16 (Z250), 4.80 (P60) and 25.21 (SureFil). The magnitudes and patterns of the change of tandelta of composites with increasing frequency were significantly different between brands. The relationships between the complex modulus E*, the phase angle delta and the frequency omega were represented by frequency domain phasor form, E* (omega) = E*e(idelta) = E* 45 degree angle delta. CONCLUSIONS: The viscoelasticity of composites that influences handling characteristics is significant different between brands. The VOR is a relatively simple device for dynamic, mechanical analysis of high viscous dental composites. The locus of frequency domain phasor plots in a complex plane is a valuable method of representing the viscoelastic properties of composites.
Subject(s)
Composite ResinsABSTRACT
OBJECTIVES: The aim of this study was to investigate the effect of monomer and filler compositions on the rheological properties related to the handling characteristics of resin composites. METHODS: Resin matrices that Bis-GMA as base monomer was blended with TEGDMA as diluent at various ratio were mixed with the Barium glass (0.7 um and 1.0 um), 0.04 um fumed silica and 0.5 um round silica. All used fillers were silane treated. In order to vary the viscosity of experimental composites, the type and content of incorporated fillers were changed. Using a rheometer, a steady shear test and a dynamic oscillatory shear test were used to evaluate the viscosity (eta) of resin matrix, and the storage shear modulus (G'), the loss shear modulus (G"), the loss tangent (tandelta) and the complex viscosity (eta*) of the composites as a function of frequency omega = 0.1-100 rad/s. To investigate the effect of temperature on the viscosity of composites, a temperature sweep test was also undertaken. RESULTS: Resin matrices were Newtonian fluid regardless of diluent concentration and all experimental composites exhibited pseudoplastic behavior with increasing shear rate. The viscosity of composites was exponentially increased with increasing filler volume%. In the same filler volume, the smaller the fillers were used, the higher the viscosities were. The effect of filler size on the viscosity was increased with increasing filler content. Increasing filler content reduced tandelta by increasing the G' further than the G". The viscosity of composites was decreased exponentially with increasing temperature.
Subject(s)
Barium , Bisphenol A-Glycidyl Methacrylate , Glass , Rheology , Silicon Dioxide , ViscosityABSTRACT
The aim of this study was to measure the cusp deflection during composite restoration for MOD cavity in premolar and to examine the influence of cavity dimension, C-factor and restoration method on the cusp deflection. Thirty extracted maxillary premolar were prepared to four different sizes of MOD cavity and divided into six groups. The width and depth of the cavity were as follows. Group 1; 1.5 x 1 mm, Group 2; 1.5 x 2 mm, Group 3; 3 x 1 mm, and Group 4-6; 3 x 2 mm respectively. Group 1-4 were restored using bulk filling method with Z-250 composite. However, Group 5 was restored incrementally, and Group 6 was restored with an indirect resin inlay. The cusp deflection was recorded at the buccal and lingual cusp tips using LVDT probe for 10,000 seconds. The measured cusp deflections were compared between groups, and the relationship between the cube of the length of cavity wall/the cube of the thickness of cavity wall (L3 / T3), C-factor and cusp deflection or %flexure (100 x cuspal deflection / cavity width) was analyzed. The cusp deflection of Group 1-4 were 12.1 microm, 17.2 microm, 16.2 microm and 26.4 microm respectively. The C-factor was related to the %flexure rather than the cusp deflection. There was a strong positive correlationship between the L3 / T3 and the cusp deflection. The cusp deflection of Group 5 and 6 were 17.4 microm and 17.9 microm respectively, which are much lower value than that of Group 4.