Microhardness of glass ionomer cements indicated for the ART technique according to surface protection treatment and storage time

The aim of this study was to assess the microhardness of 5 glass ionomer cements (GIC) - Vidrion R (V, SS White), Fuji IX (F, GC Corp.), Magic Glass ART (MG, Vigodent), Maxxion R (MR, FGM) and ChemFlex (CF, Dentsply) - in the presence or absence of a surface protection treatment, and after different storage periods. For each GIC, 36 test specimens were made, divided into 3 groups according to the surface protection treatment applied - no protection, varnish or nail varnish. The specimens were stored in distilled water for 24 h, 7 and 30 days and the microhardness tests were performed at these times. The data obtained were submitted to the ANOVA for repeated measures and Tukey tests (á = 5 percent). The results revealed that the mean microhardness values of the GICs were, in decreasing order, as follows: F > CF = MR > MG > V; that surface protection was significant for MR, at 24 h, without protection (64.2 ± 3.6a), protected with GIC varnish (59.6 ± 3.4b) and protected with nail varnish (62.7 ± 2.8ab); for F, at 7 days, without protection (97.8 ± 3.7ab), protected with varnish (95.9 ± 3.2b) and protected with nail varnish (100.8 ± 3.4a); and at 30 days, for F, without protection (98.8 ± 2.6b), protected with varnish (103.3 ± 4.4a) and protected with nail varnish (101 ± 4.1ab) and, for V, without protection (46 ± 1.3b), protected with varnish (49.6 ± 1.7ab) and protected with nail varnish (51.1 ± 2.6a). The increase in storage time produced an increase in microhardness. It was concluded that the different GICs, surface protection treatments and storage times could alter the microhardness values.

Bond strength of resin modified glass ionomer cement to primary dentin after cutting with different bur types and dentin conditioning

The aim of this in vitro study was to evaluate the effect of different bur types and acid etching protocols on the shear bond strength (SBS) of a resin modified glass ionomer cement (RM-GIC) to primary dentin. Forty-eight clinically sound human primary molars were selected and randomly assigned to four groups (n=12). In G1, the lingual surface of the teeth was cut with a carbide bur until a 2.0-mm-diameter dentin area was exposed, followed by the application of RM-GIC (Vitremer - 3M/ESPE) prepared according to the manufacturer's instructions. The specimens of G2, received the same treatment of G1, however the dentin was conditioned with phosphoric acid. In groups G3 and G4 the same procedures of G1 and G2 were conducted respectively, nevertheless dentin cutting was made with a diamond bur. The specimens were stored in distilled water at 37ºC for 24h, and then tested in a universal testing machine. SBS. data were submitted to 2-way ANOVA (= 5 percent) and indicated that SBS values of RM-GIC bonded to primary dentin cut with different burs were not statistically different, but the specimens that were conditioned with phosphoric acid presented SBS values significantly higher that those without conditioning. To observe micromorphologic characteristics of the effects of dentin surface cut by diamond or carbide rotary instruments and conditioners treatment, some specimens were examined by scanning electron microscopy. Smear layer was present in all specimens regardless of the type of rotary instrument used for dentin cutting, and specimens etched with phosphoric acid presented more effective removal of smear layer. It was concluded that SBS of a RM-GIC to primary dentin was affected by the acid conditioning but the bur type had no influence.

Avaliação clínica da laserterapia no tratamento da hipersensibilidade dentinária / Clinical evalutation of lasertherapy on dentin hypersensitivity treatment

O objetivo deste estudo foi avaliar clinicamente a eficácia do tratamento de hipersensibilidade dentinária por meio dolaser AsGaAl e Nd:YAG. Foram selecionados 14 pacientes (72 dentes) da clínica de Dentística da FOSJCûUNESP que apresentavam sensibilidade dentinária aos testes táctil e evaporativo. Os pacientes foram divididos aleatoriamente emdois grupos de sete indivíduos (36 dentes), de acordo com o tipo de tratamento: laser de baixa intensidade de AsGaAl (Three Light - Clean Line) e laser de alta intensidade de Nd:YAG (Pulse Master 600IQ - American Dental Technologies). O laser AsGaAl foi ajustado em 50mW/2J, aplicado com contato, em 4 pontos na região cervical do dente: mesial, médio, distal da face vestibular e um ponto na face lingual. O laser Nd:YAG foi ajustado em 30mJ/10Hz, aplicado por varredura não contato, por 2min. Foram realizadas 4 aplicações, com intervalos de sete dias, e os pacientes atribuíam escores para os testes táctil e evaporativo realizados antes e depois da aplicação do laser. Os dados foram submetidos à análise de variância não paramétrica de Friedman e teste de comparação múltipla de Dunn (p<0,05), e demonstraramque ambos os grupos apresentaram diferença estatisticamente significante entre a condição inicial sem tratamento e a última aplicação do laser para os testes táctil e evaporativo. Concluiu-se que o laser de AsGaAl e o laser de Nd:YAG são efetivos no tratamento de hipersensibilidade dentinária e que não houve diferença significante entre os resultados obtidos entre o laser de AsGaAl e o laser de Nd:YAG.

Effect of surface treatment on the shear bond strength of a resin-based cement to porcelain

The purpose of this in vitro study was to evaluate the effect of different surface treatments on the shear bond strength of a resin-based cement to porcelain. Sixty pairs of 50 percent aluminous porcelain discs were fabricated. In each pair, one disc measured 6 mm in diameter X 3 mm thickness (A) and the other measured 3 mm in diameter X 3mm thickness (B). The specimens were randomly assigned to 6 groups (n=10 pairs of discs), according to the surface treatment: etching with 10 percent hydrofluoric acid for 2 or 4min (G1 and G2); 50-æm particle aluminum oxide sandblasting for 5 s (G3); sandblasting followed by etching for 2 or 4min (G4 and G5) and control - no treatment (G6). A silane agent was applied to the treated surface of both discs of each pair. Bistite II DC dual-cure resin cement was applied and the B discs were bonded to their respective A discs. Specimens were stored in distilled water at 37°C for 24 h and were tested in shear strength at a crosshead speed of 2 mm/min. Means in MPa were: G1: 14.21 ± 4.68; G2: 8.92 ± 3.02; G3: 10.04 ± 2.37; G4: 12.74 ± 5.15; G5: 10.99 ± 3.35; G6: 6.09 ± 1.84. Data were compared by one-way ANOVA and Tukey's test at 5 percent significance level. Bond strength recorded after 2-min acid etching was significantly higher than 4-min etching (p<0.05) and control (p<0.05), but did not differ significantlyfrom sandblasting alone (p>0.05) or followed by etching for 2 or 4 min (p>0.05). Within the limitations of an in vitro study, it may be concluded that 2-min hydrofluoric acid etching produced a favorable micromechanical retention that enhanced resin cement bond strength to porcelain.

O objetivo deste estudo in vitro foi avaliar o efeito de diferentes tratamentos de superfície na resistência ao cisalhamento da união entre porcelana e cimento resinoso. Foram confeccionados sessenta pares de discos de porcelana aluminizada a 50 por cento, de 6 mm de diâmetro por 3 mm de espessura (A) e 3 mm de diâmetro por 3 mm de espessura (B). Os espécimes foram divididos aleatoriamente em 6 grupos (n=10 pares), de acordo com os tratamentos de superfície: condicionamento com ácido fluorídrico por 2 e 4 min (G1 e G2), jateamento com óxido de alumínio (50 æm) por 5 s (G3), jateamento seguido de ácido fluorídrico por 2 e 4 min (G4 e G5) e controle (G6). Em seguida, foi aplicado silano na superfície tratada de ambos os discos, e os discos B foram cimentados sobre os respectivos discos A, utilizando o cimento resinoso dual Bistite II DC. Os espécimes foram armazenados em água destilada a 37°C por 24 h, para posterior teste de cisalhamento em máquina de ensaio universal. As médias em MPa foram: G1: 14,21 ± 4,68; G2: 8,92 ± 3,02; G3: 10,04 ± 2.37; G4: 12,74 ± 5,15; G5: 10,99 ± 3,35; G6: 6,09 ± 1,84. Os dados foram submetidos à análise de variância a um critério e teste de Tukey (p<0,05). O condicionamento ácido por 2 min apresentou resultados significantemente superiores ao condicionamento por 4 min (p<0,05) e ao grupo controle (p<0,05), porém não diferiu estatisticamente do jateamento, associado ou não ao ácido fluorídrico por 2 ou 4 min (p>0,05). Dentro das limitações de um estudo in vitro, conclui-se que o condicionamento com ácido fluorídrico por 2 min produziu uma retenção micromecânica favorável, que aumentou a resistência de união entre o cimento resinoso e a porcelana.

Influência da espessura da cerâmica na fotopolimerização de cimentos resinosos / Influence of ceramic thickness on light curing of resin cement

O objetivo deste trabalho foi verificar, por meio de validação da microdureza, a interferência de diferentes espessuras (0,1 e 2mm) de cerâmica IPS Empressll na fotopolimerização dos cimentos resinosos duais Variolink (V) e Enforce (E). As amostras foram divididas em seis grupos (n= 12) de acordo com o cimento e a espessura da barreira cerâmica: VO - sem barreira; V1 - 1mm; V2- 2mm; EO - sem barreira; E1 - 1mm; E2 - 2mm. As médias (± desvio - padrão) obtidas foram: VO - 47,88 ± 2,24; V1 - 44,42 ± 2,71; V2 - 39,15 ± 1,98; E0 - 54,70 ± 3,36; E1 - 50,34 ± 2,68; E2 - 44,16 ± 2,95. Concluiu-se que a interposição da cerâmica reduziu microdureza dos cimentos e que o Enforce apresentou uma microdureza superior ao Variolinkll.

Efeitos do condicionamento ácido sobre fissuras de molares decíduos: estudo in vitro ao microscópio eletrônico de varredura / Effects of acid etching on fissures of primary molars: an in vitro study by scanning electron microscopy

O objetivo deste estudo in vitro foi avaliar os padrões de condicionamento ácido exibidos nas fissuras de molares decíduos, após a aplicação do ácido fosfórico a 35 por cento, com diferentes tempos de condicionamento. Foram utilizados 12 segundos molares decíduos, que foram divididos em três grupos, conforme o tempo de condicionamento ácido: G1 - 15 segundos; G2 - 30 segundos; G3 - 45 segundos. Os padrões de condicionamento ácido foram avaliados ao microscópio eletrônico de varredura. As amostras do Grupo 1 apresentaram predominância do padrão tipo II, e nas amostras do Grupo 2 e 3 foi observada uma predominância do padrão tipo I. Em todas as amostras não foi observado condicionamento ácido no fundo da fissura