Effect of bleaching agent on dental ceramics roughness

The aim of this study was to assess the effect of bleaching agents (10% and 16% carbamide peroxide) on the roughness of two dental ceramics in vitro, and to analyze the surface by scanning electronic microscopy (SEM). Two bleaching agents (10% and 16% / Whiteness, FGM Gel) and two microparticle feldspathic ceramics (Vita VM7 and Vita VM13) were used. Forty disks of Vita VM7 and Vita VM13 ceramic were manufactured, measuring 4mm in diameter and 4mm high, in accordance with the manufacturers’ recommendations, and were divided into 4 groups (n=10): (1) VM7 + Whiteness 10%; (2) VM7 + Whiteness 16%; (3) VM13 + Whiteness 10%; (4) VM13 + Whiteness 16%. The bleaching agent was applied for 8 hours a day for 15 days and during the intervals the test specimens were stored in distilled water at 37°C. The roughness (Ra) of the test specimens was evaluated before and after exposure to the bleaching agents using a laser roughness meter and the topographic description was analyzed by SEM. The statistical analysis of roughness data showed significant differences in the VM7 groups, using paired t-test, p=0.05 (VM7 + Whiteness 10%: p=0.002; VM7 + Whiteness 16%: p=0.001) and two-sample t-test (VM7 p=0,047), and no significant difference was found among VM13 groups. The qualitative SEM analysis showed different degrees of surface changes. The results suggest that the roughness of the tested ceramic surfaces increased after exposure to the bleaching agents.

O objetivo do estudo foi avaliar o efeito de agente clareador (10% e 16% de peroxido de carbamida) na rugosidade de duas ceramicas dentais in vitro e analisar a superficie atraves da microscopia eletronica de varredura (SEM). Foram utilizados dois agentes clareadores (10% e 16% / Whiteness, FGM Gel) e duas ceramicas feldspaticas microparticuladas (Vita VM7 e Vita VM13). Foram confeccionados quarenta discos de ceramica Vita VM7 e Vita VM13, com 4mm de diametro e 4mm de altura, de acordo com as recomendacoes do fabricante, sendo divididos em 4 grupos (n=10): G1- VM7 + Whiteness 10%, G2- VM7 + Whiteness 16%, G3- VM13 + Whiteness 10% e G4- VM13 + Whiteness 16%. O agente clareador foi aplicado por 8 horas durante 15 dias e durante os intervalos os corpos de prova (cp) ficavam armazenados em agua destilada a 37°C. A rugosidade (Ra) dos cp foi avaliada antes e apos a exposicao aos agentes clareadores utilizando o rugosimetro a laser Perthomether S8P, e a descricao topografica foi analisada no MEV. A analise estatistica na rugosidade mostrou diferenca significante entre os grupos da VM7, usando o teste pareado, p=0.05 (VM7 + Whiteness 10%: p=0.002; VM7 + Whiteness 16%: p=0.001) e nao foi encontrado diferenca estatistica para os grupos da VM13. A descricao qualitativa no SEM evidenciou alteracao nas superficies em diferentes graus. Os resultados sugeriram que as superficies das ceramicas testadas aumentaram a rugosidade apos a exposicao ao agente clareador.

The effect of carbamide peroxide bleaching agents on the microhardness of dental ceramics

This study examined the effect of 10% and 16% carbamide peroxide bleaching agents on the surface microhardness of micro-particulate feldspathic ceramics (VM7 and VM13, Vita Zahnfabrik). Forty specimens (8-mm diameter, 2-mm thickness) were divided into four groups (n=10): G1- VM7 + 10% Whiteness, G2- VM7 + 16% Whiteness, G3- VM13 + 10% and G4- VM13 + 16% Whiteness. The home-use bleaching agents were applied for 8 hours on 15 days, and the specimens were stored in distilled water at 37°C. The Vickers hardness number (HV) was determined for each specimen. Data were analyzed by the Wilcoxon and Mann- Whitney tests (p<0.05). The microhardness values before exposure were: g1- 433 (57); g2- 486 (22); g3- 509 (28); g4- 518 (24), and after exposure: G1- 349 (32); G2- 496 (95); G3- 519 (38); G4- 502 (81). G2 exhibited a higher and significant difference than G1 in VM7 groups, and the effect of bleaching concentration was shown to be significant by the Mann-Whitney test. And for VM13, both the Wilcoxon and Mann-Whitney tests showed no significant differences. When using 10% carbamide peroxide, the microhardness of VM7 ceramic was affected, and there were no effect on the microhardness between VM7 and VM13 ceramics when 16% carbamide peroxide was used.

Este estudo examinou o efeito do agente clareador peroxido de carbamida a 10% e a 16% na microdureza superficial de ceramicas feldspaticas micro-particuladas (VM7 e VM13, Vita Zahnfabrik). Quarenta corpos-de-prova (8 mm de diametro, 2 mm de espessura) foram divididos em quatro grupos (n=10): G1- VM7 + 10% Whiteness, G2- VM7 + 16% Whiteness, G3- VM13 + 10% e G4- VM13 + 16% Whiteness. Os agentes clareadores foram aplicados por 8 horas durante 15 dias e os cp foram armazenados em agua destilada a 37°C. A dureza Vickers (HV) de cada cp foi determinada. Os dados foram analisados pelos testes de Wilcoxon e Mann-Whitney (p<0.05). Os valores da dureza antes da exposicao ao agente clareador foram: g1- 433 (57); g2- 486 (22); g3- 509 (28); g4- 518 (24), e depois da exposicao: G1- 349 (32); G2- 496 (95); G3- 519 (38); G4- 502 (81). G2 exibiu diferenca significante e microdureza maior comparado ao G1 nos grupos da VM7 e o efeito da concentracao do clareador foi significante, apresentados atraves dos testes Mann-Whitney. Para VM13, ambos testes, Wilcoxon e Mann-Whitney, nao apresentaram diferenca significante. Quando o peroxido de carbamida a 10% foi avaliado, a microdureza da ceramica VM7 foi afetada, e nao houve diferenca na microdureza entre as ceramicas VM7 e VM13 quando o peroxido de carbamida a 16% foi utilizado.