ABSTRACT
Objective The generate of posterior capsular opacification(PCO)is associated with the adhensive and migration of residual subcapsular lens epithelial cells(LECs).Titanium dioxide(TiO_2)nanometer is proved to have the ability of killing tumor cells and cultured bovine LECs.This study tried to observe the effects of TiO_2 nanometer thin film provoked by light on adhesiveness and migration of bovine LECs in vitro.MethodsThe fresh bovine lenses were obtained and cultured in DMEM containing 10% of newborn bovine serum.The second to fifth generation of cells were used in this experiment.The slide modified by TiO_2 photocatalyst film was prepared by sol-gel method.Cultured cells were seeded in filmed or unfilmed slides respectively and exposed to ultraviolet(wavelength 365 nm)for 20 or 40 minutes.The contact angle between water drop and slide was measured by droping method and the cells adhered to slides were calculated after 24 and 48 hours of culture.The growth status and migration distance of bovine LECs were assayed and compared between filmed and unfilmed groups.ResultsThe contact angle between water drop and slide was 0°±2°and 18.825°±2.342° in filmed and unfilmed group respectively,indicating a obviously smaller contact angle in TiO_2 filmed group than unfilmed one.The numbers of bovine LECs adhered to filmed slide was considerably reduced in TiO_2 filmed group compared with unfilmed group in different UVA exposure time(t_(0 min)=5.492,P=0.001;t_(20 min)=6.031,P=0.000;t_(40 min)=6.828,P=0.000).However,no significant difference was found in the numbers of adhensive cells among 3 UVA irradiation time points(F=1.278,P=0.297).The migration distance of the cells was significantly shorter in TiO_2 filmed group in comparison with unfilmed group in 24 and 48 hours after UVA irradiation(F_(group)=14.965,P=0.000;F_(time)=38.033,P=0.000).ConclusionThe TiO_2 nanometer thin film is characterized by the superhydrophilic property.So it can effectively impede the adhesion and migration of bovine LECs in vitro.