Chinese Journal of Tissue Engineering Research ; (53): 4033-4037, 2015.
Article in Chinese | WPRIM | ID: wpr-461896

ABSTRACT

BACKGROUND:Bacterial adhesion is closely related to the surface properties of cobalt-chromium al oys, and therefore, the surface modification technology has become the focus of research in this area. OBJECTIVE:To verify whether the cobalt-chromium al oy with zirconium nitride coating can improve the bacterial adhesion of metal denture materials. METHODS:Magnetron sputtering deposition method was used to plate zirconium nitride film on the surface of cobalt-chromium al oys (experimental group), and cobalt-chromium al oy specimens uncoated served as control group. Streptococcus mutans, Candida albicans, and Actinomyces viscosus were respectively inoculated on the two kinds of test specimen, and at end of culture, the colony counting was done. RESULTS AND CONCLUSION:In the bacterial adhesion test, the number of colonies of three kinds of bacteria in the experimental group was significantly lower than that in the control group (P<0.05). The number of bacterial adhesion in the control group was significantly higher than that in the experimental group. These findings indicate that the cobalt-chromium al oy covered with zirconium nitride coating can significantly reduce the adhesion amount of Streptococcus mutans, Candida albicans and Actinomyces viscosus, and thus improve bacterial adhesion properties of cobalt-chromium al oys.

SELECTION OF CITATIONS
SEARCH DETAIL