ABSTRACT
Abstract To evaluate the effect of acidic challenge on erosion depth and topographic characteristics of different materials used as occlusal sealants. Two hundred specimens of five sealant materials (Fuji IX, Ketac Molar, Fuji II, Equia and Clinpro) and forty bovine teeth enamel samples (control) were prepared and exposed to acidic challenge. The specimens were immersed in four different solutions (orange juice, coke drink, citric acid or distilled water) under mildly shaken conditions for 3 days. The erosion depth profiles were measured using a profilometer and Scanning Electron Microscope (SEM). Two-way ANOVA with Tukey post-hoc test was performed to evaluate the interactions. Sealant material and acidic challenge had significant effects on erosion depth. Among the materials, Fuji II presented the highest mean of erosion depth after immersion in orange juice, coke drink, and citric acid. All materials groups presented higher erosion depth values after immersion in the citric acid solution, except Clinpro. Bovine enamel presented higher erosion depth values compared to all materials when submitted to erosive challenge. Sealant materials submitted to the acidic challenge presented different degrees of erosion and topographic modification; however, they are less susceptible to erosion than bovine teeth enamel.
ABSTRACT
ABSTRACT Objectives: To evaluate the translucency, contrast ratio and masking ability of a translucent zirconia with different thicknesses. Methods: Disc shaped specimens (n= 3) with 10 mm (Ø) x 1.5 mm, 1 mm and 0.7 mm (thickness) were manufactured simulating all-ceramic simplified restorations. Substrate discs (n= 2; Ø: 10 mm; thickness: 2 mm) were simulated with composite resin shades: A2 (positive control) and C4; and metal alloys: silver (Ni-Cr) and golden (Cu-Al). Optical properties of the 9 translucent zirconia specimens placed on the 3 different substrates were analyzed by a spectrophotometer. The color variation (ΔE00) between each ceramic structure over the positive control substrate (A2) and over the dark backgrounds (C4, silvery, golden) were obtained as to their ceramic masking ability and subjected to non-parametric Kruskal Wallis test (5%). The translucency parameter (TP00) and contrast ratio (CR) of the different thicknesses of the ceramic discs were also collected and analyzed by one-way ANOVA and the Tukey test (5%). Results: The translucent zirconia showed greater opacity in the thickness of 1.5 mm, although it was not statistically different between 0.7 and 1.0 mm. All dark backgrounds significantly affected the final color of the simplified restoration in all evaluated thicknesses. However, the increase in ceramic thickness showed a decrease in ΔE00 values for all substrates. Conclusion: The translucent zirconia was not able to mask the dark substrates, independent of the evaluated thickness.
RESUMO Objetivos: Avaliar a translucidez, razão de contraste e capacidade de mascaramento de uma zircônia translúcida com diferentes espessuras. Métodos: Espécimes em forma de disco (n= 3) com 10 mm (Ø) x 1,5 mm, 1 mm e 0,7 mm (espessura) foram confeccionados simulando restaurações simplificadas em cerâmica pura. Discos de substrato (n= 2; Ø: 10 mm; espessura: 2 mm) foram simulados com as cores de resina composta: A2 (controle positivo) e C4; e ligas metálicas: prata (Ni-Cr) e ouro (Cu-Al). As propriedades ópticas dos 9 espécimes de zircônia translúcida posicionados nos 3 substratos diferentes foram analisadas por um espectrofotômetro. A variação de cor (ΔE00) entre cada espécime cerâmico sobre o substrato controle positivo (A2) e sobre os fundos escuros (C4, prateado, dourado) foi calculada quanto à capacidade de mascaramento da cerâmica e submetida ao teste não paramétrico de Kruskal Wallis (5%). O parâmetro de translucidez (TP00) e a razão de contraste (CR) das diferentes espessuras dos discos cerâmicos também foram coletados e analisados por ANOVA de uma via e teste de Tukey (5%). Resultados: A zircônia translúcida apresentou maior opacidade na espessura de 1,5 mm, embora não tenha sido estatisticamente diferente entre 0,7 e 1,0 mm. Todos os fundos escuros afetaram significativamente a cor final da restauração simplificada em todas as espessuras avaliadas. No entanto, o aumento da espessura da cerâmica mostrou uma diminuição nos valores de ΔE00 para todos os substratos. Conclusão: A zircônia translúcida não foi capaz de mascarar os substratos escuros, independente da espessura avaliada.