Braz. dent. j ; Braz. dent. j;34(4): 34-43, July-Aug. 2023. tab, graf
Article in English | LILACS-Express | LILACS, BBO | ID: biblio-1520331

ABSTRACT

Abstract This study evaluated the effect of heating on the physicochemical properties and surface changes of tricalcium silicate sealers. Three tricalcium silicate root canal sealers (Bio-C Sealer, BioRoot-RCS, EndoSequence BC Sealer), and one epoxy resin-based sealer (AH Plus; control) were tested. The effect of heating on setting time (ST) and flowability were assessed according to ANSI/ADA 57 and ISO 6876 standards. Solubility and dimensional change (DC) of the set sealers were evaluated at 24 hours and after 30 days; the pH of the water used in the DC testing was also measured. Tests were repeated with heated sealers in an oven at 100 °C for 1 min. SEM and EDS analysis were performed. Data were analyzed using One-Way ANOVA and Tukey post-hoc tests (α=5%). Heating decreased the ST for AH Plus and EndoSequence (p<0.05). Heating reduced flowability (p<0.05) and increased pH for AH Plus (p<0.05). The solubility of Bio-C (dried specimens) was not in accordance with the ANSI/ADA standard. The solubility of EndoSequence was significantly higher (p<0.05) when it was heated and dried after 30 days. DC of Bio-C (24 h and 30 days), BioRoot-RCS (30 days) and AH Plus (24 h and 30 days) were not in accordance with the standards. SEM and EDS analysis showed significant changes in sealer microstructure after heating. In conclusion, heating decreased the ST and increased the solubility of EndoSequence BC sealer. No significant changes in flowability, DC, and pH were identified for all three tricalcium silicate sealers after heat application. However, all sealers had significant surface changes.


Resumo Este estudo avaliou o efeito do aquecimento nas propriedades físico-químicas e nas alterações superficiais de cimentos de silicato tricálcico. Três cimentos endodônticos de silicato tricálcico (Bio-C Sealer, BioRoot-RCS, EndoSequence BC Sealer) e um cimento à base de resina epóxi (AH Plus) foram testados para avaliar o efeito do aquecimento no tempo de presa (TP) e escoamento de acordo com as normas ANSI/ADA 57 e ISO 6876. A solubilidade e alteração dimensional (AD) dos cimentos foram avaliadas após 24 horas e 30 dias. O pH da água usada no teste de AD também foi medido. Os testes foram repetidos com cimentos aquecidos em um forno a 100 °C por 1 min. Análises em MEV e EDS foram realizadas. Os dados foram analisados pelos testes de ANOVA-1 via e post hoc de Tukey (α=5%). O aquecimento diminuiu o TP para AH Plus e EndoSequence (p<0,05). O aquecimento reduziu o escoamento (p<0,05) e aumentou o pH do AH Plus (p<0,05). A solubilidade do Bio-C (amostras desidratadas) não estava de acordo com o padrão ANSI/ADA. A solubilidade da EndoSequence foi significativamente maior (p<0,05) quando aquecida e desidratada após 30 dias. As AD de Bio-C (24 h e 30 dias), BioRoot-RCS (30 dias) e AH Plus (24 h e 30 dias) não estavam de acordo com as normas ADA e ISO. A análise em MEV e EDS mostrou alterações significativas na estrutura dos cimentos após aquecimento. Em conclusão, o aquecimento diminuiu o TP e aumentou a solubilidade do cimento EndoSequence BC. Não foram identificadas mudanças significativas no escoamento, AD e pH para os cimentos de silicato tricálcico após aquecimento. Porém, todos os cimentos tiveram alterações significativas na superfície.

2.
Braz. dent. sci ; 16(3): 56-62, 2013. tab
Article in English | LILACS, BBO | ID: lil-707563

ABSTRACT

Objetivo: O objetivo deste estudo foi avaliar a resistência de união dentinária tratada com clorexidina, ácido hialurônico, vitamina C e chá verde. Material e Métodos: As raízes de 50 dentes bovinos foram removidas e a superfície de dentina vestibular exposta. Após o condicionamento ácido, os espécimes foram divididos em 5 grupos (n = 10), de acordo com as estratégias adesivas na dentina: CO - dentina não tratada; CHX – tratamento com clorexidina 2% por 30 s; HA - tratamento com ácido hialurônico 1% por 30 s; VC - tratamento com vitamina C 10% por 30 s; GT – tratamento com extrato de chá verde 1% por 30 s. Sistema adesivo Adper Single Bond II foi aplicado segundo recomendações do fabricante. Os espécimes foram restaurados com uma camada de 4 mm de espessura de resina composta, que foi polimerizada por 40 s. As amostras foram armazenadas em água destilada a 37 ° C durante 24 h, e seccionada em palitos de 1 x 1 mm2 contendo a interface adesiva. Teste de microtração foi realizado com uma máquina de ensaios universal a uma velocidade de 0,5 mm/min. Resultados: Os resultados foram analisados com teste de variância ANOVA um-fator e testes de múltipla comparação de Tukey (p < 0,05). Grupo GT apresentou os maiores valores de resistência de união (29,4 ± 3,1) a, mas sem diferença significativa em relação aos demais grupos experimentais HA (26,7 ± 3,1) ab, CHX (25,4 ± 2,6) ab e VC (22,4 ± 6,0) b. Resistência de união dos grupos experimentais não foi significativamente diferente do grupo CO. Conclusão: a resistência de união imediata foi mantida mesmo após os diferentes tratamentos dentinários.


Objective: The aim of this study was to evaluate the bond strength of dentin treated with chlorhexidine, hyaluronic acid, vitamin C and green tea. Material and Methods: The roots of 50 bovine teeth were removed and buccal coronal dentin was exposed. After acidetching, the specimens were divided into 5 groups (n= 10), according to the dentin treatment strategy: CO -untreated dentin; CHX - treated with 2 wt% chlorhexidine for 30 s; HA - treated with 1 wt% hyaluronic acid for 30s; VC - treated with 10 wt% vitamin C for 30 s; GT - treated a 1% green tea extract for 30 s. Adper Single Bond was then applied to the treated according to the manufacturer’s recommendations. The specimens were restored with a 4 mm thick layer of the resin composite, which was polymerized for 40 s. The specimens were stored in distilled water at 37°C for 24 h and sectioned into 1 x 1 mm2 sticks containing the adhesive interface. Microtensile bond strength testing was performed with a universal testing machine at a cross-head speed of 1.0 mm/min. Results: The results were analyzed with onefactor ANOVA and Tukey’s multiple comparison tests. GT group presented the highest values bond strength (29.4 ± 3.1) a, but no significant difference compared to the other experimental groups HA (26.7 ± 3.1) ab, CHX (25.4 ±2.6) ab and VC (22.4 ± 6.0) b. Bond strengths of experimental groups were not significantly different from the CO. Conclusion: Immediate bond strength was preserved after acid-etched dentin was treated.


Subject(s)
Animals , Cattle , Ascorbic Acid , Camellia sinensis , Chlorhexidine , Hyaluronic Acid
3.
J. appl. oral sci ; J. appl. oral sci;12(3): 171-176, July-Sept. 2004. ilus, tab
Article in English | LILACS, BBO | ID: lil-392449

ABSTRACT

As técnicas adesivas permitiram inovações nos tratamentos restauradores da atualidade. Este estudo investigou a qualidade de união de diferentes sistemas adesivos ao substrato dentinário afetado e infectado por cárie, através de testes de microtração e microscopia eletrônica de transmissão e varredura (MET). Os resultados sugerem que a resina adesiva pôde infiltrar na dentina infectada e envolver as bactérias na camada híbrida. Esse conceito de controle da cárie foi denominado de "Restauração-Selante Modificada" (RSM). Por outro lado, a empresa Kuraray Med. Inc .(Japão) desenvolveu um sistema adesivo com propriedades anti-bacterianas (ABF), o qual é comercializado nos EUA como Protect Bond. Para avaliar a efetividade do sistema ABF sobre cáries radiculares, empregou-se testes de resistência adesiva e análise por microscopia eletrônica. O sistema ABF foi capaz de formar uma estrutura interfacial semelhante à camada híbrida, através da infiltração na superfície da dentina cariada radicular e os valores de resistência de união foram em média de 23 MPa. Os achados sugerem que a combinação da técnica RSM com o sistema ABF parece ser uma alternativa para o emprego da terapia de mínima invasão em cáries radiculares.


Subject(s)
Dentin-Bonding Agents , Dental Caries , Dentin , Anti-Bacterial Agents , Bacterial Infections
4.
J. appl. oral sci ; J. appl. oral sci;12(n.esp): 12-25, 2004. ilus, graf
Article in English | LILACS, BBO | ID: lil-362607

ABSTRACT

Over the last decade, the classic concept of 3-step bonding to dental tissues has developed rapidly to more user-friendly, simplified adhesive systems. These comprise the total-etch 2 step, self-etch 2step and the self-etch "all-in-one" adhesives. These adhesives carry along with simplicity some characteristics that are relevant to their efficacy in providing long-lasting bond stability. They share with the glass ionomer cements a class of materials that have high affinity for water. Such hydrophilicity renders such adhesives very permeable and denies their ability to hermetically seal dentin surfaces. Additionally, the water flux across simplified adhesives may compromise bonding in certain circumstances and their durability in the oral environment. This paper presents evidences of the water transport across simplified adhesive systems and glass ionomer cements and relates them with clinical implications of the phenomenon.


Subject(s)
Dentin-Bonding Agents , Water Movements , Cell Membrane Permeability , Tooth Permeability