Influence of surface treatments in flexural strength and superficial topography of a lithium disilicate ceramic / Influência dos tratamentos de superfície na resistência à flexão e na topografia superficial de uma cerâmica de dissilicato de lítio

Objective: The aim of the study was to evaluate the influence of different surface post-etching treatments in flexural strength, contact angle and surface roughness of a lithium disilicate ceramic. Material and Methods: 60 bars (16 x 2 x 4 mm) were divided in six groups (n=10): C, no treatment; HF, hydrofluoric acid for 20 s (HF) + washing (60 s), drying (30s); HFL, HF + washing (60 s), drying (30 s) and luting; HFNL, HF + washing (60 s) + neutralization with sodium bicarbonate (SB) for 40 s + washing (5s), drying (30 s) and luting; HFUL, HF + washing (60 s) + ultrasonic bath (UB) for 4 min, drying (30 s) and luting; HFNUL, HF + washing (60 s) + SB (40 s) + UB (4 min) and luting. The bars were submitted to three-points flexural strength test. 25 ceramic blocks (12 x 7 x 7 mm) were divided into five groups (n=5) to evaluate roughness and contact angle C - no treatment; HF - HF ; HFU - HF and UB for 5 min ; HFN - HF and SB; HFNU - HF, UB and SB. A scanning electron microscope (SEM) showed the surface of the samples. ANOVA one-way statistical analysis was done for comparison of results. Results: There was no statistical difference for flexural strength (p-value = 0.15) and for surface roughness (p-valor = 0.15). However, it was obtained statistically significant difference for contact angle (p-valor = 0.00). SEM images showed precipitates after the acid etching, which were removed by post-etching treatments. Conclusion: It can be concluded that the different post-etching surface treatments did not increase the flexural strength, surface roughness, but it influenced the ceramic wetting and SEM images (AU)

Objetivo: O objetivo do estudo foi avaliar a influência de diferentes tratamentos pós-condicionamento na resistência à flexão, ângulo de contato e rugosidade superficial de uma cerâmica de dissilicato de lítio. Material e Métodos: 60 barras (16 x 2 x 4 mm) foram divididas em seis grupos (n = 10): C, sem tratamento; HF, ácido fluorídrico durante 20 s (HF) + lavagem (60 s), secagem (30 s); HFL, lavagem com HF + (60 s), secagem (30 s) e cimentação; HFNL, HF + lavagem (60 s) + neutralização com bicarbonato de sódio (SB) por 40 s + lavagem (5s), secagem (30 s) e cimentação; HFUL, HF + lavagem (60 s) + banho ultrassônico (UB) por 4 min, secagem (30 s) e cimentação; HFNUL, HF + lavagem (60 s) + SB (40 s) + UB (4 min) e cimentação. As barras foram submetidas ao teste de resistência à flexão de três pontos. 25 blocos cerâmicos (12 x 7 x 7 mm) foram divididos em cinco grupos (n = 5) para avaliação da rugosidade superficial e ângulo de contato C - sem tratamento; HF - HF; HFU - HF e UB por 5 min; HFN - HF e SB; HFNU - HF, UB e SB. Um microscópio eletrônico de varredura (MEV) foi utilizado para análise da superfície das amostras. A análise estatística unidirecional ANOVA-um fator foi realizada para comparação dos resultados. Resultados: Não houve diferença estatística para a resistência à flexão (p-valor = 0,15) e para a rugosidade superficial (p-valor = 0,15). No entanto, obteve-se diferença estatisticamente significante para o ângulo de contato (p-valor = 0,00). Imagens de microscopia eletrônica de varredura mostraram a formação de precipitados após o ataque ácido, que foram removidos pelos tratamentos pós-condicionamento. Conclusão: Pode-se concluir que os diferentes tratamentos de superfície pós-condicionamento não aumentaram a resistência à flexão, rugosidade da superfície, mas influenciaram na molhabilidade da cerâmica e nas imagens em MEV.(AU)

Eficácia do uso de plasma em pressão atmosférica na adesão de cerâmicas zircônia / Efficacy of the use of plasma at atmospheric pressure in zirconia adhesion

Um dos maiores desafios atuais da ciência dos materiais dentários é a obtenção de união efetiva e durável às cerâmicas de alto conteúdo cristalino. O objetivo do presente estudo foi avaliar a resistência de união, energia de superfície e tipos de fratura de dois sistemas cerâmicos após diferentes formas de tratamento de superfície associada à aplicação do plasma em pressão atmosférica. Para o estudo foram obtidas quarenta placas de zircônia (12 mm x 5 mm x 1,5 mm) de dois tipos de cerâmicas zircônia (E.max ZirCad e Calypso), polidas e limpas por ultrassom durante 5 minutos. Divididas aleatoriamente em 2 grupos de acordo com o sistema cerâmico e 4 subgrupos (n=5) de acordo com o tratamento de superfície, (I) controle (primer), (II) jateamento com partículas micrométricas de alumina (Al2O3) + primer, (III) jateamento com partículas micrométricas de alumina (Al2O3) + plasma + primer, (IV) plasma + primer. Foram confeccionados cento e vinte cilindros de resina composta (Z100), utilizando matrizes cilíndricas (1,0 mm x 3,0 mm) cimentadas com cimento resinoso, Multilink N, sobre as placas de zircônia. Os espécimes foram armazenados em água destilada durante 24 horas a 37° C, depois testados para microcisalhamento em máquina de teste Shimadzu EZ a 1,0 mm/min. Os dados obtidos foram submetidos à análise estatística para comparação entre os grupos E.max e Calypso em relação à resistência à união (força/área ­ MPa), ângulo de contato e os tipos de fratura. Os dados foram analisados pelos testes ANOVA One-Way e Kruskal-Wallis para resistência de união (p=0,003) e (p=0,005) e ângulo de contato (p<0,001) e (p<0,001). Não houve diferença significativa para os dados de fratura (p=0,145), pelo teste quiquadrado, com predomínio de fraturas mistas. Os valores de resistência de união das cerâmicas Y-TZP apresentaram maiores valores quando o plasma foi associado ao jateamento com óxido de alumínio e/ou primer e a aplicação somente do plasma não superou os valores alcançados pelas outras formas de tratamento da superfície. Essa associação resultou em menores valores dos ângulos de contato. Houve maior frequência de fraturas mistas quando realizado somente o tratamento com óxido de alumínio e quando em associação com o plasma.(AU)

One of the major challenges today in the science of dental materials is the achievement of effective and durable bonding to ceramics with high crystalline content. The objective of the present study was to evaluate the efficacy of plasma at atmospheric pressure in the adhesion of ceramic zirconia through the bond strength, surface energy and type of fracture of two ceramic systems after different forms of surface treatment associated with the application of plasma at atmospheric pressure. For the study forty zirconia plates (12 mm x 5 mm x 1.5 mm) were obtained from two zirconia ceramics (E.max ZirCad and Calypso), polished and cleaned by ultrasound for 5 minutes. Randomly divided into 2 groups according to the ceramic system and 4 subgroups (n = 5) according to the surface treatment, control (primer), primer + blasting with micrometric alumina (Al2O3) particles, primer + blasting with micrometric particles of alumina (Al2O3) + plasma, primer + plasma. One hundred and twenty cylinders of composite resin (Z-100) were made using cylindrical matrices (1.0 mm x 3.0 mm) cemented on the zirconia plates. The specimens were stored in distilled water for 24 hours at 37°C, then tested for microshear on a Shimadzu EZ test machine at 0.5 mm / min. The obtained data were submitted to statistical analysis for comparison between the E.max and Calypso groups in relation to the bond strength (strength / area - Mpa), contact angle and fracture types. The data were analyzed by ANOVA One-Way and Kruskal-Wallis tests for bond strength (p=0.003) and (p=0.005) and contact angle (p<0.001) and (p<0.001). There was no significant difference for the fracture data (p = 0.145), by the chi-square test, with a predominance of mixed fractures. The bond strength values of the Y-TZP ceramics showed higher values when the plasma was associated with blasting with aluminum oxide and / or primer and the application of only the plasma did not exceed the values reached by the other forms of surface treatment. This association resulted in lower values of contact angles. It is a higher frequency of mixed fractures when only aluminum oxide treatment is performed and when it is associated with plasma.(AU)

Efeitos do suco de laranja e da molhabilidade da cerâmica sobre a formação do in situ / The effects of orange juice and ceramic wettability on in situ biofi lm formation

Este estudo procurou determinar os parâmetros do biofilme formado in situ, em cerâmica de revestimento, de acordo com a disponibilidade de carboidrato (suco de laranja) e a molhabilidade da superfície cerâmica. Discos de duas cerâmicas foram feitos (Vita VM7 e VM13, Vita Zahnfabrik, Bad Sackingen, Alemanha). Quatro discos foram aderidos a dispositivos palatais usados por oito voluntários. Colocou-se três gotas da água destilada (pH=6) ou suco de laranja (pH=3,5) sobre os discos oito vezes/dia. Após 48 horas in situ, os dois discos mais palatais foram removidos do dispositivo e analisados com microscopia confocal de varredura a laser (MCVL) para caracterização do biofilme (espessura média, μm e biovolume, μm3/μm2). O ângulo de contato (°) foi medido nas superfícies polidas de espécimes controle, e após 15 dias de uso nos espécimes da região frontal do dispositivo palatal. Os dados foram submetidos à estatística descritiva e inferencial (Mann-Whitney e teste t, p < 0,05). A molhabilidade de ambas as cerâmicas não diferiu estatisticamente. A formação do biofilme sobre as cerâmicas de revestimento não foi influenciada pelo suco de laranja ou pela molhabilidade da cerâmica...

This study aimed to determine the in situ biofilm parameters on veneering ceramics, according to the carbohydrate (orange juice) availability and the ceramic surface wettability. Disks were made out of two veneering ceramics (Vita VM7 and VM13, Vita Zahnfabrik, Bad Sackingen, Alemanha). Four disks were bonded to palatal devices worn by eight volunteers. The subjects dripped three drops of distilled water (pH=6) or orange juice (pH=3.5) on the disks 8x/day. After 48 h in situ, the two palatal disks were removed from the device and analyzed by Confocal Laser Scanning Microscopy (CLSM) for biofilm characterization (mean thickness, μm and biovolume, μm3/ μm2). The contact angle (°) was measured on the polished surfaces of as sintered specimens and after 15 day of in situ usage, on the frontal disks of the palatal device. The data were subjected to descriptive and inferential (Mann-Whitney and paired-t test, at p < 0.05) statistics. The biofi lm parameters of VM13 were not measurable, whereas the VM7 biofilm parameters were not signifi cantly affected by the type of liquid. The wettability of both ceramics also did not differ statistically. The biofi lm formation on the veneering ceramics was neither influenced by the orange juice dripping nor the ceramics’ wettability...

Rugosidade e molhabilidade do titânio usado em implantes dentários com superfícies tratadas / Roughness and wettability of titanium for treated dental implant surface

Para a análise da biocompatibilidade e da osseointegração dos implantes dentários são necessárias informações quantitativas da energia livre, rugosidade e composição química da superfície dos implantes. Tais propriedades influenciam na atração, repulsão e interações das proteínas e das células com a superfície do biomaterial. Uma das formas de obter informações da energia livre superficial dos sólidos é por meio da medição do ângulo de contato. No presente trabalho, determinou-se o ângulo de contato e a rugosidade de amostras de titânio polidas, submetidas ao ataque ácido, anodizadas e tratadas com soluções contendo fluoretos. Os resultados mostraram que pequenas variações na rugosidade modificam a molhabilidade. A superfície anodizada apresenta maior molhabilidade e existe a tendência de a molhabilidade aumentar com a diminuição da rugosidade das superfícies tratadas.