Article | IMSEAR | ID: sea-185996

ABSTRACT

Biodentine is a novel material introduced to combat inferior properties of existing calcium silicate-based materials and is a special micronised concrete derived from the main component of Portland cement, tricalcium silicate. This material has very good compressive strength, and more adaptable for permant restorations more likely material to adapt in dentistry.

2.
Article in English | IMSEAR | ID: sea-152350

ABSTRACT

Introduction: The ability of mineral trioxide aggregate (MTA),Biodentinand and Calcium phosphate cement to seal large furcation perforations were evaluated using a dye-extraction leakage method. Method: 30 extracted human mandibular first molars were divided into three experimental groups (n -10) according to the repair material used. Dye leakage was tested from an orthograde direction, and dye extraction was performed using full concentration nitric acid. Dye absorbance was measured at 550 nm using spectrophotometer. Result : ProRoot MTA (Maillfer, Dentsply) showed the least dye absorbance. Calcium phosphate showed the highest dye absorbance. and Biodentin came at intermediate level then other groups.

SELECTION OF CITATIONS
SEARCH DETAIL