ABSTRACT
The aim of this study was to evaluate the microleakage of teeth according to root canal preparation with & without apical enlargement in various size of apical foramen. 60 extracted one canal roots were cross-cutted at 5 mm from root apex and divided into two groups according to their apical foramen size of large (L) and small (S). Each group was subdivided into two groups accordance with their cross-sectional configuration at 5 mm from apex, round (R) and ovoid (O); SR Group, SO Group, LR Group, LO Group. Each group was shaped in .02 taper by Quantec series Nickel-Titanium (NiTi) rotary file, obturated by lateral condensation method. Leakage was measured using a fluid transport model under 40 cmH2O pressure. After the leakage test, blocks which had showed the leakage retreated with .04 taper and .06 taper and evaluated the degree of fluid filtration in each group. The data was analysed statistically using chi-square test and fisher's exact test. The results obtained were as follows: 1. Significant difference in leakage was found in groups which had different apical foramen size in .02 taper instrumentation (p 0.05). 2. The difference in microleakage according to the shape of canal was not evident at 5 mm from apex (p > 0.05). 3. There was correlation between .02 taper instrumentation and .04 taper instrumentation in LR group , LO group (p < 0.05).
Subject(s)
Filtration , Root Canal Preparation , Tooth Apex , ToothABSTRACT
The purpose of this in vitro study was to evaluate the effect of surface defects and cross-sectional configuration of NiTi rotary files on the fatigue life under cyclic loading. Three NiTi rotary files (K3(TM), ProFile(R), and HERO 642(R)) with #30/.04 taper were evaluated. Each rotary file was divided into 2 subgroups: control (no surface defects) and experimental group (artificial surface defects). A total of six groups of each 10 were tested. The NiTi rotary files were rotated at 300rpm using the apparatus which simulated curved canal (40 degree of curvature) until they fracture. The number of cycles to fracture was calculated and the fractured surfaces were observed with a scanning electron microscope. The data were analyzed statistically. The results showed that experimental groups with surface defects had lower number of cycles to fracture than control group but there was only a statistical significance between control and experimental group in the K3(TM) (p<0.05). There was no strong correlation between the cross-sectional configuration area and fracture resistance under experimental conditions. Several of fractured files demonstrated characteristic patterns of brittle fracture consistent with the propagation of pre-existing cracks. This data indicate that surface defects of NiTi rotary files may significantly decrease fatigue life and it may be one possible factor for early fracture of NiTi rotary files in clinical practice.