ABSTRACT
Objective@#To quantitatively evaluate the adaptation of polylactic acid (PLA) pattern of mandibular complete denture fabricated by fused deposition modeling (FDM) technology.@*Methods@#A mandibular complete denture digital model was designed through a complete denture design software based on a pair of standard maxillomandibular edentulous plaster model and their occlusion bases. Ten PLA mandibular complete dentures were printed with a FDM machine. The dentures were scanned with and without the plaster model using a three-dimensional (3D) scanner. In Geomagic software, the scanning data of printed dentures were registered to its computer aided design (CAD) data, and the printing error was analyzed using the multipoint registration command. For quantitatively evaluating the adaptation of the denture, the data of plaster model and PLA denture were registered to the whole data of denture located in the plaster model using the best-fit alignment command, the 3D deviation of the plaster model and tissue surface of the denture represent the space between them. The overall area was separated into three parts: primary stress-bearing area, secondary stress-bearing area and border seal area, and the average deviations of these three parts were measured. The values were analyzed using analysis of variance.@*Results@#Compared with the CAD data, the printing error was (0.013±0.004) mm. The overall 3D deviation between PLA denture and plaster model was (0.164±0.033) mm, in which the primary stress-bearing area was (0.165± 0.045) mm, the secondary stress-bearing area was (0.153 ± 0.027) mm, the border seal area was (0.186 ± 0.043) mm. These showed a good fit in the majority parts of the FDM denture to the plaster model. No statistically significant difference was observed between the three areas (F=1.857, P=0.175>0.05).@*Conclusions@#Combined with the 3D scanning, CAD and FDM technology, a FDM 3D printing process of complete denture for injection moulding can be established. As a result, high efficiency and low cost can be used to print out the complete denture, to lay the basis for further clinical applications.
ABSTRACT
Objective To investigate the effect of different investing materials on the complete denture flasking deformation.Methods The denture wax casts were invested by plaster,dental stone,and dental stone together with silicone,respectively.8 trial dentures were randomly chosen from above each group,and 4 reference points were selected in the cast.The conventional water bath polymerization system was used for the process.The distance between reference points were measured before and after thermally processing the Acrylic base.F test and Kruskal-Wallis H test were applied for statistical analysis.Results The distance between A and B (F =3.768,P =0.040) and the mean of total distance among O,A,B and C(F =4.830,P =0.019) had statistically significant differences among the three groups.The deformation variance of Group 1 (a conventional plaster) between 175μm and 267μm was maximum.The deformation values of Group2 (a dental stone) was appropriate with Group3 (a dental stone + a silicone).Smoothness (x2 =17.575,P ＜ 0.01) was statistically different among the three groups.Conclusion The flaskingprocess with the plaster had the maximum movement.The process with dental stone showed the minimal toothmovement,the process with the dental stone along with with thesilicone caused a similar movement as from the single dental stone but resulted in a smoother denture surface.