ABSTRACT
objective: To investigate the effects of cerium oxide content on the color of alumina glass composite. Methods: Infiltration glass powder with different content of cerium oxide (1%～4%) were fabricated. Alumina glass composite was prepared by infiltrating molten glass into presintered alumina block at 1 250 ℃ for 2 h, and the color of the alumina glass composite were measured with Minolta chromatic instrument(CR 321) . For comparison, the color of VITA In Ceram alumina technical shade guide was recorded too. Results: After infiltration, the b * range of the alumina glass composite was in accord with that of the shade guide. With the increasing content of the cerium oxide, a *, b * and chroma increased, L * decreased, the hue of the alumina glass composite shifted from yellow green to yellow red. Conclusion: Cerium oxide may effectively enhance b * of the alumina glass composite, but its ability of reducing L * and enhancing a * is weak.