The histometric analysis of osseointegration in hydroxyapatite surface dental implants by ion beam-assisted deposition / 대한치주과학회지

PURPOSE: This study compared the effects of coating implants with hydroxyapatite (HA) using an ion beam-assisted deposition (IBAD) method prepared with machined, anodized, sandblasted and large-grit acid etched (SLA) surfaces in minipigs, and verified the excellency of coating method with HA using IBAD. MATERIAL AND METHODS: 4 male Minipigs(Prestige World Genetics, Korea), 18 to 24 months old and weighing approximately 35 to 40 kg, were chosen. All premolars and first molars of the maxilla were carefully extracted on each side. The implants were placed on the right side after an 8 week healing period. The implant stability was assessed by resonance frequency analysis (RFA) at the time of placement. 40 implants were divided into 5 groups; machined, anodized, anodized plus IBAD, SLA, and SLA plus IBAD surface implants. 4 weeks after implantation on the right side, the same surface implants were placed on the left side. After 4 weeks of healing, the minipigs were sacrificed and the implants were analyzed by RFA, histology and histometric. RESULTS: RFA showed a mean implant stability quotient (ISQ) of 75.625+/-5.021, 76.125+/- 3.739 ISQ and 77.941+/-2.947 at placement, after 4 weeks healing and after 8 weeks, respectively. Histological analysis of the implants demonstrated newly formed, compact, mature cortical bone with a nearby marrow spaces. HA coating was not separated from the HA coated implant surfaces using IBAD. In particular, the SLA implants coated with HA using IBAD showed better contact osteogenesis. Statistical and histometric analysis showed no significant differences in the bone to implant contact and bone density among 5 tested surfaces. CONCLUSION: We can conclude that rough surface implants coated with HA by IBAD are more biocompatible, and clinical, histological, and histometric analysis showed no differences when compared with the other established implant surfaces in normal bone.

Bone response of three different surface implants : Histomorphometric, perio test value and resonance frequency analysis in beagle dogs / 대한치과보철학회지

STATEMENT OF PROBLEM: The intial stability for osseointegration of implant has been an interesting factor. Especially, in the case of poor bone quality or immediately loaded implant, various strategies have been developed focusing on the surface of materials to improve implant fixation to bone. The microscopic properties of implant surfaces play a major role in the osseous healing of dental implants. PURPOSE: The aims of this study are to perform a histologic and histomorphometric comparison of the healing characteristics of three different surfaces and the comparison of resonance frequency analysis (RFA) values measured by Osstell(TM) and perio-test values (PTV) measured by Periotest. MATERIAL AND METHODS: A total of 24 screw titanium implants (Dentium Co., Seoul, Korea) with 6mm in length and 3.4mm in diameter, were placed in the mandible of 4 beagle dogs. Implants were divided into three groups following the surface treatment methods: Group I is machined(control group). Group II is anodically oxidized. Group III is coated 500nm in thickness with hydroxyapatite(HA) by ion beam assisted deposition(IBAD) on the anodized oxidization. Bone blocks from 2 dogs were caught after 3 weeks of covered healing and another blocks from 2 dogs after 6 weeks. RFA values and PTV were measured right after insertion and at 3 and 6weeks. Histomorphometric analysis was made with Kappa Image Base System to calculate bone-to-implant contact (BIC) and bone area inside the threads. Pearson's correlation analyses were performed to evaluate the correlation between RFA and PTV, BIC and bone area ratio of three different surfaces at 3 and 6 weeks. RESULTS: 1) In all surface treatment methods, the RFA values decreased and the PTV values increased until 6 weeks in comparison to initial values. 2) At 3 weeks, no significant difference was found from bone-to-implant contact ratio and bone area ratio of three different surface treatment methods(P>0.05). However, at 6 weeks, different surface treatment methods showed significantly different bone-toimplant contact ratio and bone area ratio(P<0.05). 3) In the implants with the IBAD on the anodic oxidization, significant difference was found between the 3 weeks and the 6 weeks bone area ratio(P<0.05). 4) Correlation was found between the RFA values and the bone area ratio at 3 and 6 weeks with significant difference(P<0.05). CONCLUSIONS: These results indicate that the implants with the IBAD on the anodic oxidization may have a high influence on the initial stability of implant.