Utilization of sodium borohydride (NaBH4) in kraft pulping process.

Aim of this study is to investigate the effect of adding sodium borohydride (NaBH4) in kraft pulping. First of all, six kraft cooks were carried out for varying active alkali and sulfidity. Then, kraft methods for K1 and K6 cooks were modified by adding 1, 2 and 3 % NaBH4. The results indicated that modifying kraft method (K1) by adding 3% NaBH4 (KB13) resulted in 9.97% (relative percentage) yield increase and 10.1% (relative percentage) kappa reduction. Although the mechanical properties of NaBH4 modified pulps were lower compared to the kraft pulps, NaBH4 modified pulps were much brighter.

Thermal and spectroscopic analyses on the molecular interaction between eucalyptus kraft pulp components and offset printing inks

Thermal and infrared spectroscopic analyzes were carried out in order to study the kind of interaction between the anatomical components of the bleached eucalyptus kraft pulp with offset inks. A Bauer-McNett fiber classifier was used in order to obtain the anatomical components of the pulp, separately. The determinations of the enthalpy of the processes occurring in the samples of inks and pulp, as well as the enthalpy of these components interactions were obtained by Differential Scanning Calorimetry. In the interaction between pulp and offset ink, the reduced enthalpy values of the endothermic peak were interpreted as due to the released energy for adhesion of the ink pigment to the substratum. The low enthalpy value, 58 to 121 cal.g -, ¹indicated that the settling of the ink occurs by physical interactions. The pulp fraction enriched with vessel elements caused a higher energy release during the adherence of the pigment into the pulp.

O conhecimento técnico-científico das interações que ocorrem no processo de impressão offset é escasso, embora várias observações mostrem sua importância. O objetivo deste trabalho foi estudar por análises térmicas e espectroscópicas, na região 1do infravermelho, o tipo de interação dos componentes anatômicos da polpa branqueada kraft de eucalipto com tintas de impressão offset. Foi utilizado um classificador de fibras Bauer-McNett com o intuito de se obter os componentes anatômicos da polpa separadamente. As determinações da entalpia dos processos que ocorrem com as amostras de tintas, polpa e também a entalpia de interação destes componentes foram obtidas por Calorimetria Diferencial de Varredura. Na interação entre polpa e tinta offset, a redução dos valores de entalpia do pico endotérmico foi interpretada como sendo devida à liberação de energia para a adesão do pigmento da tinta ao substrato. Os baixos valores de entalpia (58 a 121 cal.g-1) indicam que o assentamento da tinta ocorre por meio de interações físicas A fração de polpa enriquecida com elementos de vasos acarreta uma maior liberação de energia, durante a aderência do pigmento na polpa.