Comparative Study on Color Stability of Denture Reline Polymers when Using Microwave and Chemical Disinfection

This study investigated the color stability of reline resin after two methods of disinfection i.e microwave disinfection and chemical disinfection. A stainless steel moldwith a breakaway compartment (10 mm in diameter by 0.7 mm thickness) was made to fabricate specimens of various resins. Each material was mixed according to manufacturer’s instructions and applied into the mold. Prior to color stability testing, specimenswere cleaned in distilled water for 20 minutes to kill any microorganisms that may had contaminated the discs during fabrication. And then specimens were immersed in Sodium Perborate Monohydrate 200 ml of solution for 15 days and microwaved for 15 days sothat it is comparable to chemical disinfection soaking. The color stability of each specimen was measured again using spectrophotometer and values were obtained. The data of ∆E, ∆L, ∆b, ∆a were analysed by 2 way repeated measures ANOVAs test. Significant statistic changes in color parameters ∆L, ∆a, ∆b of the reline resin DPI, Ufi Gel Hard And Kooliner were observed when dentures were disinfected by Sodium Perborate Monohydrate 2% solutions. The color stability of the reline resin was influenced by time, regardless of disinfection or non disinfection. This can be attributed to bleaching (whitening) effect of reline material. Discoloration Original Research Article of resin based materials may be caused by intrinsic or extrinsic factors. Intrinsic factors are related to internal alterations in material resulting from physicochemical reactions or residual monomer oxidation with time. Thus the initiator, quantity and type of monomer and the polymerisation efficiency can affect the color stability of resin based materials. The color stability deviation value ∆E significantly increased to maximum for chemical disinfectant, least for Control group and intermediate for microwaved group. Ufi Gel showed the highest deviation ∆E and Control Group showed the lowest deviation according to results

Effect of repeated microwave disinfection on surface roughness and baseplate adaptation of denture resins polymerized by different techniques / Efeito da desinfecção repetida por microondas sobre rugosidade superficial e adaptação de bases de resinas polimerizadas por diferentes técnicas

Purpose: To evaluate the cumulative effect of two protocols of microwave disinfection (Protocol 1: 690 W/6 min; Protocol 2: 345 W/6 min) on surface roughness (Ra) and baseplate adaptation of two denture resins polymerized by microwave energy (Onda Cryl) or hot water bath(QC-20). Methods: For Ra evaluation, rectangular specimens were fabricated and subjected to the following disinfection treatment (n=8/group): 1) Control (no disinfection), 2) Protocol 1, and 3) Protocol 2. Ra was measured using a profilometer at baseline (T0) and after two disinfection procedures (T1, T2) with a 7-day interval immersed in distilled water. To evaluate dimensional stability, maxillary baseplates were divided into the disinfection treatment groups (n=6), and adaptation was measured by weighing a silicon film reproducing the gap between resin baseplate and a metallic master model. Results: Ra had a significant interaction between type of resin/polymerization technique, disinfection treatment, and number of disinfection procedures (P<0.001). For Ra, Protocol 2 and control groups had similar increase of Ra over time, but Protocol 1 groups showed a significant decrease of Ra in T2. Baseplate adaptation was affected by a significant interaction between disinfection treatment and number of disinfection procedures (P<0.001), and Protocol 1 yielded the largest mean in T2. Conclusion: Onda Cryl displayed greater changes of Ra and adaptation than QC-20. Protocol 1 promoted overall damage to both types of denture resins after two disinfection procedures.

Objetivo: Avaliar o efeito cumulativo de dois protocolos de desinfecção por energia de micro-ondas (Protocolo 1: 690 W/6 min; Protocolo 2: 345 W/6 min) na rugosidade superficial (Ra) e adaptação de bases de dentadura de duas resinas polimerizadas por micro-ondas (Onda Cryl) ou banho de água quente (QC-20). Metodologia: Para Ra, espécimes retangulares foram fabricados e dividid os de acordo com o tratamento de desinfecção (n=8/grupo): 1) Controle (sem desinfecção), 2) Protocolo 1, e3) Protocolo 2. Para medir Ra usou-se um rugosímetro no baseline (T0) e após 2 procedimentos de desinfecção (T1, T2) com intervalo de 7 dias de imersão em água destilada. Para avaliar a estabilidade dimensional, bases maxilares foram divididas nos 3 grupos (n=6) e a adaptação foi medida por pesagem de uma película de silicone que reproduzia o espaço entre a base de resina e um modelo-mestre metálico. Resultados: Para Ra, houve interação significativa entre tipo de resina e técnica de polimerização, tratamento de desinfecção, e número de procedimentos desinfecção (P<0,001). Os grupos Protocolo 2 e controle apresentaram aumento semelhante de Ra ao longo do tempo, mas os grupos Protocolo 1 tiveram uma redução significativa de Ra em T2. A adaptação da base foi afetada por uma interação significante entre tratamento de desinfecção e número de procedimentos de desinfecção (P<0,001); o Protocolo 1 apresentou a maior média em T2. Conclusão: Onda Cryl teve maiores alterações de Ra e adaptação que QC-20. O Protocolo 1 promoveu dano geral para ambos os tipos de resina após dois procedimentos de desinfecção.

Effect of repeated disinfections by microwave energy on the physical and mechanical properties of denture base acrylic resins

The present study evaluated the effect of repeated simulated microwave disinfection on physical and mechanical properties of Clássico, Onda-Cryl and QC-20 denture base acrylic resins. Aluminum patterns were included in metallic or plastic flasks with dental stone following the traditional packing method. The powder/liquid mixing ratio was established according to the manufacturer's instructions. After water-bath polymerization at 74ºC for 9 h, boiling water for 20 min or microwave energy at 900 W for 10 min, the specimens were deflasked after flask cooling and finished. Each specimen was immersed in 150 mL of distilled water and underwent 5 disinfection cycles in a microwave oven set at 650 W for 3 min. Non-disinfected and disinfected specimens were subjected to the following tets: Knoop hardness test was performed with 25 g load for 10 s, impact strength test was done using the Charpy system with 40 kpcm, and 3-point bending test (flexural strength) was performed at a crosshead speed of 0.5 mm/min until fracture. Data were analyzed statistically by ANOVA and Tukey's test (α= 0.05 percent). Repeated simulated microwave disinfections decreased the Knoop hardness of Clássico and Onda-Cryl resins and had no effect on the impact strength of QC-20. The flexural strength was similar for all tested resins.

Este estudo verificou o efeito de repetidas desinfecções por microondas sobre a dureza, impacto e resistência à flexão das resinas acrílicas Clássico, Onda-Cryl e QC-20. Matrizes de alumínio foram incluídas em muflas metálica ou plástica com gesso pedra tipo III, de acordo com a técnica de inclusão tradicional. A proporção polímero/monômero usada foi de acordo com as recomendações dos fabricantes. Depois da polimerização em água à temperatura de 74ºC por 9 h, água em ebulição por 20 min ou por energia de microondas a 900 W por 3 min, os corpos-de-prova foram demuflados após esfriamento da mufla em temperatura ambiente e submetidos ao polimento convencional. Testes de dureza, impacto e resistência à flexão foram feitos nos corpos-de-prova controle e experimentais. Cada corpo-de-prova foi submetido individualmente a 5 desinfecções por microondas em forno doméstico com 900 W de energia por 3 min, imersos em 150 mL de água destilada. O teste de dureza Knoop foi realizado com carga de 25 g por 10 s, de resistência ao impacto pelo sistema Charpy com 40 kpcm e de resistência à flexão por três pontos com velocidade de 0,5 mm/min até fratura. Os dados obtidos foram submetidos à análise de variância e ao teste de Tukey (α=0,05 por cento). Repetidas desinfecções por microondas diminuíram a dureza das resinas Clássico e Onda-Cryl, não promoveram nenhum efeito sobre a resistência ao impacto da resina QC-20. A resistência à flexão foi similar para todas as resinas.

Effect of microwave disinfection on physical and mechanical properties of acrylic resins

This study evaluated the effect of microwave energy on the hardness, impact strength and flexural strength of the Clássico, Onda-Cryl and QC-20 acrylic resins. Aluminum die were embedded in metallic or plastic flasks with type III dental stone, in accordance with the traditional packing technique. A mixing powder/liquid ratio was used according to the manufacturer's instructions. After polymerization in water batch at 74ºC for 9 h, boiling water for 20 min or microwave energy at 900 W for 10 min, the specimens were deflasked after flask cooling at room temperature, and submitted to finishing. Specimens non-disinfected and disinfected by microwave irradiation were submitted to hardness, impact and flexural strength tests. Each specimen was immersed in distilled water and disinfected in a microwave oven calibrated to 650 W for 3 min. Knoop hardness test was performed with 25 g load for 10 s, impact test was carried out using the Charpy system with 40 kpcm, and 3-point bending test with a crosshead speed of 0.5 mm/min until fracture. Data were submitted to statistical analysis by ANOVA and Tukey's test (?=0.05). Disinfection by microwave energy decreased the hardness of Clássico and Onda-Cryl acrylic resins, but no effect was observed on the impact and flexural strength of all tested resins.

Este estudo verificou o efeito da desinfecção por microondas sobre a dureza, impacto e resistência à flexão das resinas acrílicas Clássico, Onda-Cryl e QC-20. Matrizes de alumínio foram incluídas em muflas metálica ou de plástico com gesso pedra tipo III, de acordo com a técnica de inclusão tradicional. A proporção polímero/monômero foi de acordo com as recomendações dos fabricantes. Depois da polimerização em água à temperatura de 74ºC por 9 h, água em ebulição por 20 min ou por energia de microondas a 900 W por 3 min, os corpos-de-prova foram demuflados após esfriamento da mufla em temperatura ambiente e submetidos ao polimento convencional. Testes de dureza, impacto e resistência à flexão foram feitos nos corpos-de-prova submetidos ou não à desinfecção por microondas. Cada corpo-de-prova foi submetido individualmente à desinfecção por microondas em forno doméstico com 900 W de potência por 3 min, imersos em 150 mL de água destilada. O teste de dureza Knoop foi realizado com carga de 25 g por 10 s, a de impacto pelo sistema Charpy com 40 kpcm e o de flexão por três pontos com velocidade de 0,5 mm/min até fratura. Os dados foram submetidos à análise de variância e ao teste de Tukey (?=0,05). A desinfecção simulada por microondas diminuiu a dureza Knoop das resinas Clássico e Onda-Cryl e não promoveu nenhum efeito nas resistências ao impacto e à flexão das resinas estudadas.