Success rate and marginal bone loss of Osstem USII plus implants; Short term clinical study / 대한치과보철학회지

PURPOSE: The aim of this study was to evaluate the clinical value of Osstem(R) USII plus system implants. Clinical and radiographic data were analyzed for 88 implants placed and functionally loaded for a 12 month period at the Yonsei University Dental Hospital. MATERIALS AND METHOD: Based on the patient's medical records, clinical factors and their effects on implant marginal bone resorption, distribution and survival rate were analyzed. The marginal bone loss was evaluated at implant placement and during a 6 to 12 months functional loading period. The independent sample t-test was used to evaluate the interrelationship between the factors (alpha=0.05), and one way repeated measures ANOVA was used to compare the amount of marginal bone resorption. RESULTS: The cumulative survival rate for 88 implants was 100%. The marginal bone resorption from implant placement to prosthetic delivery was 0.24 mm and the average marginal bone resorption from prosthetic delivery to 12 months of functional loading was 0.19 mm. The total average bone resorption from implant placement to 12 months of functional loading was 0.43 mm. There were no statistically differences in the amount of marginal bone resorption when implants were placed in the maxilla or the mandible (P>.05), however, implants placed in the posterior areas showed significantly more marginal bone loss than those placed in the anterior areas (P<.05). CONCLUSION: Based on these results, the short term clinical success rate of RBM surface treated external connection domestic implants showed satisfactory results and the marginal bone loss was in accord with the success criteria of dental implants.

Influence of surface treatment on the insertion pattern of self-drilling orthodontic mini-implants / 대한치과교정학회지

OBJECTIVE: The purpose of this study was to compare self-drilling orthodontic mini-implants of different surfaces, namely, machined (untreated), etched (acid-etched), RBM (treated with resorbable blasting media) and hybrid (RBM + machined), with respect to the following criteria: physical appearance of the surface, measurement of surface roughness, and insertion pattern. METHODS: Self-drilling orthodontic mini-implants (Osstem implant, Seoul, Korea) with the abovementioned surfaces were obtained. Surface roughness was measured by using a scanning electron microscope and surface-roughness-testing machine, and torque patterns and vertical loadings were measured during continuous insertion of mini-implants into artificial bone (polyurethane foam) by using a torque tester of the driving-motor type (speed, 12 rpm). RESULTS: The mini-implants with the RBM, hybrid, and acid-etched surfaces had slightly increased maximum insertion torque at the final stage (p < 0.05). Implants with the RBM surface had the highest vertical load for insertion (p < 0.05). Testing for surface roughness revealed that the implants with the RBM and hybrid surfaces had higher Ra values than the others (p < 0.05). Scanning electron microscopy showed that the implants with the RBM surface had the roughest surface. CONCLUSIONS: Surface-treated, self-drilling orthodontic mini-implants may be clinically acceptable, if controlled appropriately.

The Micromorphometric change of the GBA and RBM implant surface conditioned with tetracycline-HCl / 대한치주과학회지

The present study was performed to evaluate the effect of tetracycline-HCl on the change of implant surface microstructure according to application time. Implant with pure titanium machined surface, GBA surface and RBM surface were utilized. Implant surface was rubbed with 50mg/ml tetracycline-HCl solution for 1/2min. 1min. 1 1/2min. 2min. and 2 1/2min. respectively in the test group. Then, specimens were processed for scanning electron microscopic observation. The results of this study were as follow. 1. Both test and control group showed a few shallow grooves and ridges in pure titanium machined surface implants. There were not significant differences between two group. 2. In GBA surfaces, control group exhibit many porous depression, and each depression were divided by strict border. Experimental group applied with tetracycline-HCl for 2min. were similar with control group. But when applied for 2 1/2min. surface alteration and border breakdown started, resulting enlargement of the porous depression. 3. In RBM surface, control group exhibit rough, uneven surface with crater-like depression can be found. The surface alteration started when tetracycline-HCl was applied for 30sec. resulting breakdown of the crater-like depression. Depression became larger as applying time increased.