Journal of Korean Academy of Conservative Dentistry ; : 98-106, 2008.
Article in Korean | WPRIM | ID: wpr-105062

ABSTRACT

The purpose of this study was to evaluate whether intracanal irrigation method could affect the adhesion between intracanal dentin and root canal filling materials (Gutta-percha/AH 26 sealer and Resilon/Epiphany sealer). Thirty extracted human incisor teeth were prepared. Canals were irrigated with three different irrigation methods as a final rinse and obturated with two different canal filling materials (G groups : Gutta-percha/AH 26 sealer, R groups : Resilon/Epiphany sealer) respectively. Group G1, R1 - irrigated with 5.25% NaOCl. Group G2, R2 - irrigated with 5.25% NaOCl, sterile saline. Group G3, R3 - irrigated with 5.25% NaOCl, 17% EDTA, sterile saline. Thirty obturated roots were horizontally sliced and push-out bond strength test was performed in the universal testing machine. After test, the failure patterns of the specimens were observed using Image-analyzing microscope. The results were as follows. 1. Gutta-percha/AH 26 sealer groups had significantly higher push-out bond strength compared with the Resilon/Epiphany sealer groups (p < 0.05). 2. Push-out bond strength was higher when using 17% EDTA followed by sterile saline than using NaOCl as a final irrigation solution in the Resilon/Epiphany sealer groups (p < 0.05). 3. In the failure pattern analysis, there was no cohesive failure in Group G1, G2, and R1. Gutta-percha/AH 26 sealer groups appeared to exhibit predominantly adhesive and mixed failure patterns, whereas Resilon/Epiphany sealer groups exhibited mixed failures with the cohesive failure occurred within the Resilon substrate.


Subject(s)
Humans , Adhesives , Collodion , Dentin , Edetic Acid , Incisor , Root Canal Filling Materials , Tooth
SELECTION OF CITATIONS
SEARCH DETAIL