Results 1 - 6 de 6
Filter
1.
São José dos Campos; s.n; 2016. 64 p. bi, tab, graf.
Thesis in Portuguese | LILACS, BBO | ID: biblio-867667

ABSTRACT

O propósito deste estudo foi avaliar, in vitro, a influência de remanescente de materiais obturadores endodônticos, após desobturação e preparo para pino, sobre a resistência de união adesiva de pinos de fibra de vidro cimentados. Foram utilizados 60 dentes humanos unirradiculados sem coroa. As raízes foram preparadas pela técnica coroa-ápice com sistema Reciproc. Para obturação, as raízes foram divididas em grupos (n = 10) de acordo com o cimento endodôntico utilizado: SO= sem obturação; GP=guta percha sem cimento; AHP= guta-percha +AHPlus; SLP= guta-percha + Sealapex; IRT= guta-percha + iRoot SP; e ERZ= gutapercha + EndoRez. As raízes foram obturadas pela técnica do cone único. Acimentação dos pinos de fibra de vidro Rebilda n.12 foi realizada com sistema adesivo futurabond DC e cimento Rebilda DC em 10 mm do comprimento da raiz.Após esse período, as raízes foram seccionadas obtendo-se discos de 2 mm de espessura em cada terço da raiz (3 discos por raiz) que foram submetidos ao teste de push out, análise por meio de uma lupa estereoscópica (40x) para identificação através de scores da presença de remanescente de material obturador na luz do canal e avaliação por espectroscopia de energia dispersiva (EDS) para identificação de remanescente de componentes químicos do cimento endodôntico presentes nos tíbulos dentinários. Os dados obtidos foram analisados estatisticamente pelos testes de Kruskal Wallis, Qui Quadrado e teste de Anova e Tukey, todos com nível de significância de 5%. Não houve diferença estatística para a resistência adesiva entre os cimentos na região cervical (p = 0,49), media (p = 0,28) e apical (p = 0,09). Os grupos SLP e ERZ apresentaram menos remanescente de material obturador nas regiões cervical (p = 0,045) e apical (p = 0,006). Significantes diferenças de remanescentes de componentes químicos foram observadas na região apical dos grupos AHP, IRT e SLP. Conclui-se que os materiais endodônticos não influenciaram na resistência de...


The purpose of this study was to evaluate the influence of remnants endodontic fillingmaterial in root canal on the bond strength of fiberglass posts cemented. Sixty singlerootedhuman teeth were used.Crowns were removed. The roots were prepared bycrown-down technique with Reciproc system. For fillings, the roots were divided (n =10) according to the sealer used: SO- without fillings; GP-gutta-percha withoutsealer; AHP- gutta-percha + AHPlus; SLP- gutta-percha + Sealapex; IRT-guttapercha+ iRoot SP; ERZ-and gutta-percha + EndoRez. Single cone obturationtechnique was used. After root canal fillings, the teeth were kept in an oven 37 0C for7 days. Cementing fiberglass posts Rebilda n.12 was performed with fiber adhesivesystem Futurabond DC and cement Rebilda DC in 10 mm of root length, gettingstored in an oven at 37 0C for 48 h. After this period, roots were sectioned obtaining 1disc of 2 mm thickness in each third of the root (3 discs per root), this discs wereunderwent to push out test, analyzed by means of a stereomicroscope (40x) toidentify the presence of remnants of filling material in the lumen of the canal, andthen evaluated by energy dispersive spectroscopy (EDS) for identification ofchemical components remnants sealer present in the dentinal tubules. Datas wereanalyzed with Kruskal-Wallis test, Chi square test, and also Anova and Tukey test,5% of significance. There were no significant differences in push-out bond strengthsamong the different groups in the coronal (p = 0.49), middle (p = 0.28) or apical third(p = 0.09). Sealeapex and EndoRez groups showed significantly less remnants offilling material at coronal (p = 0.045) and apical levels (p = 0.006).Significantdifferences of chemical components remnants were found in AHP, IRT and SLPgroups on apical third. It is concluded that residual endodontic filling material doesnot influence on the bond strength of fiberglass


Subject(s)
Dental Cements , Dental Pulp Cavity , Root Canal Obturation/methods , Dental Pins
2.
São José dos Campos; s.n; 2016. 64 p. bi, tab, graf.
Thesis in Portuguese | LILACS, BBO | ID: biblio-870218

ABSTRACT

O propósito deste estudo foi avaliar, in vitro, a influência de remanescente de materiais obturadores endodônticos, após desobturação e preparo para pino, sobre a resistência de união adesiva de pinos de fibra de vidro cimentados. Foram utilizados 60 dentes humanos unirradiculados sem coroa. As raízes foram preparadas pela técnica coroa-ápice com sistema Reciproc. Para obturação, as raízes foram divididas em grupos (n = 10) de acordo com o cimento endodôntico utilizado: SO= sem obturação; GP=guta percha sem cimento; AHP= guta-percha +AHPlus; SLP= guta-percha + Sealapex; IRT= guta-percha + iRoot SP; e ERZ= gutapercha + EndoRez. As raízes foram obturadas pela técnica do cone único. Acimentação dos pinos de fibra de vidro Rebilda n.12 foi realizada com sistema adesivo futurabond DC e cimento Rebilda DC em 10 mm do comprimento da raiz.Após esse período, as raízes foram seccionadas obtendo-se discos de 2 mm de espessura em cada terço da raiz (3 discos por raiz) que foram submetidos ao teste de push out, análise por meio de uma lupa estereoscópica (40x) para identificação através de scores da presença de remanescente de material obturador na luz do canal e avaliação por espectroscopia de energia dispersiva (EDS) para identificação de remanescente de componentes químicos do cimento endodôntico presentes nos tíbulos dentinários. Os dados obtidos foram analisados estatisticamente pelos testes de Kruskal Wallis, Qui Quadrado e teste de Anova e Tukey, todos com nível de significância de 5%. Não houve diferença estatística para a resistência adesiva entre os cimentos na região cervical (p = 0,49), media (p = 0,28) e apical (p = 0,09). Os grupos SLP e ERZ apresentaram menos remanescente de material obturador nas regiões cervical (p = 0,045) e apical (p = 0,006). Significantes diferenças de remanescentes de componentes químicos foram observadas na região apical dos grupos AHP, IRT e SLP. Conclui-se que os materiais endodônticos não influenciaram na resistência de...


The purpose of this study was to evaluate the influence of remnants endodontic fillingmaterial in root canal on the bond strength of fiberglass posts cemented. Sixty singlerootedhuman teeth were used.Crowns were removed. The roots were prepared bycrown-down technique with Reciproc system. For fillings, the roots were divided (n =10) according to the sealer used: SO- without fillings; GP-gutta-percha withoutsealer; AHP- gutta-percha + AHPlus; SLP- gutta-percha + Sealapex; IRT-guttapercha+ iRoot SP; ERZ-and gutta-percha + EndoRez. Single cone obturationtechnique was used. After root canal fillings, the teeth were kept in an oven 37 0C for7 days. Cementing fiberglass posts Rebilda n.12 was performed with fiber adhesivesystem Futurabond DC and cement Rebilda DC in 10 mm of root length, gettingstored in an oven at 37 0C for 48 h. After this period, roots were sectioned obtaining 1disc of 2 mm thickness in each third of the root (3 discs per root), this discs wereunderwent to push out test, analyzed by means of a stereomicroscope (40x) toidentify the presence of remnants of filling material in the lumen of the canal, andthen evaluated by energy dispersive spectroscopy (EDS) for identification ofchemical components remnants sealer present in the dentinal tubules. Datas wereanalyzed with Kruskal-Wallis test, Chi square test, and also Anova and Tukey test,5% of significance. There were no significant differences in push-out bond strengthsamong the different groups in the coronal (p = 0.49), middle (p = 0.28) or apical third(p = 0.09). Sealeapex and EndoRez groups showed significantly less remnants offilling material at coronal (p = 0.045) and apical levels (p = 0.006).Significantdifferences of chemical components remnants were found in AHP, IRT and SLPgroups on apical third. It is concluded that residual endodontic filling material doesnot influence on the bond strength of fiberglass.


Subject(s)
Dental Cements , Dental Pulp Cavity , Root Canal Obturation/methods , Dental Pins
3.
Rio de Janeiro; s.n; 2012. 54 p. ilus, tab.
Thesis in Portuguese | LILACS, BBO | ID: lil-673664

ABSTRACT

O objetivo deste estudo foi realizar uma avaliação tridimensional da rugosidade superficial em 3 tipos de pinos de fibra - DT LightPost®, FRC Postec Plus® e Transluma Post™ - submetidos a diferentes tratamentos de superfície e avaliar os efeitos dos pré-tratamentos na resistência adesiva a um compósito de presa dual Biscore™. Os tratamentos de superfície foram: imersão em ácido hidrofluorídrico, jateamento com óxido de alumínio a 50µm, imersão em peróxido de hidrogênio, jateamento com óxido de alumínio a 50µm seguido de imersão em ácido hidrofluorídrico e jateamento com óxido de alumínio a 50µm seguido de imersão em peróxido de hidrogênio. No experimento 1, 75 pinos foram divididos em 3 grupos (n = 25), de acordo com seu fabricante e subdivididos em cinco subgrupos. A rugosidade superficial foi medida usando um rugosímetro tridimensional e analisada com o software de análise 3D. Os valores de rugosidade foram obtidos antes e após diferentes tratamentos de superfície na área dos mesmos corpos-de-prova. Para o experimento 2, foram utilizados os mesmos corpos-de-prova, os mesmos grupos e subgrupos do experimento 1, tendo sido adicionado o subgrupo de controle (n=90) e a resistência adesiva a um compósito presa dual Biscore™ foi mensurada através de um teste push-out. A resistência adesiva foi medida em uma máquina universal de ensaios, com uma célula de carga tipo SLBL-5kN em uma velocidade de 0,5 mm / min. Os resultados do experimento 1 foram analisados através de um teste estatístico t-Student. Jateamento e jateamento seguido de imersão em ácido hidrofluorídrico produziram um aumento estatisticamente significante na rugosidade, contudo somente o tratamento por jateamento proporcionou um aumento significativo nos valores de rugosidade. Os resultados do experimento 2 foram obtidos através de um um teste t-unilateral de hipótese com variância desconhecida. Concluiu-se que o jateamento com óxido de alumínio a 50μm em uma distância de 30 mm a 2,5 bar ...


The aim of this study was to perform a tridimensional surface roughness test evaluation of different surface treatments to 3 types of fiber posts - DT LightPost®, FRC Postec Plus® e Transluma Post™ - and evaluate the effects of the different pretreatments on the bond strength of a dual-cure resin core material Biscore™. The different surface treatments were: immersion in hydrofluoric acid, sandblasting abrasion with 50 µ alumina particles, immersion in hydrogen peroxide, sandblasting abrasion with 50 µ alumina particles followed by immersion in hydrofluoric acid and sandblasting abrasion with 50 µ alumina particles followed by immersion in hydrogen peroxide. In the first experiment seventy five fiber posts were divided into 3 groups (n = 25), according to their manufacturer and subdivided into 5 subgroups. Surface roughness was measured using a tridimensional surface roughness test and analyzed with 3D analysis software. Surface roughness was obtained before and after the different surface treatments at the same post area. In the second experiment the same samples divided in groups and subgroups were used, but a control group (no treatment) was added (n = 90) and the bond strength to a composite resin core material Biscore™ was measured using a push-out design. The interfacial push-out bond strength was measured in a universal testing machine, with a load cell type SLBL-5kN at a crosshead speed of 0.5 mm/min. Results in experiment 1 were statistically analyzed using Student´s t-Test. Sandblasting and sandblasting followed by immersion in hydrofluoric acid produced a significant increase in roughness, but the sandblasting treatment was able to provide a significant roughness increase. Results in experiment 2 were statistically analysed using one-sided t-Test of Hypothesis with unknown variance. It was concluded that sandblasting airborne-particle abrasion with alumina 50µ at a distance of 30 mm at 2.5 bars pressure for 5 seconds was ...


Subject(s)
Composite Resins , Dental Pins , Adhesiveness , Aluminum Oxide , Hydrogen Peroxide , Surface Properties , Self-Curing of Dental Resins
4.
Rio de Janeiro; s.n; 2012. 54 p. ilus, tab.
Thesis in Portuguese | LILACS, BBO | ID: biblio-866133

ABSTRACT

O objetivo deste estudo foi realizar uma avaliação tridimensional da rugosidade superficial em 3 tipos de pinos de fibra - DT LightPost®, FRC Postec Plus® e Transluma Post™ - submetidos a diferentes tratamentos de superfície e avaliar os efeitos dos pré-tratamentos na resistência adesiva a um compósito de presa dual Biscore™. Os tratamentos de superfície foram: imersão em ácido hidrofluorídrico, jateamento com óxido de alumínio a 50µm, imersão em peróxido de hidrogênio, jateamento com óxido de alumínio a 50µm seguido de imersão em ácido hidrofluorídrico e jateamento com óxido de alumínio a 50µm seguido de imersão em peróxido de hidrogênio. No experimento 1, 75 pinos foram divididos em 3 grupos (n = 25), de acordo com seu fabricante e subdivididos em cinco subgrupos. A rugosidade superficial foi medida usando um rugosímetro tridimensional e analisada com o software de análise 3D. Os valores de rugosidade foram obtidos antes e após diferentes tratamentos de superfície na área dos mesmos corpos-de-prova. Para o experimento 2, foram utilizados os mesmos corpos-de-prova, os mesmos grupos e subgrupos do experimento 1, tendo sido adicionado o subgrupo de controle (n=90) e a resistência adesiva a um compósito presa dual Biscore™ foi mensurada através de um teste push-out. A resistência adesiva foi medida em uma máquina universal de ensaios, com uma célula de carga tipo SLBL-5kN em uma velocidade de 0,5 mm / min. Os resultados do experimento 1 foram analisados através de um teste estatístico t-Student. Jateamento e jateamento seguido de imersão em ácido hidrofluorídrico produziram um aumento estatisticamente significante na rugosidade, contudo somente o tratamento por jateamento proporcionou um aumento significativo nos valores de rugosidade. Os resultados do experimento 2 foram obtidos através de um um teste t-unilateral de hipótese com variância desconhecida. Concluiu-se que o jateamento com óxido de alumínio a 50μm em uma distância de 30 mm a 2,5 bar ...


The aim of this study was to perform a tridimensional surface roughness test evaluation of different surface treatments to 3 types of fiber posts - DT LightPost®, FRC Postec Plus® e Transluma Post™ - and evaluate the effects of the different pretreatments on the bond strength of a dual-cure resin core material Biscore™. The different surface treatments were: immersion in hydrofluoric acid, sandblasting abrasion with 50 µ alumina particles, immersion in hydrogen peroxide, sandblasting abrasion with 50 µ alumina particles followed by immersion in hydrofluoric acid and sandblasting abrasion with 50 µ alumina particles followed by immersion in hydrogen peroxide. In the first experiment seventy five fiber posts were divided into 3 groups (n = 25), according to their manufacturer and subdivided into 5 subgroups. Surface roughness was measured using a tridimensional surface roughness test and analyzed with 3D analysis software. Surface roughness was obtained before and after the different surface treatments at the same post area. In the second experiment the same samples divided in groups and subgroups were used, but a control group (no treatment) was added (n = 90) and the bond strength to a composite resin core material Biscore™ was measured using a push-out design. The interfacial push-out bond strength was measured in a universal testing machine, with a load cell type SLBL-5kN at a crosshead speed of 0.5 mm/min. Results in experiment 1 were statistically analyzed using Student´s t-Test. Sandblasting and sandblasting followed by immersion in hydrofluoric acid produced a significant increase in roughness, but the sandblasting treatment was able to provide a significant roughness increase. Results in experiment 2 were statistically analysed using one-sided t-Test of Hypothesis with unknown variance. It was concluded that sandblasting airborne-particle abrasion with alumina 50µ at a distance of 30 mm at 2.5 bars pressure for 5 seconds was ...


Subject(s)
Composite Resins , Dental Pins , Adhesiveness , Aluminum Oxide , Hydrogen Peroxide , Surface Properties , Self-Curing of Dental Resins
5.
Bauru; s.n; 2011. 82 p. ilus, tab.
Thesis in Portuguese | LILACS, BBO | ID: biblio-865833

ABSTRACT

Este estudo avaliou a resistência ao deslocamento vertical push-out de pinos de fibra de vidro cimentados à dentina intra-radicular utilizando uma resina fluida padrão como agente cimentante em combinação com um adesivo dentinário experimental e um adesivo disponível comercialmente. 20 pré-molares unirradiculares humanos foram previamente extraídos e tratados endodonticamente. Os espécimes foram divididos em quatro estratégias de união a dentina: Grupo 1 com adesivo experimental com etanol na proporção em volume 1:1 (resina/etanol) e Grupo 2 com adesivo experimental com etanol na proporção em volume 1:2(resina/etanol); adesivos experimentais aplicados de acordo com a técnica úmida de adesão simplificada com etanol, Grupo 3: One-Step Plus aplicado de acordo com a técnica úmida de adesão simplificada com etanol; Grupo 4: One-Step Plus aplicado seguindo as instruções do fabricante. Os espécimes foram seccionados em fatias de 1 mm de espessura e apos o teste push-out foi realizado. Espécimes representativos foram selecionados para exame ultra-estrutural. Não houve diferença estatística na resistência ao deslocamento push-out entre as estratégias testadas de adesão (p> 0,05). O padrão predominante de fratura foi entre os pinos de fibra e o agente cimentante. A partir deste estudo devemos considerar como promissora a técnica com etanol utilizada na cimentação de pinos no canal radicular devido aos possíveis benefícios das resinas altamente hidrófobas. Mais estudos são necessários para validar o uso da técnica úmida de adesão simplificada com etanol quando cimentados pinos de fibra.


This study evaluated the push-out bond strength of glass fiber posts adhesively bonded to intraradicular dentin using a standard unfilled resin as luting agent in combination with an experimental and a commercially available adhesive. Twenty extracted single-rooted human teeth were endodontically treated. Specimens were assigned to 4 dentin bonding strategies: Group 1 (co-monomers to ethanol on ratio 1:1) and Group 2 (co-monomers to ethanol on ratio 1:2): Experimental adhesives applied in accordance with the simplified ethanol-wet bonding technique; Group 3: One-Step Plus (OSP) applied in accordance with the simplified ethanol-wet bonding technique; Group 4: OSP applied following manufacturers instructions. Bonded specimens were sectioned in 1-mm-thick slices and the push-out test was performed. Representative specimens were selected for ultrastructural examination. No statistical differences in push-out bond strength were found among the tested bonding strategies (p>0.05). The major failure pattern was between the post and the luting cement. From this study the ethanol technique should be considered as a promising approach in the luting of fiber posts into the root canal due to the possible benefits of highly hydrophobic resins. Further studies are needed to validate the use of the ethanol-wet bonding technique when luting a fiber post.


Subject(s)
Humans , Dentin-Bonding Agents/chemistry , Dental Pulp Cavity , Dentin/chemistry , Ethanol/chemistry , Post and Core Technique , Dental Bonding/methods , In Vitro Techniques , Materials Testing , Microscopy, Electron, Scanning , Tensile Strength
6.
Rev. odonto ciênc ; 24(3): 283-289, July-Sept. 2009. graf, ilus, tab
Article in English | LILACS, BBO | ID: biblio-873868

ABSTRACT

Purpose: To evaluate the effect of blood contamination and different decontamination procedures on marginal adaptation and bond strength of a two-step total-etch adhesive system to dentin. Methods: A total of 135 bovine incisors had the labial surfaces ground to receive cylindrical cavities, and were randomly divided into a control and 8 experimental groups (n=15) according to contamination and decontamination procedures. Freshly collected human blood was applied onto the cavity either before or after light-curing of the adhesive. Four decontamination protocols were tested (drying with paper, water rinsing, phosphoric acid etching, and 10% NaOCl rinsing). The cavities were restored with Adper Single Bond and Filtek Z250 (3M ESPE). The specimens were subjected to thermal cycling before the dye staining test. The cavity floor was removed and the restorations were subjected to a push-out test. Data were analyzed by two-way ANOVA and Tukey's test (α=0.05). Results: Blood contamination after adhesive light-curing increased marginal gap and yielded lower push-out bond strength values (P<0.01). Conclusion: Water rinsing seems to be a reliable procedure for cavity decontamination. The decontamination procedures tested do not recover marginal sealing and bond strength when blood contamination occurs after light-curing of the adhesive.


Objetivo: Avaliar o efeito da contaminação com sangue e de procedimentos de descontaminação na adaptação marginal e resistência de união de um adesivo convencional de dois passos à dentina. Metodologia: Um total de 135 incisivos bovinos receberam cavidades cilíndricas na superfície vestibular, previamente desgastada. Os dentes foram divididos em grupo controle e 8 grupos experimentais (n=15), com base no momento da contaminação e nos procedimentos de descontaminação. Sangue recém-coletado foi aplicado nas cavidades, antes ou após a fotoativação do adesivo. Quatro procedimentos de descontaminação foram testados: secagem com papel, lavagem com água, condicionamento com ácido fosfórico e lavagem com hipoclorito de sódio a 10%. As cavidades foram restauradas com Adper Single Bond e Filtek Z250 (3M ESPE). Os espécimes foram submetidos à termociclagem antes da marcação com corante. O assoalho das cavidades foi removido e as restaurações foram submetidas ao teste de push-out. Os dados foram analisados por two-way ANOVA e teste de Tukey (α=0,05). Resultados: A contaminação após fotoativação do adesivo gerou fendas marginais maiores e resistência de união menor (P<0,001). Conclusão: A lavagem com água parece ser um método confiável de descontaminação. Os procedimentos testados não recuperam o selamento marginal e a resistência de união quando a contaminação ocorre após fotoativação do adesivo.


Subject(s)
Animals , Cattle , Dental Marginal Adaptation , Blood , Composite Resins , Environmental Pollution , Dental Restoration, Permanent , Dentin-Bonding Agents , Decontamination/methods , Tensile Strength