ABSTRACT
El artículo propone estudiar la propagación de los campos electromagnéticos a través de la mitocondria. Se presenta un modelo simplificado de la mitocondria como un sistema periódico de multicapas de índices de refracción alternantes. Mediante el método de transferencia matricial se calcula la dependencia, la reflectancia y transmitancia en función de la longitud de onda del campo electromagnético incidente. Se observa la existencia de una región de longitudes de onda (o frecuencia prohibidas) en la cual no existe propagación de los campos a través del sistema, esto corresponde a una reflectancia máxima R=1.
The article aims to study the propagation of electromagnetic fields through the mitochondria. We present a simplified model of the mitochondrion as a periodic multilayer of alternating refractive indices. Using the transfer matrix method calculates dependence reflectance and transmittance versus wavelength of incident electromagnetic field. Observe the existence of a wavelength region (or prohibited frequency) in which there is no spread of the fields through the system, this corresponds to a maximum reflectance R = 1.
O artigo tem como objetivo estudar a propagação de campos eletromagnéticos através das mitocôndrias. Nós apresentamos um modelo simplificado da mitocôndria como uma multicamada periódica de alternância de índices de refração. Utilizando o método de matriz de transferência calcula reflectância dependência e transmitância contra o comprimento de onda de campo eletromagnético incidente. Note-se a existência de uma região de comprimento de onda (ou frequência proibida) em que não há nenhuma propagação dos campos através do sistema, isto corresponde a um máximo de reflectância R = 1.
ABSTRACT
O objetivo desta pesquisa foi avaliar a transmitância de diferentes tipos e cores de cerâmicas e seus efeitos no grau de conversão (GC) de dois tipos de cimentos resinosos com modo de polimerização dual. Foram confeccionadas 60 pastilhas com a cerâmica IPS e.max (Ivoclar Vivadent, Schaan, Liechtenstein) e divididas em 3 grupos: LT, MO e Z, com 20 pastilhas cada um. Nos grupos LT e MO, as pastilhas foram confeccionadas com a cerâmica de dissilicato de lítio de baixa translucidez (LT - low transluscency) e de média opacidade (MO - medium opacity), respectivamente. No grupo Z, as pastilhas foram confeccionadas em zircônia. Cada grupo foi subdividido em 5 subgrupos (n=4), de acordo com a cor da cerâmica: A2; A3,5; B2; C2; D3. No grupo LT, as pastilhas foram prensadas nas cores anteriormente citadas e, nos grupos MO e Z, as pastilhas foram, inicialmente, confeccionadas para simular infraestruturas e, posteriormente, receberem aplicação de cerâmica de revestimento IPS e.max Ceram (Ivoclar Vivadent, Schaan, Liechtenstein) nas mesmas cores. O espectrofotômetro UV 1800 Shimadzu foi utilizado para medir a transmitância de cada espécime de cerâmica (2,0 mm de espessura). Para medir o GC, espécimes dos cimentos resinosos Variolink II (Ivoclar Vivadent, Schaan, Liechtenstein) e Rely X U200 (3M ESPE, St. Paul, MN, USA), com espessura de 100 μm, foram fotopolimerizados sob os discos de cerâmica por 40 s. Espécimes dos cimentos fotoativados sem a interposição da cerâmica foram usados como grupo controle. A polimerização dos cimentos foi avaliada através da espectrometria no infravermelho com transformada de Fourier (FTIR) empregando o método de reflexão atenuada total (ATR) imediatamente após a fotopolimerização. Os resultados foram submetidos aos testes ANOVA a 1 critério e Teste de Tukey (α=5%). Os valores de transmitância foram inferiores a 1%, sendo que as do grupo LT apresentaram, em geral, os maiores valores de transmitância, seguidos dos grupos MO e Z. O GC do cimento...
The aim of the present study was to evaluate the transmittance of different ceramic types and shades and their effects on the degree of conversion (DC) of two dual-cure resin cements. Sixty discs were fabricated with IPS e.max ceramic (Ivoclar Vivadent, Schaan, Liechtenstein) and divided into three groups (n= 20 in each group): LT, MO and Z. For LT and MO groups discs were fabricated with low translucency (LT) and medium opacity (MO) lithium disilicate ceramic, respectively. Discs from Z group were manufactured of zirconia. Each group was divided into five subgroups (n = 4), according to the ceramic shade: A2; A3,5; B2; C2; D3. In the LT group, specimens were heat-pressed in shades cited above and in the MO and Z groups, the discs were initially fabricated as core materials and then veneered with veneer ceramic (IPS e.max Ceram, Ivoclar Vivadent, Schaan, Liechtenstein) in the same shades. A spectrophotometer UV-1800 Shimadzu was used to determine the transmittance percentage of each ceramic specimen (2.0-mm-thick). For DC measurements, the resin cements (Variolink II - Ivoclar Vivadent, Schaan, Liechtenstein and Rely X U200 - 3M ESPE, St. Paul, MN, USA) specimens (thickness: 100 μm) were photocured under the ceramic discs (2.0-mm-thick) for 40 s. Specimens photocured without the ceramics discs were used as control group. ATR/FTIR spectrometry was used to evaluated the extent of polymerization for all cement specimens immediately after photocuring. The results were submitted to one-way ANOVA and Tukey test (α=5%). The transmittance percentage was less than 1% and the LT group had the highest transmittance values, followed by MO and Z groups. The %DC of Variolink II cement was not influenced by the ceramic disc interposition. For Rely X U200 cement, the interposition of some ceramics types/shades (LT A3,5, MO A2, MO A3,5 and Z A3,5) significantly decreased the %DC compared to control group. It was concluded that the transmittance values and %DC...
Subject(s)
Humans , Self-Curing of Dental Resins/methods , Color , Ceramics/chemistry , Resin Cements/chemistry , Light-Curing of Dental Adhesives/methods , Analysis of Variance , Materials Testing , Spectroscopy, Fourier Transform InfraredABSTRACT
O objetivo desta pesquisa foi avaliar a transmitância de diferentes tipos e cores de cerâmicas e seus efeitos no grau de conversão (GC) de dois tipos de cimentos resinosos com modo de polimerização dual. Foram confeccionadas 60 pastilhas com a cerâmica IPS e.max (Ivoclar Vivadent, Schaan, Liechtenstein) e divididas em 3 grupos: LT, MO e Z, com 20 pastilhas cada um. Nos grupos LT e MO, as pastilhas foram confeccionadas com a cerâmica de dissilicato de lítio de baixa translucidez (LT - low transluscency) e de média opacidade (MO - medium opacity), respectivamente. No grupo Z, as pastilhas foram confeccionadas em zircônia. Cada grupo foi subdividido em 5 subgrupos (n=4), de acordo com a cor da cerâmica: A2; A3,5; B2; C2; D3. No grupo LT, as pastilhas foram prensadas nas cores anteriormente citadas e, nos grupos MO e Z, as pastilhas foram, inicialmente, confeccionadas para simular infraestruturas e, posteriormente, receberem aplicação de cerâmica de revestimento IPS e.max Ceram (Ivoclar Vivadent, Schaan, Liechtenstein) nas mesmas cores. O espectrofotômetro UV 1800 Shimadzu foi utilizado para medir a transmitância de cada espécime de cerâmica (2,0 mm de espessura). Para medir o GC, espécimes dos cimentos resinosos Variolink II (Ivoclar Vivadent, Schaan, Liechtenstein) e Rely X U200 (3M ESPE, St. Paul, MN, USA), com espessura de 100 μm, foram fotopolimerizados sob os discos de cerâmica por 40 s. Espécimes dos cimentos fotoativados sem a interposição da cerâmica foram usados como grupo controle. A polimerização dos cimentos foi avaliada através da espectrometria no infravermelho com transformada de Fourier (FTIR) empregando o método de reflexão atenuada total (ATR) imediatamente após a fotopolimerização. Os resultados foram submetidos aos testes ANOVA a 1 critério e Teste de Tukey (α=5%). Os valores de transmitância foram inferiores a 1%, sendo que as do grupo LT apresentaram, em geral, os maiores valores de transmitância, seguidos dos grupos MO e Z. O GC do cimento...
The aim of the present study was to evaluate the transmittance of different ceramic types and shades and their effects on the degree of conversion (DC) of two dual-cure resin cements. Sixty discs were fabricated with IPS e.max ceramic (Ivoclar Vivadent, Schaan, Liechtenstein) and divided into three groups (n= 20 in each group): LT, MO and Z. For LT and MO groups discs were fabricated with low translucency (LT) and medium opacity (MO) lithium disilicate ceramic, respectively. Discs from Z group were manufactured of zirconia. Each group was divided into five subgroups (n = 4), according to the ceramic shade: A2; A3,5; B2; C2; D3. In the LT group, specimens were heat-pressed in shades cited above and in the MO and Z groups, the discs were initially fabricated as core materials and then veneered with veneer ceramic (IPS e.max Ceram, Ivoclar Vivadent, Schaan, Liechtenstein) in the same shades. A spectrophotometer UV-1800 Shimadzu was used to determine the transmittance percentage of each ceramic specimen (2.0-mm-thick). For DC measurements, the resin cements (Variolink II - Ivoclar Vivadent, Schaan, Liechtenstein and Rely X U200 - 3M ESPE, St. Paul, MN, USA) specimens (thickness: 100 μm) were photocured under the ceramic discs (2.0-mm-thick) for 40 s. Specimens photocured without the ceramics discs were used as control group. ATR/FTIR spectrometry was used to evaluated the extent of polymerization for all cement specimens immediately after photocuring. The results were submitted to one-way ANOVA and Tukey test (α=5%). The transmittance percentage was less than 1% and the LT group had the highest transmittance values, followed by MO and Z groups. The %DC of Variolink II cement was not influenced by the ceramic disc interposition. For Rely X U200 cement, the interposition of some ceramics types/shades (LT A3,5, MO A2, MO A3,5 and Z A3,5) significantly decreased the %DC compared to control group. It was concluded that the transmittance values and %DC...
Subject(s)
Self-Curing of Dental Resins/methods , Color , Ceramics/chemistry , Resin Cements/chemistry , Light-Curing of Dental Adhesives/methods , Analysis of Variance , Materials Testing , Spectroscopy, Fourier Transform InfraredABSTRACT
A pesquisa tem como objetivo a aplicação da transmitância espectral utilizando uma esfera de integração para estimar o Fator de Proteção Solar (FPS) de fotoprotetores comerciais para o uso infantil. Fotoprotetores com FPS 30 (A, B e C), disponíveis comercialmente, foram selecionados para avaliação conforme as seguintes metodologias: valor de pH, perfil reológico, e valor de FPS in vitro por espectroscopia. As amostras A, B e C apresentaram, respectivamente, os seguintes valores de pH: 7.8, 7.4 e 7.0. O perfil reológico identificou os sistemas como semissólidos pseudoplásticos não-Newtonianos, com área de histerese. O teste-T (p < 0.05) foi utilizado para confrontar o FPS alegado (FPS = 30) com o estimado por espectroscopia. Estudos in vitro foram considerados de grande importância para a área cosmética, podendo corroborar, previamente, a realização dos estudos de eficácia in vivo. De acordo com os resultados, as amostras A, B e C apresentaram valores de FPS sem diferença estatisticamente significativa, quando comparados àqueles citados nos rótulos. A transmitância espectral utilizando esfera de integração provou ser uma metodologia conveniente, rápida e reprodutível para a avaliação estimada do FPS.
This research focused on the measurement of spectral transmittance using an integrating sphere to estimate the Sun Protection Factor (SPF) of commercial sunscreens oriented for child use. Commercially available SPF 30 sunscreens (A, B and C) were selected and assessed by the following methodology: pH measurement; rheological profile analysis; and in vitro SPF estimation by spectroscopy. Samples A, B and C exhibited, respectively, pH values of 7.8, 7.4 and 7.0. The rheological profile identified the systems as pseudoplastic non-Newtonian semisolids with hysteresis loops. The t-test (p < 0.05) was used to confront the claimed SPF (SPF = 30) with that estimated by spectroscopy. In vitro tests are considered of utmost importance in the cosmetic , since their results may be used to validate submission to subsequent in vivo efficacy experiments. According to our results, sunscreens A, B and C generated SPF values without any significant difference from those claimed on the commercial sunscreen labels. The measurement of spectral transmittance with an integrating sphere proved to be a convenient, fast and reproducible method for SPF estimation.
Subject(s)
Rheology , Spectrum Analysis , Sunscreening AgentsABSTRACT
O presente trabalho teve como objetivo verificar a porcentagem de refletância (R) e transmitância direta (Td), e avaliar a intensidade de fluorescência (F) de 3 sistemas de resinas compostas, Filtek Supreme XT - 3M ESPE (SU), 4 Seasons - Ivoclar Vivadent (4S) e Durafill VS - Kulzer (DU), em cores indicadas para reproduzir esmalte cromático (EC), esmalte acromático (EA) e dentina (D). Como controle foram utilizados discos de esmalte e dentina humanos obtidos a partir de 5 terceiros molares extraídos. Foram confeccionados 5 espécimes por grupo a partir de matrizes metálicas (20 x 38 x 0,37 ± 0,01mm) contendo um orifício circular de 8mm. Os mesmos espécimes foram utilizados para todos os testes, sendo mantidos imersos em água filtrada. Para análise quantitativa dos resultados foi feita a média dos valores percentuais e determinada a área sob a curva de espectrofotometria entre os comprimentos de onda de 340 a 800nm. Foi usado um software gráfico para cálculo da área sob a curva no feixe de luz visível. Para a fluorescência foi utilizado um espectrofluorímetro com incidência de 390nm, sendo escolhido o comprimento de 449nm para a estatística e avaliação. A homogeneidade das variâncias foi verificada através do teste de Levene (α=0,05) e a normalidade dos resíduos de cada conjunto de dados através do teste de Shapiro-Wilk (α=0,05). Os dados foram, então, submetidos à análise de variância de um fator (material) e teste de Tukey para contraste de médias (α = 0,05). Em relação à refletância todas as resinas para EC obtiveram menores valores em comparação ao esmalte. Para Td somente a DU para EC apresentou semelhança estatística com o esmalte. Todas as resinas para dentina obtiveram menores valores de refletância em comparação à dentina, enquanto em Td somente a 4S diferiu das demais, apresentando os maiores valores. As resinas para EA apresentaram menores valores em refletância e maiores em Td em comparação ao esmalte, com exceção da ...
The objective of this study was to verify the percentage of reflectance (R) and direct transmittance (Td), and intensity of fluorescence of 3 resin composite systems, Filtek Supreme XT - 3M ESPE (SU), 4 Seasons Ivoclar Vivadent (4S) and Durafill VS - Kulzer (DU), in colors indicated to reproduce chromatic enamel (CE), achromatic enamel (AE) and dentin (D). Human enamel and dentin discs were obtained from 5 extracted molars and used as control groups. Five specimens were prepared for each group using standardized metallic matrices (20 x 38 x 0.37 ± 0.01mm) with a round perforation of 8mm. The same specimen was assayed under all tests and was maintained stored in water. For quantitative analysis of obtained data, mean values were calculated and the area below the spectrophotometry graph curve between wave lengths of 340 and 800nm (visible light) was determined using a specific software. For fluorescence test, a spectrofluorimeter with 390nm incidence was employed, so that the 449nm wave length was chosen for statistical analysis and evaluations. Variance homogeneity was verified using Levene test (α=0.05) and residual normality for each data set was analyzed by means of Shapiro-Wilk test (α=0.05). Data were submitted to statistical analysis using one-way ANOVA (material) and Tukey's test to verify differences among groups (α = 0.05). Regarding reflectance, all composites for CE obtained lower values when compared to enamel. For Td, only DU for CE presented statistically similar results to enamel. All materials for dentin obtained lower reflectance values than dentin, whereas in Td only 4S presented statistically higher values than the other composites. AE composites showed lower values in reflectance mode and higher values in T d when compared to enamel, except for DU in Td. SU for AE presented the highest values in Td and lowest in R. Among composites for CE evaluated ...