ABSTRACT
Objective:To evaluate the effects of resin infiltration in the treatment of post-orthodontic white spot lesions (WSLs)and compare it with microabrasion.Methods:1 0 subjects with 66 teeth with noncavitated and unrestored WSLs after multibracket treatment were recruited.A simple randomized,split-mouth and controlled design was used to allocate WSLs to the resin infiltration and micro-abrasion groups(n =33).The area of the WSLs were measured photographically by using image analysis software before treatment (T0),1 week(T2)and 3 months(T3)after treatment.Data were analyzed with multifactorial analysis of the variances with repeated measures at an a level of 5% and a power of 80%.Results:The area of the white spot lesions(R)decreased significantly in both groups(P <0.05).At T3 the success rate of resin infiltration group(88.68%)was significantly higher than that of microabrasion group (64.67%)(P <0.05).Conclusion:Resin infiltration is more effective than microabrasion in the treatment of post-orthodontic WSLs.
ABSTRACT
OBJECTIVE: A low-viscosity resin (infiltrant) was used to inhibit the progression of white spot lesions (WSLs) and resolve associated esthetic issues. An alternative pretreatment was explored to increase the pore volume of the surface layer of the WSLs. Also, the penetration effects of the infiltrant were evaluated for various pretreatments. METHODS: Sixty two artificial lesions were fabricated on bovine teeth. As a positive control, 15% HCl gel was applied for 120 seconds. Further, 37% H3PO4 gel was applied for 30 seconds using three methods. The samples were divided as follows: H3PO4 only group, H3PO4 sponge group, and H3PO4 brush group. The acid was gently rubbed with the applicators (i.e., a sponge or brush) throughout the application time. To compare the effects of resin infiltration, twenty paired halves of specimens were treated with an infiltrant (ICON(R)). RESULTS: Thicknesses of the removed surface layers and infiltrated areas were evaluated by confocal laser scanning microscope. The positive control and the 37% H3PO4 brush group failed to show significant differences in the removed thickness (p > 0.05); however, the mean percentage of the infiltrated area was higher in the 37% H3PO4 brush group (84.13 +/- 7.58%) than the positive control (63.51 +/- 7.62%, p < 0.001). Scanning electron microscope observations indicate higher pore volumes for the 37% H3PO4 brush group than for the positive control. CONCLUSIONS: Application of 37% H3PO4 with a brush for 30 seconds increased the pore volume of WSL surface layers and the percentage of infiltrated areas in comparison to the use of 15% HCl for 120 seconds.