ABSTRACT
ZnO nanoparticle-containing carbon composite nanofiber ( ZnO-CNF ) was prepared by the electrospinning of the ZnCl2-PAN precursor, followed by preoxidation and carbonization. The ZnO nanoparticles were uniformly distributed on the surface of the carbon nanofiber with the size of 20-30 nm, confirmed by scanning electron microscopy ( SEM ) . The wettability of the ZnO-CNF was studied by water contact angle test. With Nafion as an additive, the ZnO-CNF modified electrode was successfully constructed by dip-coating. The surface morphology and electrochemical properties of the modified electrode were investigated by SEM and cyclic voltammetry. There was a sensitive response of the ZnO-CNF modified electrode on Pb ions in solution, demonstrated by square wave stripping voltammetry. Under the optimized conditions, a good linear relationship between peak current and Pb2+concentration was obtained in the range of 2. 4×10-10-2. 4×10-7 mol/L (R=0. 998) by 10 min preconcentration at -1. 0 V in 0. 1 mol/L NaAc buffer solution (pH=4. 6). The detection limit was 4. 8×10-11 mol/L. The practical analytical application of the ZnO-CNF modified electrode was assessed by the measurement of the actual water sample and the result was consistent with that obtained by ICP-MS.