ABSTRACT
Objective:To investigate the effects of 3 adhesives on the bond force and durability of polished and glazed zirconia ceram-ics to orthodontic metal brackets respectively.Methods:Universal adhesives,Single Bond Universal(SBU)and Prime&Bond Universal(PBU)were respectively used to bond polished and glazed zirconia to metal braces of maxillary central incisors using TransbondTM MIP(TM)as the control.The shear bond strength(SBS),the fracture morphology and adhesive residual index(ARI)were examed after wa-ter bath or water bath-thermal cycling storage.Results:The adhesive(P<0.001)and storage conditions(P<0.001)significantly af-fected the shear bond strength of zirconia to brackets.There was no significant difference between the polished or glazed groups(P=0.09).SBU showed the stronger SBS and lower ABI,there were significant differences in ARI scores among the 3 cements(P<0.001).Conclusion:SBU may have better bonding performance than PBU and TM in the orthodontic bonding of polished or glazed zir-conia surfaces to the zirconia ceramics.
ABSTRACT
BACKGROUND:For teeth with normal dental crown height,pulp cavity retention crown restoration with different depths of the pulp cavity and different repair materials affects the stress and flexural strength of tooth tissue.For short crown molar defects,the research on pulp cavity repair mainly focuses on clinical observation and in vitro flexural strength experiments. OBJECTIVE:To establish a three-dimensional finite element model for short crown molar restored by the endocrown after root canal treatment to analyze the effects of different pulp cavity retention depths and different repair materials on the distribution and size of dentin equivalent stress. METHODS:Based on establishing the complete model of the short crown mandible first molar,a three-dimensional finite element model was established for repairing the distal adjacent defect of the short crown molar with different pulp cavity retention depths(h=2,3,4 mm)and different repair materials(zirconia,lithium disilicate).Under the oblique loading,the equivalent stress distribution was observed.The peak value of dentin equivalent stress and the mean value of equivalent stress near the bottom of the mesial pulp cavity wall were calculated. RESULTS AND CONCLUSION:(1)Equivalent stress concentration areas:The stress of complete short crown molar and restored models mainly concentrated in the mesial root mesial neck and mesial root lingual neck.The stress concentration area was found in the mesial pulp cavity wall corresponding to the bottom layer of restored models,and the stress concentration was obvious in the 4 mm retention depth group.(2)Under the same repair material,the peak value of dentin equivalent stress was the lowest at 3 mm for all models after repair.The average value of equivalent stress near the bottom of the mesial pulp cavity wall was lowest at 3 mm.(3)Under the same retention depth,there was no significant difference between the two materials in the dentin equivalent stress peak and the mean value near the bottom of the mesial pulp cavity.(4)The results showed that under the conditions of this experiment,the endocrown was used to repair the defect of the short crown molar and the retention depth was 3 mm,which was more beneficial to protect the remaining dental tissue.The selection of zirconia or lithium disilicate as the repair material had little effect on the dentin stress.
ABSTRACT
Objective@#To compare the effects of 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP)- and silane-based primers with those of MDP-based primers on zirconia-resin bonding via multiple levels of aging.@*Methods@#Zirconia blocks were divided into 4 groups (n = 21) according to the primer used: MDP-based Z-Prime Plus (ZP), silane-based Monobond-S (MS), MDP- and silane-based Clearfil Ceramic Primer (CCP) and no primer (Blank). After pretreatment with or without the primers followed by bonding with cement Duo-Link, each group was subdivided into 3 subgroups (n = 7) according to aging level: 24 hours of water storage at 37 ℃ (24 h), 30 days of water storage at 37 ℃(30 d), and 30 d plus 3 000 thermal cycles (30 d/TC). After aging, shear bond strength (SBS) tests and failure mode analyses were conducted@*Results@#ZP, MS and CCP groups had greater SBSs than did the BLANK group (P<0.01). From 24 h to 30 d, the shear bond strength significantly increased (P<0.05); however, the shear bond strength decreased significantly from 30 d to 30 d/TC (P<0.01) and fell below baseline (30 d/TC vs. 24 h, P<0.01). Within the primer groups, CCP exhibited a higher SBS than ZP and MS at each aging level (P<0.001). The bonding strength of ZP was greater than that of MS at 30 d (P = 0.029) but lower than that of MS at 30 d/TC (P = 0.037). From 30 d to 30 d/TC, the percent decrease in the bonding strength of ZP was significantly greater than that of MS (82.43% vs. 64.90%).@*Conclusion@#MDP-based primers function better for zirconia-resin bonding when they contain silane coupling agents.
ABSTRACT
Objective@#To investigate the clinical effect of lithium disilicate glass ceramic cantilever resin-bonded fixed partial dentures (CRBFPDs) on single anterior tooth loss to provide a reference for the selection of restoration methods for single anterior tooth loss.@*Methods@#This study was reviewed and approved by the Ethics Committee, and informed consent was obtained from the patients. Forty-two patients with less than two anterior teeth with monomaxillary loss were included in this study. After 6 months, 1 year, 2 years, and 3 years, the aesthetic and functional effects of the restorations and the periodontal health status were evaluated, and the visual analog scale (VAS) was used to assess patient satisfaction.@*Results@#During the observation period, the connector fractured in one case within 3 months. One case had debonded within 2 years. The aesthetic restoration effect of all lithium disilicate glass ceramic CRBFPDs was categorized as Class A. The periodontal health was good, there was no clinical absorption in the soft and hard tissues of the abutment or subbridge, periodontal status according to the evaluation indices was classified as class A, and the total satisfaction rate of the patient was 100%.@*Conclusion@#For single anterior tooth loss patients, lithium disilicate glass ceramic cantilever resin-bonded fixed partial denture can achieve the restoration effect of less invasion, better adhesion, aesthetics, comfort and good biocompatibility. With high patient satisfaction, it can be considered an ideal restoration method for replacing a single anterior tooth.
ABSTRACT
Objective: The aim of this study was to evaluate the marginal gap of frameworks produced using the CAD-CAM system, from zirconia and lithium disilicate blocks, adapted to a tooth preparation and a gypsum die. Material and Methods: For this study, a human first molar tooth was used as a master model with a full crown preparation. It was molded 20 times to obtain the gypsum die and randomly divided into 2 groups (n=10) for the fabrication of zirconia and lithium disilicate frameworks. The frameworks were made using pre-sintered zirconia blocks and lithium disilicate blocks, both CAD-CAM systems. The marginal gap was measured in µm at four points (buccal, palatal, mesial, and distal) using a comparator microscope with 30x magnification, with the framework seated on the master model (tooth), and on the gypsum die. Marginal gap data (µm) were evaluated using two-way analysis of variance and Tukey's test with a significance level of 5%. Results: The results showed that there was no statistically significant interaction between the factors studied (p=0.223) or isolated factors (ceramic factor p=0.886 and die factor p=0.786). Conclusion: Both ceramics produced using the CAD-CAM technique did not exhibit statistical differences in marginal adaptation on the two types of substrates, both on tooth preparation and on the gypsum die (AU)
Objetivo: O objetivo deste estudo foi avaliar o espaço marginal de estruturas produzidas usando o sistema CAD-CAM, a partir de blocos de zircônia e dissilicato de lítio, adaptadas a um preparo sobre dente e a um troquel de gesso. Material e Métodos: Para este estudo, um dente molar humano foi utilizado como modelo mestre com preparo para coroa total. Este foi moldado 20 vezes para obter o troquel de gesso e dividido aleatoriamente em 2 grupos (n=10) para a fabricação de estruturas de zircônia e dissilicato de lítio. As estruturas foram feitas usando blocos de zircônia pré-sinterizados e blocos de dissilicato de lítio, ambos sistemas para CAD-CAM. O espaço marginal foi medido em µm, em quatro pontos (bucal, palatal, mesial e distal), utilizando um microscópio comparador com ×30 de ampliação e com a estrutura assentada no modelo mestre (dente) e no troquel de gesso. Os dados de espaço marginal (µm) foram avaliados usando análise de variância bidirecional e teste de Tukey com um nível de significância de 5%. Resultados: Os resultados mostraram que não houve interação estatisticamente significativa entre os fatores estudados (p=0,223) ou isoladamente (fator cerâmica p=0,886 e fator troquel p=0,786). Conclusão: Ambas as cerâmicas produzidas usando a técnica CAD-CAM não apresentaram diferenças estatísticas em relação à adaptação marginal nos dois tipos de substratos, tanto na preparação dentária quanto no troquel de gesso(AU)
Subject(s)
Dental Prosthesis , Computer-Aided Design , Dental Marginal Adaptation , Dental PorcelainABSTRACT
Context: Fracture of endodontically treated teeth is a grave sequela that a clinician should seriously ponder. Suitable selection of restorative materials is a requisite for long?term clinical success. Aims: To compare the fracture resistance of endodontically treated teeth restored with three different posts luted using two different cements under all ceramic crowns. Settings and Design: This in vitro study was conducted in the Department of Prosthodontics, Government Dental College, Kottayam, Kerala, India. Methods and Material: Thirty endodontically treated single?rooted mandibular premolars in which post spaces were prepared and divided into three different groups. Group 1 (n = 10): zirconia post group. Group 2 (n = 10): quartz fibre post group. Group 3 (n = 10): glass fibre post group. Each group is sub?divided into two based on the luting system: resin?modified glass ionomer cement (RMGIC) or dual?cure resin cement (DCRC). The fracture resistance testing was performed in a universal testing machine with a crosshead speed of 0.5 mm/min. Statistical Analysis Used: The mean fracture resistance were analysed using independent sample Student t?test and one?way ANOVA. Results: Within the zirconia post group, the mean fracture resistance was higher in DCRC sub?group compared to the RMGIC sub?group and the difference was statistically significant (p = 0.017). The difference in fracture resistance between three different post systems was not found to be statistically significant with respect to both the luting systems. Conclusions: It was observed that when zirconia post is used, the mean fracture resistance was higher in dual?cure resin group compared to the resin?modified GIC group.
ABSTRACT
OBJECTIVE@#To study microstructure, friction and wear behaviors of silicon-lithium spray coating on the surface of zirconia ceramics and to preliminarily evaluate its esthetic so as to provide support and guidance for the clinical application.@*METHODS@#Zirconia ceramic specimens were randomly divided into three groups: coating group (two subgroups), polishing group (two subgroups), and glazing group (four subgroups), with 10 samples in each subgroup. The two subgroups of coating group were the zirconia ceramics with the untreated and preliminary polishing surfaces sprayed with silicon-lithium coating, respectively. The two subgroups of polishing group were preliminary polishing and fine polishing of zirconia ceramics, respectively. The four subgroups of glazing group were preliminarily polished zirconia ceramics glazed with Biomic and Stain/Glaze products, respectively; and untreated zirconia ceramics glazed with Biomic and Stain/Glaze products, respectively. The above 8 subgroups of zirconia ceramic specimens were used as friction pairs with 80 steatite ceramics for 50 000 chewing cycles under 50 N vertical load and artificial saliva lubrication using chewing simulation. Scanning electron microscope was used to observe the microstructure of the surface and section of the coating group, and the thickness of the coating and glazing were measured. The linear roughness of the coating and polishing groups was mea-sured using a laser confocal scanning microscope. Vickers hardness was measured using a microhardness tester and the esthetic of zirconia ceramic full crown sprayed with silicon-lithium coating was preliminarily evaluated. White light interferometer was used to measure the width, the maximum depth and the volume of the wear scars of each group, and the wear depth of steatite ceramics and wear rate of zirconia ceramic specimens were calculated. Kruskal-Wallis nonparametric test and Dunn's multiple comparisons test were used to analyze the wear depth of each group (α=0.05).@*RESULTS@#The microstructures of the silica-lithium spray coatings on the untreated and preliminarily polished zirconia ceramic surfaces showed the protruding defects, and the line roughness of coating group was larger than that of the polishing group. The median thickness of the silica-lithium spray coating on the preliminarily polished zirconia ceramic was 13.0 μm (interquartile range, IQR: 11.6, 17.9), while that of the silica-lithium spray coating on the untreated zirconia ceramic was 4.4 μm (IQR: 4.1, 4.7). The Vickers hardness and wear rate of the coating group were between the polishing group and the glazing group. The wear depths of the wear scars of steatite ceramics were the glazing group, coating group, and polishing group in descending order, and there was statistically significant difference between glazing and polishing groups (P < 0.05). With the increase of polishing procedure, the wear depth of steatite ceramics decreased in each subgroups. The orders of maximum depth and volume of wear scars of zirconia ceramic were the glazing group, coating group, and polishing group in descending order, and there was statistically significant difference in the maximum depth of wear scars between glazing and polishing groups (P < 0.05).@*CONCLUSION@#The silica-lithium spray coating on the zirconia ceramic, can be used as a new method for zirconia ceramic surface treatment, because it can increase the esthetic of zirconia ceramics compared with polishing and reduce the wear of steatite ceramics compared with glazing.
Subject(s)
Humans , Silicon , Materials Testing , Friction , Lithium , Cicatrix , Surface Properties , Silicon Dioxide , Zirconium/chemistry , Ceramics , Dental PorcelainABSTRACT
Objective: to evaluate the effect of novel zirconia surface treatment method on shear bond strength between zirconia and veneering porcelain compared to air abrasion and CoJet surface treatment methods. Material and Methods: twenty-one zirconia ceramic discs were fabricated with diameter of 7mm and 3mm thickness and divided according to surface treatment into three subgroups, control group I: Air Abrasion (n=7), group II: CoJet (n=7) and group III: Z-etch (n=7). Porcelain was built over the zirconia specimens with a customized mold and fired in a ceramic furnace. All specimens were thermocycled (20000 cycles) between 5°C 55 °C with a dwell time of 30 seconds in distilled water and shear bond strength of veneering porcelain to each zirconia specimen was tested using a universal testing machine. Results: numerical data were explored for normality by checking the distribution of data and using tests of normality (Kolmogorov-Smirnov and Shapiro-Wilk tests). One-way ANOVA test was used to compare between the groups. There was a statistically significant difference between the three groups (P-value = 0.002, Effect size = 0.503). Pair-wise comparisons between groups revealed that Z-etch showed the statistically significantly highest mean shear bond strength. Conclusion: zirconia coating using z-etch is showing promising results in promoting higher bond strength than conventional surface treatment methods as air abrasion and silica coating (AU)
Objetivo: avaliar o efeito do novo método de tratamento de superfície de zircônia na resistência ao cisalhamento entre a zircônia e a porcelana de cobertura em comparação com os métodos de abrasão a ar e jateamento com CoJet. Material e Métodos: vinte e um discos de zircônia foram confeccionados com diâmetro de 7mm e espessura de 3mm e divididos de acordo com o tratamento de superfície em três subgrupos, grupo controle I: Abrasão a ar (n=7), grupo II: CoJet (n=7) e grupo III: Z-etch (n=7). A porcelana foi aplicada sobre os espécimes de zircônia com um molde personalizado e sinterizada em forno de cerâmica. Todos os espécimes foram termociclados (20.000 ciclos) entre 5°C - 55°C com um tempo de permanência de 30 segundos em água destilada e a resistência ao cisalhamento da porcelana de cobertura foi testada através de uma máquina de ensaio universal. Resultados: os dados numéricos foram avaliados quanto à normalidade, verificando a distribuição dos dados e utilizando testes de normalidade (testes de Kolmogorov-Smirnov e Shapiro-Wilk). O teste ANOVA de um fator foi utilizado para comparar os grupos. Houve uma diferença estatisticamente significativa entre os três grupos (P-valor = 0,002, tamanho do efeito = 0,503). As comparações pareadas entre os grupos revelaram que o Z-etch apresentou a resistência de união ao cisalhamento estatisticamente significativamente mais alta. Conclusão: o revestimento de zircônia utilizando Z-etch mostrou resultados promissores para o aumento da resistência de união em comparação aos métodos convencionais de tratamento de superfície, como abrasão a ar e revestimento de sílica (AU)
Subject(s)
Air Abrasion, Dental , Shear Strength , Dental MaterialsABSTRACT
Objective: the aim of this study was to compare the mechanical behavior of different ceramics when used in thin vertical preparations versus traditional horizontal preparation. Material and Methods: two stainless-steel dies were milled to simulate a minimally invasive vertical preparation (VP) and a traditional horizontal preparation (HP) for an all-ceramic crown of a maxillary first premolar. The stainless-steel dies were duplicated using epoxy resin. Eighty monolithic crowns were milled and divided into 2 groups according to preparation design. Each design group was subdivided into 4 sub-groups according to material (n=10): IPS e.max CAD (lithium disilicate), Bruxzir shaded zirconia (full contour zirconia), CeraSmart (resin nanoceramic) and CEREC Tessera (advanced lithium disilicate). The crowns were cemented on their relevant epoxy resin dies using self-adhesive resin cement. All specimens were subjected to 15,000 thermocycles and then loaded to fracture in a universal testing machine. Data were analyzed using two-way ANOVA and Tukey pair wise comparison test. Results: the fracture resistance mean values of the VP (1344 + 118 N) was significantly lower than the HP design (1646 + 191 N). Ceramic crowns made of full contour zirconia had higher fracture resistance mean values (2842 + 380 N) than advanced lithium disilicate (1272 + 125 N) followed by lithium disilicate crowns (983 + 52 N) and resin nanoceramic (882 + 61 N). Conclusion: both vertical and horizontal preparations, regardless the different ceramic materials, showed clinically acceptable fracture resistance values. (AU)
Objetivo: o objetivo deste estudo foi comparar o comportamento mecânico de diferentes cerâmicas quando utilizadas em preparos verticais finos ou preparos horizontais tradicionais. Material e Métodos: dois modelos de aço inoxidável foram fresados para simular um preparo vertical minimamente invasivo (PV) e um preparo horizontal tradicional (PH) para uma coroa totalmente em cerâmica de um primeiro pré-molar superior. As matrizes de aço inoxidável foram duplicadas usando resina epóxi. Oitenta coroas monolíticas foram fresadas e divididas em 2 grupos de acordo com o desenho do preparo. Cada grupo foi subdividido em 4 subgrupos de acordo com o material (n=10): IPS e.max CAD (dissilicato de lítio), zircônia Bruxzir (zircônia de contorno total), CeraSmart (resina nanocerâmica) e CEREC Tessera (dissilicato de lítio avançado). As coroas foram cimentadas em suas respectivas matrizes de resina epóxi usando cimento resinoso autoadesivo. Todos os espécimes foram submetidos a 15.000 ciclos térmicos e então carregados até a fratura em uma máquina de teste universal. Os dados foram analisados usando ANOVA com dois fatores e teste de comparação por pares de Tukey. Resultados: os valores médios de resistência à fratura do PV (1344 + 118 N) foram significativamente menores do que PH (1646 + 191 N). As coroas de cerâmica feitas de zircônia de contorno total apresentaram maiores valores médios de resistência à fratura (2842 + 380 N) do que dissilicato de lítio avançado (1272 + 125 N), seguido por coroas de dissilicato de lítio (983 + 52 N) e resina nanocerâmica (882 + 61 N). Conclusão: preparos verticais e horizontais, independentemente dos diferentes materiais cerâmicos, apresentaram valores de resistência à fratura clinicamente aceitáveis. (AU)
Subject(s)
Bicuspid , Dental Prosthesis , Tooth Crown , Resin Cements , Epoxy Resins , Fractures, BoneABSTRACT
Objective: The aim of the study was to evaluate the short and long-term effects of different surface treatments on the bond strengths of zirconia. Material and Methods: 225 blocks of sintered zirconia samples (4 x 4 x 3 mm) were divided into five groups and subjected to different surface treatments: control group (without surface treatment), alumina group (sandblasting [25-µm-aluminum-oxide]), alumina+Ambar Universal-APS (AU) group, CoJet group (silica-coated [30-µm silica-modified aluminum particles]), and CoJet+AU group. Subsequently, zirconia samples were cemented against resin samples (total dimensions: 8x8x6mm) and assigned to three storage conditions: dry, humid (artificial saliva at 37°C for 30-days) or thermocycling [100.000-cycles] (n=15 per group). The microtensile bond strength (µTBS) was determined using a universal testing machine. The failure modes were observed and analyzed using a stereomicroscope. Normality tests, descriptive statistics, and two-way ANOVA, followed by post-hoc comparisons, were performed to evaluate the effect of surface treatments and storage conditions on µTBS (α=0.05). Results: µTBS was influenced by surface treatment in the short and long-term (P<0.0001). The highest values were found in CoJet+AU in dry (33.51 ±2.48 MPa), humid (32.87 ±2.68 MPa) and thermocycling (21.37 ±1.68 MPa) storage conditions compared with others. Interestingly, no significant differences in µTBS were found among alum +AU and CoJet alone under any of the three storage conditions. Adhesive failure increased in all groups after thermocycling, but CoJet+AU had the lowest values of adhesive failure compared with others. Conclusion: The combination of CoJet and Ambar universal as a surface treatment for zirconia specimens provides significantly higher short and long-term bond strengths of adhesive cementation (AU)
Objetivo: O objetivo do estudo foi avaliar os efeitos de curto e longo prazo de diferentes tratamentos de superfície na resistência de adesão da zircônia. Material e Métodos: 225 blocos de amostras de zircônia sinterizada (4 x 4 x 3 mm) foram divididos em cinco grupos e submetidos a diferentes tratamentos de superfície: grupo controle (sem tratamento de superfície), grupo de alumina (jateamento de 25 µm de óxido de alumínio), grupo alumina+Ambar Universal-APS (AU), grupo CoJet (partículas de alumínio modificadas por sílica de 30 µm), e grupo CoJet+AU. Posteriormente, as amostras de zircônia foram cimentadas em amostras de resina (dimensões totais: 8x8x6mm) e designadas para três condições de armazenamento: seco, úmido (saliva artificial a 37°C por 30 dias) ou ciclagem térmica (100.000 ciclos) (n=15 por grupo). A resistência de adesão de microtensão (µTBS) foi determinada usando uma máquina de teste universal. Os modos de falha foram observados e analisados usando um estereomicroscópio. Testes de normalidade, estatísticas descritivas e ANOVA de duas vias, seguidas de comparações pos-hoc, foram realizados para avaliar o efeito dos tratamentos de superfície e das condições de armazenamento na µTBS (α=0.05). Resultados: A µTBS foi influenciada pelo tratamento de superfície a curto e longo prazo (P<0.0001). Os valores mais altos foram encontrados em CoJet+AU nas condições de armazenamento a seco (33.51 ±2.48 MPa), úmido (32.87 ±2.68 MPa) e ciclagem térmica (21.37 ±1.68 MPa) em comparação com os outros. Curiosamente, não foram encontradas diferenças significativas na µTBS entre alum +AU e CoJet sozinho em nenhuma das três condições de armazenamento. A falha adesiva aumentou em todos os grupos após a ciclagem térmica, mas CoJet+AU teve os valores mais baixos de falha adesiva em comparação com os outros. Conclusão: A combinação de CoJet e Ambar Universal como tratamento de superfície para espécimes de zircônia proporciona resistências de adesão significativamente mais altas a curto e longo prazo para cimentação adesiva. (AU)
Subject(s)
Dental CementsABSTRACT
Os implantes de zircônia estão cada vez maispresentes no mercado, e no catálogo das grandes marcas, devido à sua alta capacidade estética e excelente compatibilidade com os tecidos moles, além de trazer uma opção metal freepara a Implantodontia, algo bastante discutido nos tempos atuais. No entanto, uma questão bastante observada, mas ainda pouco comentada, é o surgimento das novas conexões protéticas presentes nestes implantes. Dessa forma, a proposta deste artigo é apresentar ao leitor as conexões protéticas desses implantes de zircônia, levando-o a refletir sobre as mudanças e futuro da implantodontia.
ABSTRACT
Background: Porcelain combined with zirconia core substructure has low fracture toughness. Nanoparticles are incorporated into the porcelain to boost its mechanical properties. Aims: To evaluate the effect of the incorporation of silver oxide and titanium oxide nanoparticles into porcelain powder on the bond strength of porcelain veneer to zirconia core. The flexural strength of nanoparticles?modified porcelain was also evaluated. Materials and Methods: The flexural strength of feldspathic porcelain was measured (according to ISO specifications number 6872) after the incorporation of silver and titanium oxide nanoparticles. For measuring the bond strength at the porcelain?zirconia interface, 70 bars (4 × 4 × 12 mm) of zirconia were cut and fired in a furnace. The control and nanoparticles?modified porcelain powders were built up on the zirconia bars and fired to create veneers of 3 mm height, 4 mm width and 4 mm thickness. The porcelain veneers were de?attached from the zirconia core by the universal testing machine. The failure load was recorded to calculate the bond strength. Statistical Analysis: The data were analysed with one?way analysis of variance followed by Tukey’s test. Results: The addition of 0.5–1.5% silver oxide nanoparticles to feldspathic porcelain increased the flexural strength. The addition of 1.0–4.0% titanium oxide nanoparticles to feldspathic porcelain increased the flexural strength. Either 0.5–1.0% silver oxide or 3.0–4.0% titanium oxide nanoparticles in feldspathic porcelain increased the shear bond strength to zirconia core. Conclusion: The flexural strength of porcelain veneer and the bond strength at porcelain?zirconia interface can be improved by adding either 0.5% silver oxide nanoparticles or 4% titanium oxide nanoparticles to porcelain powder.
ABSTRACT
Background and Aim of Study: Early childhood caries is a multifactorial disease process affecting children below 71 months of age and continues to be a global health problem. Stainless steel crowns (SSCs) are widely used and are very popular in pediatric dentistry due to its superiority and durability when compared with multisurface amalgam restorations. However, one of the major disadvantages with these crowns is the poor esthetics. Parents often request for a more esthetic alternative to the SSC. Zirconia crowns are one of the tooth-colored full crown restorations currently available for use in primary teeth. These are available as both preformed and custom-made crowns and show excellent esthetics. However, these require extensive tooth preparation with a subgingival finish lines, which would cause gingival trauma and bleeding during the preparation. The present study uses intraoral scanners for making the custom-made zirconia crowns, which will avoid the conventional impressions. Currently, there are no studies available in pediatric dentistry regarding CAD-CAM crowns. Hence, there is a need for the study. Aim: The aim of this study is to clinically evaluate the performance of preformed SSCs and custom-made zirconia crowns in primary molars. To elicit parental and patient satisfaction with respect to preformed SSCs and custom made zirconia crowns and to radiographically compare the interproximal bone height for 1 year. Methods: The patients were selected with purposive sampling. The tooth of interest was prepared according to the crown it would receive. The upper and the lower arch of the tooth receiving custom-made zirconia crown was scanned using an intraoral scanner. The crowns were cemented using Type 1 glass ionomer cement (GIC) (SSC) and resin modified GIC (custom-made zirconia crown). After the crown placement, the patient and the parent's satisfaction was scaled regarding the time taken, comfort, cost of crown, appearance of crown, etc., using a 5-point Likert scale. A baseline radiograph was taken after crown placement. The patient was recalled every 3 months till 1 year for evaluation (loss of retention, loss of proximal contact, gingival inflammation, opposing tooth wear, and marginal integrity). At the end of 1 year, radiographs were taken to check the interproximal bone. Results: After 1 year evaluation of custom-made zirconia crowns and preformed SSCs in primary molars, it was shown that both SSC and zirconia crowns showed good gingival scores but zirconia crown was better than SSC in improving the gingival health. SSCs showed better results with respect to the opposing tooth wear and marginal adaptability. Parents as well as patients preferred a tooth-colored crown as a treatment option. Conclusion: Custom-made zirconia crowns are comparable to the preformed SSCs and they show better gingival scores and excellent color match.
ABSTRACT
@#The endocrown, a modified overlay or crown, is considered to have the advantages of adhesive retention and mechanical retention. Marginal adaptation and mechanical strength are common criteria for evaluating endocrowns. This review studied these aspects of endocrowns to guide further clinical application. Results from previous academic studies indicate that endocrowns made of different materials, such as glass-based ceramics, zirconia-based ceramics and resin-based ceramics, exhibit clinically acceptable marginal adaptation. Zirconia is a common dental material, but when used in endocrowns, it tends to present a risk of irreparable tooth root fractures. Compared with products manufactured with zirconia, endocrowns manufactured with resin-based ceramics and glass-based ceramics, such as lithium disilicate ceramics, do not tend to cause irreparable results, such as tooth root fracture, but their mechanical strengths are not as good as those of zirconia. At the same time, the tooth prepration design such as the types of endocrowns, the pulp chamber extension depth and angles, the endocrown thickness can influence the mechanical strength of endocrowns as well. Compared with traditional zirconia, self-glazed zirconia, a new type of material used to restore defective teeth, has the similar elasticity modulus(210 GPa)and better aesthetic advantages, and is suitable for short crown patients with insufficient occlusal space. Further study is warranted to improve the performance of endocrowns made from ceramic materials to prevent root fracture.
ABSTRACT
@#All-ceramic restorations are widely used in oral restoration because of their beauty and high strength. Glass ceramics and zirconia all-ceramic materials are the two most widely used all-ceramic materials in the clinic. However, when all-ceramic restorations need to be removed due to marginal microleakage and secondary caries, its high strength and high bonding strength greatly increase the difficulty of removal. In recent years, clinicians have tried to use Er: YAG lasers to remove all-ceramic restorations. The Er: YAG laser can be safely and efficiently applied to the removal of glass restorations, and it can also play a role in thinner zirconia restorations. Various factors, such as the material and thickness of the all-ceramic restoration, the type of cement, and the laser power, can affect the speed of removal of the Er: YAG laser. However, the current research is limited to case reports and in vitro studies, lacking systematic clinical research. The specific mechanism of Er: YAG laser removal of all-ceramic restorations and the influence of laser frequency, adhesive type, and abutment on the removal speed need to be further demonstrated by follow-up research.
ABSTRACT
OBJECTIVE@#To investigate the effect of porous surface morphology of zirconia on the proliferation and differentiation of osteoblasts.@*METHODS@#According to different manufacturing and pore-forming methods, the zirconia specimens were divided into 4 groups, including milled sintering group (M-Ctrl), milled porous group (M-Porous), 3D printed sintering group (3D-Ctrl) and 3D printed porous group (3D-Porous). The surface micromorphology, surface roughness, contact angle and surface elements of specimens in each group were detected by scanning electron microscope (SEM), 3D laser microscope, contact angle measuring device and energy-dispersion X-ray analysis, respectively. MC3T3-E1 cells were cultured on 4 groups of zirconia discs. The cell morphology of MC3T3-E1 cells on zirconia discs was eva-luated on 1 and 7 days by SEM. The cell proliferation was detected on 1, 3 and 5 days by cell counting kit-8 (CCK-8). After osteogenic induction for 14 days, the relative mRNA expression of alkaline phosphatase (ALP), type Ⅰ collagen (Colla1), Runt-related transcription factor-2 (Runx2) and osteocalcin (OCN) in MC3T3-E1 cells were detected by real-time quantitative polymerase chain reaction.@*RESULTS@#The pore size [(419.72±6.99) μm] and pore depth [(560.38±8.55) μm] of 3D-Porous group were significantly larger than the pore size [(300.55±155.65) μm] and pore depth [(69.97±31.38) μm] of M-Porous group (P < 0.05). The surface of 3D-Porous group appeared with more regular round pores than that of M-Porous group. The contact angles of all the groups were less than 90°. The contact angles of 3D-Ctrl (73.83°±5.34°) and M-Porous group (72.7°±2.72°) were the largest, with no significant difference between them (P>0.05). Cells adhered inside the pores in M-Porous and 3D-Porous groups, and the proliferation activities of them were significantly higher than those of M-Ctrl and 3D-Ctrl groups after 3 and 5 days' culture (P < 0.05). After 14 days' incubation, ALP, Colla1, Runx2 and OCN mRNA expression in 3D-Porous groups were significantly lower than those of M-Ctrl and 3D-Ctrl groups (P < 0.05). Colla1, Runx2 and OCN mRNA expressions in M-Porous group were higher than those of 3D-Porous group (P < 0.05).@*CONCLUSION@#The porous surface morphology of zirconia can promote the proliferation and adhesion but inhibit the differentiation of MC3T3-E1 cells.
Subject(s)
Cell Differentiation , Cell Proliferation , Ceramics , Osteoblasts , Osteogenesis , Porosity , ZirconiumABSTRACT
Objective: This study aimed to evaluate the clinical performance of two inlay-retained bridge designs (proximal shaped and inlay shaped) in single missing posterior teeth cases. Material and Methods: A total of 70 cases with missing single posterior teeth were included in this study and divided into two groups with a 1:1 allocation ratio (n = 35 for each group). Group 1 (the control group): this group received an inlay retained bridge with inlay design on both abutments. Group 2 (the intervention group): this group received an inlay retained bridge with a proximal box on both abutments. PMMA resin (YAMAHACHI PMMA) was used for the try-in stage and monolithic zirconia (Katana, Kuraray) was used for the final restorations. The restoration surfaces were treated using sandblasting and Z-prime S (Bisco) and the cementation was done by using self-adhesive resin cement (Bisco). Fracture, marginal adaptation, postoperative sensitivity, caries, and gingivitis were assessed using the modified United States Public Health Service for restoration clinical assessments (MUSPHS standards) over 12 months of follow-up. Results: The results show there was no significant difference between the two groups. Kaplan-Meier survival curve was constructed to calculate the mean survival estimates of the two groups and we found that the two groups were clinically successful during a one-year follow-up. Conclusion: Both designs of inlay retained fixed dental prostheses revealed successful clinical performance in terms of Fracture, marginal adaptation, postoperative sensitivity, caries, and gingivitis (AU)
Objetivo: O objetivo deste estudo foi avaliar o desempenho clínico de dois modelos de ponte fixa por inlay (formato proximal e formato inlay) em casos de dentes posteriores perdidos. Material e Métodos: Um total de 70 casos com perda de um único dente posterior foi incluído neste estudo e dividido em dois grupos com uma razão de alocação de 1: 1 (n = 35 para cada grupo). Grupo 1 (grupo controle): Este grupo recebeu uma ponte fixa por inlay com deseho de inlay em ambos os pilares. Grupo 2 (grupo intervenção): Este grupo recebeu uma ponte fixa inlay com uma caixa proximal em ambos os pilares. Resina de PMMA (YAMAHACHI PMMA) foi usada para a etapa de try-in e a zircônia monolítica (Katana, Kuraray) foi utilizada para as restaurações finais. As superfícies das restaurações foram jateadas com Z-prime S (Bisco) e a cimentação realizada com cimento resinoso autoadesivo (Bisco). Fratura, adaptação marginal, sensibilidade pós-operatória, cárie e gengivite foram avaliadas usando o Serviço de Saúde Pública dos Estados Unidos modificado para avaliações clínicas de restauração (padrões MUSPHS) ao longo de 12 meses de acompanhamento. Resultados: Os resultados mostraram que não houve diferença significativa entre os dois grupos. A curva de sobrevida de Kaplan-Meier foi construída para calcular as estimativas de sobrevida média dos dois grupos e foi concluído que os dois grupos foram clinicamente bem-sucedidos durante um acompanhamento de um ano. Conclusão: Ambos os modelos de próteses dentárias fixas de inlay revelaram desempenho clínico bem-sucedido em termos de fratura, adaptação marginal, sensibilidade pós-operatória, cárie e gengivite(AU)
Subject(s)
Resin Cements , Polymethyl Methacrylate , Denture, Partial, Fixed , Fractures, BoneABSTRACT
Abstract This study evaluated the surface characteristics and bond strength of Y-TZP treated with Er:YAG laser at different focal distances. 120 Y-TZP blocks were divided into five groups (n=24), according to the surface treatment: no treatment (C-); sandblasting with silica-coated aluminum oxide particles (C+); and Er:YAG laser application at focal distances of 1mm (Er:YAG-1), 4mm (Er:YAG-4), and 7mm (Er:YAG-7). Surface characteristics were analyzed using Vickers microhardness, confocal laser microscope, scanning electron microscopy (SEM), and X-ray diffractometer (XRD). For the bond strength test, 100 Y-TZP blocks were subdivided into two subgroups (n=10), according to the resin cement used: with (MDP+) or without 10-methacryloyloxydecyl dihydrogen phosphate (MDP-). The Vickers microhardness and surface roughness were analyzed by one-way ANOVA and bond strength by two-way ANOVA and Tukey's test for both (α=0.05). Vickers microhardness differences were not observed between the groups (p>0.05); C+ showed higher surface roughness values. SEM images showed micromorphological differences between the groups. The XRD data detected tetragonal crystals for C- and, for the other groups, tetragonal and monoclinic peaks. For bond strength, no statistically difference significance were observed among the cements with or without MDP (p>0.05) but showed significant difference between the surface treatments (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Suggested that the Er:YAG laser cannot replace conventional treatment with aluminum oxide particles and the presence of MDP in the resin cement had no influence on the bond strength.
Resumo Este estudo avaliou as características de superfície e resistência de união de Y-TZP tratado com laser de Er: YAG em diferentes distâncias focais. Cento e vinte blocos de Y-TZP foram divididos em cinco grupos (n=24), de acordo com a superfície de tratamento: sem tratamento (C-); asperização com partículas de óxido de alumínio revestidas por sílica (C +); e aplicação de laser Er: YAG a distâncias focais de 1 mm (Er: YAG-1), 4 mm (Er: YAG-4) e 7 mm (Er: YAG-7). As características de superfície foram analisadas por meio de microdureza Vickers, microscópio confocal a laser, microscopia eletrônica de varredura (MEV) e difratômetro de raios-X (DRX). Para o ensaio de resistência de união, cem blocos de Y-TZP foram subdivididos em 2 subgrupos (n=10) de acordo com o cimento resinoso utilizado (n=12): com 10-metacriloiloxidecil dihidrogenofosfato (MDP+) ou sem (MDP-). Microdureza Vickers e rugosidade de superfície foram analisadas por ANOVA a 1 fator e a resistência de união por ANOVA a 2 fatores e ambos seguidos de teste complementar de Tukey (α=0,05). Não foram observadas diferenças de microdureza Vickers entre os grupos; C+ apresentou maiores valores de rugosidade superficial. Imagens de MEV mostraram diferenças micromorfológicas entre os grupos. Os dados de DRX detectaram apenas cristais tetragonais para C- e, para os outros grupos, picos de zircônia nas fases tetragonal e monoclínica. Para a resistência de união, não foram observadas diferenças estatisticamente significante entre os cimentos com e sem MDP (p>0.05), mas foram observadas diferenças significativas entre os tratamentos de superfície (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Sugere-se que o laser de Er: YAG não pode substituir o tratamento convencional com partículas de óxido de alumínio e a presença de MDP no cimento resinoso não influenciou na resistência de união.
ABSTRACT
Background: During the past decade, parental involvement for the selection of full coronal restorations for the primary anterior teeth of their children has been increased. Two most common anterior aesthetic full coronal restorations, the strip crowns and the preformed zirconia crowns, are available options. Aim: The aim of this study is to compare parental satisfaction with strip crowns and preformed primary anterior zirconia crowns over 1 year in 3–5 years old children. Materials and Methods: Forty maxillary primary incisors were restored by either strip crown or zirconia crown in 24 children. Permuted block randomization method was used for the allocation of participants. Twenty-four parents participated were recalled to fill the questionnaire over 1 year. One parent dropped out at the end of 1 year. Data were analyzed using the t-test and Chi-square test. P < 0.05 considered statistically significant. Results: Parents were satisfied with both types of restorations. Statistically significant relationship was found between overall satisfaction and durability (P = 0.004) with strip crowns and with the color (P = 0.043) in the zirconia crowns. The parents with the lower satisfaction levels with the durability of strip crowns and color of zirconia crowns rated high overall satisfaction. Conclusion: Parental overall satisfaction was higher for preformed primary anterior zirconia crowns than strip crowns. Almost equal number of parents was satisfied with all other parameters except for durability, which was more for zirconia crowns.
ABSTRACT
La caries de la infancia temprana, al igual que otras formas de caries, se caracteriza por ser multifactorial, infecciosa y de rápida evolución. Puede presentarse como lesiones cavitadas o no cavitadas, se diagnostica principalmente en menores de seis años en la superficies de los dientes anterosuperiores, debido a que son los primeros órganos dentales en erupcionar y tienen mayor contacto con el estímulo cariogénico. En casos severos pueden llegar a ocasionar la pérdida de órganos dentales, influyendo en la salud general del paciente y repercutiendo en su autoestima y desarrollo psicosocial. Para devolver las características y funciones perdidas en ausencia de algún órgano dental, se recurre a sustituirlo mediante aparatología, mayormente en forma de un mantenedor de espacio funcional. Las necesidades estéticas individuales de cada caso generan diversas alternativas para adaptarnos a la situación del paciente (AU))
Early childhood caries, like other forms of caries, is characterized by being multifactorial, infectious, and rapidly evolving. It can present as cavitated or uncavitated lesions, it is mainly diagnosed in children under six years of age on the surfaces of the anterior superior teeth, because they are the first dental organs to erupt and have greater contact with the cariogenic stimulus. In severe cases they can cause the loss of dental organs, influencing the general health of the patient and impacting on their self-esteem and psychosocial development. In order to restore the lost features and functions in the absence of any dental organ, it is resorted to by means of appliances, mostly in the form of a functional space maintainer. The individual aesthetic needs of each case generate various alternatives to adapt to the patient's situation (AU)