ABSTRACT
Objectives: To evaluate the inflammatory tissue response and matrix metalloproteinase (MMP)-2 and -9 expression in the pulp-dentin complex in response to RelyX TM Unicem (RU) and Ketac Cem TM Easymix (KC) cements. Methods : Class V cavities were prepared in 56 teeth from six dogs, and indirect pulp capping was performed using RU (n=20), KC (n=20), zinc oxide, and eugenol cement (control, n=16). At 7 and 70 days following indirect pulp capping, the animals were euthanized, and tissues were removed for histological evaluation. The distance from the cavity floor to the odontoblastic layer was measured, and the numbers of inflammatory cells, fibroblasts, and odontoblasts were counted in pulp tissue. MMP-2 and -9 expression levels were immunohistochemically assessed. Statistical analyses were performed for all experiments (significance level=5%). Results : The dentin remnant thickness between the cavity floor and the pulp chamber was similar for all materials, ranging from 469 to 739 µm (p>0.05). At 7 days, KC and RU induced a small inflammatory response in the pulp-dentin complex, similar to the control (p>0.05). At 70 days, RU induced a tissue response characterized by fewer odontoblasts and more mononuclear cells (p<0.05), whereas KC induced a response similar to the control (p>0.05). Lutingagents induced low levels of MMP-2 and MMP-9 expression, similar to the control (p>0.05). Conclusion : KC and RU luting agents are compatible materials for use in deep cavities close to dental pulp tissue, although RU led to a slightly diminished odontoblastic population with a higher percentage of mononuclear cells.
Objetivo : Avaliar a resposta tecidual inflamatória e a expressão de metaloproteinase de matriz (MMP) -2 e -9 no complexo polpa-dentina em resposta aos cimentos RelyX TM Unicem (RU) e Ketac Cem TM Easymix (KC). Métodos : Cavidades classe V foram preparadas em 56 dentes de seis cães, e capeamento pulpar indireto foi realizado com cimento de RU (n = 20), KC (n = 20), óxido de zinco e eugenol (controle, n = 16). Aos 7 e 70 dias após o capeamento pulpar indireto, os animais foram eutanasiados, e os tecidos foram removidos para avaliação histológica. A distância entre o assoalho da cavidade e a camada odontoblástica foi medida, e os números de células inflamatórias, fibroblastos e odontoblastos foram contados no tecido pulpar. Os níveis de expressão de MMP-2 e -9 foram avaliados por imuno-histoquímica. Análises estatísticas foram realizadas para todos os experimentos (nível de significância = 5%). Resultados : A espessura da dentina remanescente entre o assoalho da cavidade e a câmara pulpar foi semelhante para todos os materiais, variando de 469 a 739 µm (p> 0,05). Aos 7 dias, KC e RU induziram uma pequena resposta inflamatória no complexo polpa-dentina, semelhante ao controle (p> 0,05). Aos 70 dias, a RU induziu uma resposta tecidual caracterizada por menos odontoblastos e mais células mononucleares (p <0,05), enquanto o KC induziu uma resposta semelhante ao controle (p> 0,05). Os agentes cimentantes induziram baixos níveis de expressão de MMP-2 e MMP-9, semelhantes ao controle (p> 0,05). Conclusão : Os agentes cimentantes KC e RU são materiais compatíveis para uso em cavidades profundas próximas ao tecido da polpa dentária, embora a UR tenha levado a uma população odontoblástica levemente diminuída, com maior porcentagem de células mononucleares.
Subject(s)
Resin Cements , Matrix Metalloproteinases , Dental Pulp , Dental Pulp CappingABSTRACT
We evaluated the histological dental pulp state in vivo after indirect pulp capping using sildenafil or LG-nitro-L-arginine (L-NAME), incorporated into a new bioadhesive thermoresponsive system (BTS). Male Wistar rats were subjected to an upper and lower first molar class I cavity preparation followed by indirect pulp capping with sildenafil or L-NAME. Calcium hydroxide (CaOH2) was used as a control. The teeth and surrounding bone were properly dissected and processed for Nissl's staining. Pulp state was evaluated considering the morphological aspects of the inflammatory response, type of inflammatory infiltrate, organization of the odontoblast layer, blood vessel condition, and presence of abscesses or necrosis. The results were expressed as average of observations. The most intense inflammatory response was observed 3 days after the cavity preparation. No identified changes were detected in the dental pulp response of the molars treated with L-NAME compared with those treated with CaOH2. A dual effect was observed in the teeth treated with sildenafil. While low sildenafil concentration (0.015% w w-1) promoted effects comparable to CaOH2, at a higher concentration (0.15% w w-1), sildenafil caused a severe inflammatory response and pulp necrosis. This pioneering suggest that NO pathway activity may be a determinant in the process of dental pulp healing.
Avaliou-se o estado histológico da polpa dental in vivo após capeamento pulpar indireto usando sildenafil ou LG-nitro-L-arginine (L-NAME), incorporados num novo sistema bioadesivo termorresponsivo (BTS). Ratos Wistar machos foram sujeitos ao preparo cavitário, classe I nos primeiros molares superiores e inferiores, seguido de capeamento pulpar indireto com sildenafil ou L-NAME incorporados em BTS. Hidróxido de cálcio (CaOH2) foi usado como controle positivo. Os dentes e tecidos adjacentes foram adequadamente dissecados e processados para a coloração de Nissl. O estado da polpa foi avaliado quanto aos aspectos morfológicos e tipo do infiltrado inflamatório, organização da camada de odontoblastos, condições dos vasos sanguíneos e presença de abcesso ou necrose. A reposta inflamatória mais intensa foi observada três dias após o preparo cavitário. Nenhuma alteração foi detectada na polpa dental dos molares tratados com L-NAME comparados com aqueles tratados com CaOH2. Um efeito dual foi observado nos dentes tratados com sildenafil. Enquanto baixas concentrações de sildenafil (0.015% v v-1) promoveram efeitos comparáveis com o CaOH2, altas concentrações (0.15% v v-1) causaram uma severa resposta inflamatória e necrose pulpar. Este estudo pioneiro sugere que a atividade da via do NO pode ser determinante no processo de cicatrização.