ABSTRACT
OBJECTIVE@#To compare the effects of resin base and different retention depth on the fracture resistance of mandibular molars restored with nano-ceramic endocrowns.@*METHODS@#Forty mandibular molars selected and randomly divided into 5 groups: ① The control group which was consisted of intact teeth, ② the non-resin base group, ③ the 2 mm retention depth group, ④ the 3 mm retention depth group, ⑤ the 4 mm retention depth group, respectively. After tooth preparation, in vitro root canal therapy was conducted, which was followed by endocrown design, production and adhesive of groups ②-⑤. All the samples were under load (N) of the universal mechanical testing machine after embedding. The fracture pattern of each sample was observed under stereomicroscope. Then the microstructure of the fracture surface was observed by scanning electron microscopy.@*RESULTS@#The fracture loads of each group were respectively: the control group fracture load was (3 069.34±939.50) N; experimental groups: fracture load of (2 438.04±774.40) N for the group without resin base; fracture load of (3 537.18±763.65) N for the group with 2 mm retention depth. The fracture load of the retention depth 3 mm group was (2 331.55±766.39) N; the fracture load of the retention depth 4 mm group was (2 786.98±709.24) N. There was statistical significance in the effect of resin base and different retention depth on the fracture loads of molars restored with nano-ceramic endocrown (P < 0.05). Repairable fractures in each group were as follows: control group 2/8, non-resin base group 1/8, retention depth of 2 mm group 1/8, retention depth of 3 mm group 2/8, and retention depth of 4 mm group 0/8. The effects of the retention depth and the presence of resin base on the fracture resistance of the resin nano-ceramic endocrowns were statistically significant (P < 0.05). Scanning electron microscopy showed more arrest lines and small twist hackles on the fracture surface of the restorations with resin base (retention depths of 2 mm, 3 mm, and 4 mm), with cracks extending towards the root. In addition to the characteristics above, more transverse cracks parallel to the occlusal surface, pointing outwards from the center of the pulp cavity retention, were also observed on the fracture surface of the non-resin base restorations.@*CONCLUSION@#When molar teeth with nano-ceramic endocrowns are restored, resin base and the retention depth of 2 mm help the teeth to obtain optimal fracture strength.
Subject(s)
Ceramics , Composite Resins , Dental Porcelain , Dental Restoration Failure , Dental Stress Analysis , Materials Testing , MolarABSTRACT
PURPOSE: To evaluate the effects of different surface treatments on the bond strength of novel CAD/CAM restorative materials to resin cement by four point bending test. MATERIALS AND METHODS: The CAD/CAM materials under investigation were e.max CAD, Mark II, Lava Ultimate, and Enamic. A total of 400 bar specimens (4×1.2×12 mm) (n=10) milled from the CAD/CAM blocks underwent various pretreatments (no pretreatment (C), hydrofluoric acid (A), hydrofluoric acid + universal adhesive (Scotchbond) (AS), sandblasting (Sb), and sandblasting + universal adhesive (SbS)). The bars were luted end-to-end on the prepared surfaces with a dual curing adhesive resin cement (Variolink N, Ivoclar Vivadent) on the custom-made stainless steel mold. Ten test specimens for each treatment and material combination were performed with four point bending test method. Data were analyzed using ANOVA and Tukey's test. RESULTS: The surface treatment and type of CAD/CAM restorative material showed a significant effect on the four point bending strength (FPBS) (P < .001). For LDC, AS surface treatment showed the highest FPBS results (100.31 ± 10.7 MPa) and the lowest values were obtained in RNC (23.63 ± 9.0 MPa) for control group. SEM analyses showed that the surface topography of CAD/CAM restorative materials was modified after treatments. CONCLUSION: The surface treatment of sandblasting or HF acid etching in combination with a universal adhesive containing MDP can be suggested for the adhesive cementation of the novel CAD/CAM restorative materials.
Subject(s)
Adhesives , Cementation , Fungi , Hydrofluoric Acid , Methods , Resin Cements , Stainless SteelABSTRACT
PURPOSE: This study was performed in order to assess the effect of the surface treatment methods and the use of bonding agent on the shear bond strength (SBS) between the aged CAD-CAM (computer aided design-computer aided manufacturing) hybrid materials and added composite resin. MATERIALS AND METHODS: LAVA Ultimate (LU) and VITA ENAMIC (VE) specimens were age treated by submerging in a 37℃ water bath filled with artificial saliva (Xerova solution) for 30 days. The surface was ground with #220 SiC paper then the specimens were divided into 9 groups according to the combination of the surface treatment (no treatment, grinding, air abrasion with aluminum oxide, HF acid) and bonding agents (no bonding, Adper Single Bond 2, Single Bond Universal). Each group had 10 specimens. Specimens were repaired (added) using composite resin (Filtek Z250), then all the specimens were stored for 7 days in room temperature distilled water. SBS was measured and the fractured surfaces were observed with a scanning electron microscope (SEM). One-way ANOVA and Scheffe test were used for statistical analysis (α=.05). RESULTS: Mostly groups with bonding agent treatment showed higher SBS than groups without bonding agent. Among the groups without bonding agent the groups with aluminum oxide treatment showed higher SBS. However there was no significant difference between groups except two subgroups within LU group, which revealed a significant increase of SBS when Single Bond Universal was used on the ground LU specimen. CONCLUSION: The use of bonding agent when repairing an aged LAVA Ultimate restoration is recommended.