Article in Korean | WPRIM | ID: wpr-122873

ABSTRACT

STATEMENT OF PROBLEM: When an implant is fixed, a fixture comes into contact with a tissue fluid. Adhesion of a tissue fluid to a surface of implant is various case by case. PURPOSE: The ultimate goal of this work is to analyze a correlation between a surface roughness and wettability of implant specimens. A measurement for wettability is performed considering 4 types of specimen implant with surface treatments different from each other to investigate the change of wettability with the elapse of time. MATERIAL AND METHODS: Firstly, 20 specimens of titanium were prepared. The specimen were made of a commercial Titanium Grade IV with the diameter of 10 mm and the thickness of 1 mm. According to the method of surface treatment, the specimens were classified into 4 groups of 5 specimens per group. Group A: Machined Surface Group B: Anodized surface Group C: RBM (HA blasting) surface Group D: CMP (calcium methaphosphate) coating surface. Surface roughness of specimen was measured using SV-3000S4 (Mituyoto, Japan). The measurement was based on the standard of JIS1994. Sessile drop method was used to measure the wettability, which measures contact angle between implant disc and saline with the time interval of 5, 10, and 15 seconds. SPSS 11.0 was used to analyze the collected data. In order to analyze the difference of wettability and surface roughness according to implant surface treatment method. The statistical significance was tested with the confidence level of 95 percent. Pearson's correlation coefficient was used to evaluate the correlation of surface roughness and wettability. RESULTS: The difference of surface roughness was statistically significant in the order of Group C (1.69 +/- 0.26), Group D (1.58 +/- 0.16), Group B (0.78 +/- 0.14) Group A (0.18 +/- 0.05). The wettability has also a statistically significant difference, which was in the order of group B (17.70 +/- 2.66), Group C (27.86 +/- 4.52), Group D (66.28 +/- 3.70) Group A (70.52 +/- 8.00). There was no difference in wettability with the passage of time. CONCLUSIONS: 1. The surface roughness was high in the order of RBM, CMP, Anodized, Machined group (P < .05). 2. The wettability was high in the order of Anodized, RBM, CMP, Machined group (P < .05). 3. There was no statistical significance in the correlation of surface roughness and wettability.


Subject(s)
Surface Properties , Titanium , Wettability
2.
Article in Korean | WPRIM | ID: wpr-84193

ABSTRACT

Purpose: This study aims to get the fundamental data which is necessary to the development direction of implant surface treatment hereafter, based on the understanding the surface structure and properties of titanium which is suitable for the absorption of initial tissue fluid by researching effects of additional surface treatments for sandblasted with large grit and acid-etched(SLA) titanium on surface micro-roughness, static wettability, fibronectin adsorption. Materials and Method: In the Control groups, the commercial pure titanium disks which is 10mm in diameter and 2mm in thickness were treated with HCI after sandblasting with 50micrometer Al2O3. The experiment groups were made an experiment each by being treated with 1) 22.5% nitric acid according to SLA+ASTM F86 protocol, 2) SLA+30% peroxide, 3) SLA+NaOH, 4) SLA+Oxalic acid, and 5) SLA+600degree C heating. In each group, the value of Ra and RMS which are the gauges of surface roughness was measured, surface wettability was measured by analyzing with Sessile drop method, and fibronectin adsorption was measured with immunological assay. The significance of each group was verified by (SPSS, ver.10.0 SPSS Inc.) Kruskal-Wallis Test.(alpha=0.05) And the correlation significance between Surface micro-roughness and surface wettability, surface roughness and fibronectin adsorption, and surface wettability and fibronectin adsorption was tested by Spearman's correlation analysis. Result: All measure groups showed the significant differences in surface micro-roughness, surface wettability, and fibronectin adsorption.(p0.05) Conclusion: Surface micro-roughness and surface wettability rarely affected the absorption of initial tissue fluid on the surface of titanium.


Subject(s)
Absorption , Adsorption , Fibronectins , Heating , Hot Temperature , Nitric Acid , Titanium , Wettability