Histological evaluation of bone response to pediatric endodontic pastes: an experimental study in guinea pig

This study aimed to evaluate by the intra-osseous implant technique the most commonly used materials for pulp therapy in pediatric dentistry: calcium hydroxide (CH), Guedes Pinto paste and CTZ paste, according to FDI (1980) and ANSI/ADA (1982) recommendations. Thirty guinea pigs, 10 for each material, divided into experimental periods of 4 and 12 weeks received one implant on each side of the lower jaw symphysis. The external lateral tube wall served as control for the technique. At the end of the observation periods, the animals were euthanized and specimens were prepared for routine histological examination. It was observed that CH and CTZ paste induced severe inflammation, a large amount of necrotic tissue, lymphocytes, foreign body cells and bone resorption, while Guedes Pinto Paste induced little or no inflammation in the 4-week observation period. After 12 weeks, the reactions to CH and Guedes Pinto paste were also absent/mild, presenting a general pattern of replacement by recently formed bone tissue while a moderate to severe inflammatory response was observed with CTZ paste. Guedes Pinto paste presented acceptable biocompatibility levels in both analyzed periods; CH only showed acceptable biocompatibility in the 12-week period while CTZ paste showed no biocompatibility in both periods. Among the tested materials, only Guedes Pinto paste presented an acceptable biocompatibility.

A pesquisa teve como objetivo avaliar a biocompatibilidade através da técnica de implantes intra-ósseos dos materiais utilizados em odontopediatria para tratamento pulpar: hidróxido de cálcio, pastas Guedes Pinto e CTZ, de acordo com as recomendações da FDI (1980) e ANSI/ADA(1982). Trinta guinea pigs, dez para cada material, divididos em períodos experimentais de 4 e 12 semanas receberam um implante em cada lado da sínfise mandibular. A parede lateral externa do copo serviu como controle para a técnica. No final dos períodos experimentais, os animais foram sacrificados e os espécimes preparados para o exame histológico de rotina. Observou-se que o hidróxido de cálcio e a pasta CTZ mostraram reação inflamatória severa, grande quantidade de tecido necrosado, linfócitos, células de corpo estranho e reabsorção óssea; enquanto a pasta Guedes Pinto induziu pouca ou nenhuma inflamação no período de 4 semanas. Após 12 semanas as reações para o hidróxido de cálcio e pasta Guedes Pinto foram ausentes/suaves apresentando um padrão geral de substituição por tecido ósseo neoformado, enquanto uma resposta inflamatória de moderada a severa foi observada para a pasta CTZ. A pasta Guedes Pinto apresentou níveis aceitáveis de biocompatibilidade nos dois períodos analisados; hidróxido de cálcio apresentou biocompatibilidade aceitável somente no período de 12 semanas e a pasta CTZ não mostrou biocompatibilidade em ambos os períodos. Entre estes, apenas a pasta Guedes Pinto apresentou níveis de biocompatibilidade nos dois períodos analisados.

Antimicrobial effect and pH of chlorhexidine gel and calcium hydroxide alone and associated with other materials

The purposes of this study were to evaluate the effectiveness of 2 percent chlorhexidine (CHX) gluconate gel, calcium hydroxide [Ca(OH)2] and their combination with iodoform and zinc oxide powder as intracanal medications against select microorganisms, and to measure the pH changes caused by these medications. Antimicrobial activity was determined by the agar diffusion method. The zones of growth inhibition were measured and the results were analyzed statistically by Kruskal-Wallis test (p<0.05). The pH of the pastes was measured right after preparation, after 24 h and 1 week later. The largest mean zones of microbial inhibition were produced by 2 percent CHX gel, followed by Ca(OH)2 + 2 percent CHX gel + iodoform, Ca(OH)2 + 2 percent CHX gel, Ca(OH)2 + 2 percent CHX gel + zinc oxide, and Ca(OH)2 + water. The mean pH of all medications stayed above 12.0 during the whole experiment, except for CHX gel (pH=7.0). The results of this study showed that all medications had antimicrobial activity, but the most effective against the tested microorganisms were 2 percent CHX gel, followed by its combination with Ca(OH)2 and iodoform.

O objetivo do estudo foi avaliar, in vitro, a efetividade antimicrobiana da clorexidina gel 2 por cento (CHX) e hidróxido de cálcio, isoladamente e associados com iodofórmio e pó de óxido de zinco como medicamentos intracanais frente a microrganismos e medidos pHs das diferentes medicações. A atividade antimicrobiana foi determinada pelo método de difusão em ágar. As áreas de inibição de crescimento foram medidas e os resultados estatisticamente analisados utilizando-se o teste de Kruskal-Wallis (p<0,05). O pH das pastas foi mensurado após a manipulação, após 24 h e após uma semana. Os resultados mostraram que a maior zona de inibição foi da CHX gel 2 por cento, seguida pelo Ca(OH)2 + 2 por cento CHX gel, Ca(OH)2 + 2 por cento CHX gel + iodofórmio, Ca(OH)2 + 2 por cento CHX gel +óxido de zinco, Ca(OH)2 + água. A média de pH de todos os medicamentos intracanais foi de 12 durante todo o experimento, exceto com CHX gel 2 por cento (pH=7,0). Estes resultados permitiram concluir que todos os medicamentos tiveram atividade antimicrobiana, no entanto, a maior foi da CHX gel 2 por cento, seguido da associação com o Ca(OH)2. e iodofórmio.

Antimicrobial analysis of different root canal filling pastes used in pediatric dentistry by two experimental methods

The objective of this study was to compare, by two experimental methods, the antimicrobial efficacy of different root canal fillingpastes used in pediatric dentistry. The tested materials were: Guedes-Pinto paste (GPP), zinc oxide-eugenol paste (OZEP), calcium hydroxide paste (CHP), chloramphenicol + tetracycline + zinc oxide and eugenol paste (CTZP) and Vitapex®. Fiven microbial strains (S. aureus, E. faecalis, P. aeruginosa, B. subtilis and C. albicans) obtained from the American Type Culture Collection were inoculated in Brain Heart Infusion (BHI) and incubated at 37°C for 24 h. For the direct exposure test (DET), 72 paper points were contaminated with the standard microbial suspensions and exposed to the root canal filling pastes for 1, 24, 48 and 72 h. The points were immersed in Letheen Broth (LB), followed by incubation at 37°C for 48 h. An inoculum of 0.1 mL obtained from LB was then transferred to 7 mL of BHI, under identical incubations conditions and the microbial growth was evaluated. The pastes showed activity between 1 and 24 h, depending on the material. For the agar diffusion test (ADT), 30 Petri plates with 20 mL of BHI agar were inoculated with 0.1 mL of the microbial suspension, using sterile swabs that were spread on the medium. Three cavities were made in each agar plate (total = 90) and completely filled with one of the filling root canal pastes. The plates were pre-incubated for 1 h at room temperature and then incubated at 37°C for 24 to 48 h. The inhibition zone around each well was recorded in mm. The complete antimicrobial effect in the direct exposure test was observed after 24 h on all microbial indicators. All root canal filling materials induced the formation of inhibition zones, except for Vitapex® (range, 6.0-39.0 mm).

O objetivo do presente estudo foi comparar o efeito antimicrobiano de diferentes pastas obturadoras do canal radicular usadas na Odontopediatria, por dois métodos experimentais. Os materiais testados foram: pasta Guedes Pinto, pasta de óxido de zinco e eugenol, pasta de hidróxido de cálcio, pasta CTZ e Vitapex®, sobre cinco microrganismos (S. aureus, E. faecalis, P. aeruginosa, B. subtilis e C. albicans) obtidos do American Type Culture Collection. As cepas foram inoculadas no Brain Heart Infusion (BHI) e incubadas a 37°C por 24 h. Para o teste de contato direto, 72 pontas de papel foram contaminadas com suspensões padrão dos microrganismos e expostas às pastas obturadoras por 1, 24, 48 e 72 h. As pontas foram imersas em Letheen Broth (LB), seguido de incubação a 37°C por 48 h. Um inóculo de 0,1 mL obtido do LB foi transferido para 7 mL de BHI, sobre condições idênticas de incubação e o crescimento microbiano foi avaliado. As pastas mostraram ação entre 1 e 24 h, dependendo da pasta testada. Para o teste de difusão em ágar, 30 placas de Petri com 20 mL de agar BHI foi inoculada com 0,1 mL da suspensão microbiana, utilizando-se de swab esterilizado, semeado de modo confluente no meio. Três cavidades foram feitas em cada placa de ágar (total = 90) e completamente preenchidas com uma das pastas obturadoras. As placas foram pré-incubadas por 1 h em temperatura ambiente e então incubadas a 37°C por 48 h. As zonas de inibição em torno das cavidades foram mensuradas. O efeito antimicrobiano completo obtido pelas pastas analisadas, por meio do teste por contato direto, foi observado após 24 h em todos os microrganismos. No teste por difusão em ágar, todos os materiais induziram a formação de zonas de inibição, exceto o Vitapex® (variando de 6,0 - 39,0 mm).

Evaluation of antimicrobial efficacy of various root canal filling materials for primary teeth.

Four materials viz. zinc oxide-eugenol, iodoform paste, Kri paste, Maisto's paste and Vitapex (Calcium hydroxide + iodoform) were tested for their antibacterial effect against the aerobic and anerobic bacteria, viz. Staphylococcus aureus, Streptococcus viridans, Streptococcus faecalis, Bacteroides melaninogenicus and mixed bacterial culture; obtained from infected non-vital deciduous anterior teeth. The antimicrobial sensitivity was checked on BHI-agar plates using well method. The results showed that all the 4 materials were distinctly different from each other in their antimicrobial activity. Maisto's paste was invariably the superior most in its antibacterial efficacy (in comparison to all the 5 micro-organism strains). Iodoformized zincoxide eugenol appeared to be the second best followed by Kri paste. Vitapex showed the least antibacterial activity.