RESUMEN
Abstract To investigate the effect of the dimethyl sulfoxide combined with cross-linking agents on microtensile bond strength, silver nitrate penetration and in situ degree of conversion analysis of adhesives to the erosive dentin treatment with Cola-based soft drink. One hundred and sixty-six molars were assigned to 20 groups: (1) Treatment: Sound dentin; Erosive dentin; Erosive dentin treated with primer of dimethyl sulfoxide; Erosive dentin treated with DMSO primer containing proanthocyanidin and rivoflavin; (2) Adhesive systems: iBond Universal and Scotchbond Universal; and (3) adhesive strategy: etch-and-rinse or self-etch strategy. After restoration, specimens were sectioned into sticks to be tested. The data from microtensile bond strength (MPa), silver nitrate penetration (%) and in situ degree of conversion (%) were analyzed by (three- and two-factor ANOVA; Tukey's test α=5%). The application of dimethyl sulfoxide combined of not with cross-linkers improved all properties evaluated when compared to only erosive dentin treatment with Cola-based soft drink. However, only when dimethyl sulfoxide was combined to cross-linkers, the values of the microtensile bond strength, silver nitrate penetration and in situ degree of conversion in erosive dentin treatment with Cola-based soft drink was similar to sound dentin, for both adhesives and adhesive strategies. The application of dimethyl sulfoxide combined with the collagen cross-linking agent contributed to increasing the bond strength and degree of conversion in erosive lesion dentin, at the same time that significantly reduction of nanoleakage in this substrate.
Resumo Este estudo investigou o efeito do dimetil sulfóxido combinado a agentes de reticulação de colágeno na resistência de união à microtração, infiltração de nitrato de prata e análise do grau de conversão por Micro-Raman de sistemas adesivos universais para a dentina erosionada por refrigerante a base de Cola. Cento e sessenta molares foram divididos em 20 grupos: (1) Tratamento: Dentina sadia; Dentina erosionada; Dentina erosionada tratada com primer de dimetil sulfóxido; Dentina erosionada tratada com primer contendo 6,5% de proantocianidina e; Dentina erosionada tratada com primer contendo 0,1% de rivoflavina; (2) Sistemas adesivos: iBond Universal e Scotchbond Universal; e (3) estratégia adesiva: estratégia condicionamento e lavagem ou autocondicionate. Após a restauração, os espécimes foram seccionados em palitos e testados. Os dados dos três testes foram analisados estatisticamente (ANOVA de 2 e 3 fatores e teste de Tukey; α = 5%). A aplicação de dimetil sulfóxido combinado ou não agentes de reticulação de colágeno melhorou todas as propriedades avaliadas quando comparado a dentina erosionada. Entretanto, apenas quando o dimetil sulfóxido foi combinado com agentes de reticulação de colágeno, os valores de adesão a dentina, infiltração de nitrato de prata e grau de conversão em dentina erosionada foi semelhante a dentina sadia, para os dois adesivos e estratégias adesivas. A aplicação de dimetil sulfóxido combinado com agentes de reticulação de colágeno contribuiu para aumentar a resistência de união e o grau de conversão dentro da camada híbrida na dentina erodida, ao mesmo tempo que reduziu significativamente a nanoinfiltração neste substrato.
RESUMEN
ABSTRACT Objective: To compare the effectiveness of the pretreatment with sandblasting and deproteinization with NaOCl on bond strength (SBS), in situ conversion degree (CD) of brackets in fluorotic enamel, and enamel etching pattern. Methods: A total of 90 non-carious maxillary premolars were used. The teeth were then assigned to six experimental groups according to: enamel surface (sound and fluorotic enamel); surface treatment (Regular etch with 37% phosphoric acid [RE]; 5.2% sodium hypochlorite + phosphoric acid [NaOCl + RE]; sandblasting + phosphoric acid [sandblasting + RE]). After storage in distilled water (37°C/24h), the specimens were tested at 1 mm/min until failure (SBS). Enamel-resin cement interfaces were evaluated for CD using micro-Raman spectroscopy. The enamel-etching pattern was evaluated under a scanning electron microscope. Data from SBS and in situ CD values were analyzed using ANOVA two-away and Tukey test (α=0.05). The enamel etching pattern was evaluated only qualitatively. Results: For sound enamel, RE showed the highest SBS values, when compared to NaOCl + RE and Sandblasting + RE groups (p< 0.01). Regarding CD, only NaOCl + RE significantly compromised the mean DC, in comparison with other groups (p= 0.002). For fluorotic enamel, the Sandblasting + RE group significantly increased the mean SBS values, in comparison with RE group (p= 0.01) and no significant change was observed for CD (p> 0.52). Conclusions: The application of NaOCl or sandblasting associated to phosphoric acid improved the SBS of the brackets in fluorotic enamel without compromising the CD of the resin cement, with improving of enamel interprismatic conditioning.
RESUMO Objetivo: Comparar a efetividade do pré-tratamento com jateamento e desproteinização com NaOCl na resistência de união (SBS), grau de conversão in situ (GC) dos braquetes metálicos ao esmalte fluorótico e o padrão de condicionamento do esmalte. Métodos: Foi utilizado um total de 90 pré-molares superiores livres de cárie. Os dentes foram divididos em seis grupos experimentais, de acordo com: superfície do esmalte (Esmalte Sadio e Fluorótico); tratamento de superfície (Condicionamento com ácido fosfórico a 37% [ER]; Hipoclorito de sódio a 5,2% + ácido fosfórico [NaOCl + ER]; e jateamento + ácido fosfórico [Jateamento + ER]). Após armazenamento em água destilada (37oC/24 h), os espécimes foram testados a 1 mm/min até a falha (SBS). As interfaces esmalte-cimento foram avaliadas para GC usando espectroscopia micro-Raman. O padrão do condicionamento do esmalte foi avaliado sob microscopia eletrônica de varredura. Os dados da SBS e GC foram analisados utilizando ANOVA dois fatores e teste de Tukey (α= 0,05). O padrão de condicionamento do esmalte foi avaliado apenas qualitativamente. Resultados: Para o esmalte sadio, o ER apresentou os maiores valores de SBS, quando comparado aos grupos NaOCl + ER e Jateamento + ER (p< 0,01). Em relação ao GC, apenas a média do grupo NaOCl + ER foi comprometida significativamente em comparação aos outros grupos (p= 0,002). Para o esmalte fluorótico, Jateamento + ER aumentou significativamente a média dos valores de SBS, em comparação com o grupo ER (p= 0,01) e nenhuma mudança significativa foi observada no GC (p> 0,52). Conclusões: A aplicação de NaOCl ou jateamento associado ao ácido fosfórico melhorou a SBS dos braquetes no esmalte fluorótico sem comprometer o GC do cimento resinoso, com a melhoria do condicionamento interprismático do esmalte.