Braz. oral res. (Online) ; 35: e012, 2021. tab, graf
Artículo en Inglés | LILACS, BBO | ID: biblio-1132751

RESUMEN

Abstract The purpose of this study was to analyze the effect of the application of different concentrations of EDTA on the adhesion of fiber posts to root dentin using self-adhesive resin cements. After endodontic treatment, 78 single roots were randomly divided into six groups (n = 13) according to the combination of the following factors: surface dentin treatment - control (distilled water), 17% EDTA and 24% EDTA; and self-adhesive resin cement - RelyX U200 (RX); and Multilink Speed (ML). After fiber post cementation, six slices were obtained for each root. Ten roots of each group were used for bond strength (BS) and three for microhardness (MH) evaluations. Data obtained from BS and MH tests for each resin cement were subjected to two-way ANOVA (surface treatment vs. root region) and to a post-hoc Tukey's test (α = 0.05). The lowest BS value was observed in the 24% EDTA group for RX cement, whereas the highest values for ML cement were observed for the control group in the middle and apical regions. In the MH test, the lowest value for RX was observed for 24% EDTA in the cervical region, whereas and the highest value for the ML cement was observed in the control group. Regarding both self-adhesive resin cements tested, the application of 24% EDTA was not able to improve the adhesion of fiber posts to root canal.


Asunto(s)
Cementos de Resina , Ensayo de Materiales , Técnica de Perno Muñón , Ácido Edético/farmacología , Cavidad Pulpar , Dentina , Vidrio
2.
Braz. j. oral sci ; 19: e206155, jan.-dez. 2020. ilus
Artículo en Inglés | BBO, LILACS | ID: biblio-1116428

RESUMEN

Aim: The roughness and micromorphology of various surface treatments in aged metal-free crowns and the bond strength of these crowns repaired with composite resin (CR) was evaluated in vitro. Methods: A CR core build-up was confectioned in 60 premolars and prepared for metal-free crowns. Prepared teeth were molded with the addition of silicone, and the laboratory ceromer/fiber-reinforced crowns (SR Adoro/Fibrex Lab) were fabricated. Subsequently, the crowns were cemented and artificially aged in a mechanical fatigue device (1.2 X 106 cycles), then divided into 4 groups (n = 15) according to the surface treatment: 1) phosphoric acid etching (PA); 2) PA + silane application; 3) roughening with a diamond bur + PA; and 4) sandblasting with Al2O3 + PA. After the treatments, the crowns (n = 2) were qualitatively analyzed by scanning electron microscope (SEM) and surface roughness (n = 5) was analyzed before and after the surface treatment (Ra parameter). The remaining crowns (n = 8) received standard repair with an adhesive system (Tetric N-Bond) and a nanohybrid CR (Tetric N-Ceram), and the microshear bond strength (SBS) test was performed (0.5 mm/min). Roughness and SBS data were analyzed by one- and two-way ANOVA, respectively, as well as Tukey's post-test (α = 0.05). Results: Sandblasting with Al2O3 + PA resulted in the highest final roughness and SBS values. The lowest results were observed in the PA group, whereas the silane and diamond bur groups showed intermediate values. Conclusion: It may be concluded that indirect ceromer crowns sandblasted with aluminum oxide prior to PA etching promote increased roughness surface and bond strength values


Asunto(s)
Propiedades de Superficie , Cerámica , Resinas Compuestas , Resistencia al Corte , Tomografía con Microscopio Electrónico
3.
Braz. oral res. (Online) ; 32: e13, 2018. tab
Artículo en Inglés | LILACS | ID: biblio-889468

RESUMEN

Abstract The aim of this study was to compare in vitro the bond strength (BS) between fiberglass posts and flared root canals reinforced with different materials. The roots of 48 premolars were endodontically treated. After one week, the root canals were prepared to simulate an oversized root canal, except for the positive control group (PCG), which was cemented with a prefabricated fiber post (PFP) compatible with the root canal size, simulating an ideal adaptation. The other samples (n=8/group) were used to test alternative restorative techniques for filling root canals: negative control group (NCG [PFP with a smaller diameter than of the root canal]), composite resin group - CRG, bulkfill group - BFG, self-adhesive cement group - SAG, and glass ionomer group - GIG. The posts were cemented and after 1 week, each root was sectioned transversely into six 1-mm thick discs and the push-out test was done to evaluate the BS. Data were analyzed by two-way repeated measures ANOVA and Tukey's tests (α=0.05). The highest BS value was observed for PCG. The NCG and the GIG groups showed the lowest BS values. Root reinforcement with conventional and bulk-fill composite resins showed the highest BS values; however, the bulk-fill resin was the only treatment able to maintain high BS values in all regions of the root canal. The self-adhesive cement showed intermediate results between CRG and GIG. Root reinforcement with bulk-fill composite resin is an effective option for flared root canals before cementation of a prefabricated fiber post.


Asunto(s)
Humanos , Recubrimiento Dental Adhesivo/métodos , Materiales Dentales/química , Cavidad Pulpar/efectos de los fármacos , Vidrio/química , Técnica de Perno Muñón , Preparación del Conducto Radicular/métodos , Análisis de Varianza , Cavidad Pulpar/anatomía & histología , Fracaso de la Restauración Dental , Ensayo de Materiales , Valores de Referencia , Reproducibilidad de los Resultados , Factores de Tiempo