Effect of laser-assisted retrograde cavity preparation on push-out-bond-strength of mineral trioxide aggregate and calcium-enriched-mixture-cement / Efeito de preparo cavitário retrógrado assistido por laser na força de união de cimento de agregado trióxido mineral e cimento enriquecido com cálcio

Objective: This study aimed to determine the push-out-bond-strength(PBS) of mineral trioxide aggregate (BIOMTA+) and calcium-enriched-mixture-cement (CEM) in retrograde cavities prepared using Er: YAG laser and stainless-steel bur. Material and Methods: The root canals of 60 extracted single-rooted human teeth were prepared, filled and their apical portion of 3-mm were resected using a diamond bur and randomly divided into four groups according to technique of retrograde preparation and filling material as follows(n=15): Group1: bur/ BIOMTA+ ,Group2: bur/ CEM, Group3: Er:YAG laser/ BIOMTA+, Group4: Er:YAG laser/ CEM. PBS test were performed to specimens and failure modes were evaluated. The data were statistically analyzed with ANOVA, Post-Hoc Tukey and t tests (p< 0.05). Results: CEM was exhibited higher than bond strength compared to BIOMTA+ in retrograde cavity prepared using laser (p= 0.021) and BIOMTA+ in retrograde cavity prepared using bur was exhibited higher than bond strength compared to in retrograde cavities prepared using laser (p= 0.024). Failure modes were dominantly cohesive in all groups tested and one representative specimen each failure mode was examined in SEM and the general characteristics of the failure modes were confirmed. Conclusion: With in the limitations of the present study, when used CEM, Er: YAG laser-assisted retrograde cavity preparation positively affected the bond strength values compared to BIO MTA+. Considering its optimal adhesion, the calcium-enriched-mixture-cement (CEM) might be a good option as a filling material in retrograde cavities in clinical use. (AU)

Objetivo: O objetivo deste estudo foi determinar a força de união (PBS) de cimento de agregado trióxido mineral (BIO MTA+) e cimento enriquecido com cálcio (CEM) em preparos cavitários retrógrados realizados com: Laser Er-YAG e brocas de aço inoxidável. Material e Métodos: Canais radiculares de 60 dentes unirradiculares extraídos foram preparados, preenchidos e 3 mm de suas porções apicais foram ressecadas usando uma broca diamantada e divididos randomicamente em quatro grupos de acordo com a técnica de preparação retrógrada e o material de preenchimento (n=15): Grupo 1: Broca/BIO MTA+, Grupo 2: Broca/CEM, Grupo 3: Laser Er-YAG/BIO MTA+, Grupo 4: Laser Er-YAG/CEM. O teste de PBS foi realizado para as amostras e os modelos de falha foram avaliados. Os dados foram analisados estatisticamente pelos testes de ANOVA, Post-Hoc Tukey e testes t (p< 0.05). Resultados: CEM apresentou maior força de união que BIO MTA+ em cavidades retrógradas preparadas com laser (p= 0.021) e BIO MTA+ em cavidades retrógradas preparadas com brocas apresentou maior força de união quando comparado à cavidades retrógradas preparadas com laser (p= 0.024). Os modelos de falha foram predominantemente coesos em todos os grupos testados e um espécime representativo de cada modelo de falha foi examinado em MEV e as características gerais dos modelos de falha foram confirmadas. Conclusão: Com as limitações do presente estudo, quando usou-se CEM, o preparo de cavidades retrógradas através de Laser Er-YAG afetou positivamente os valores da força de união quando comparados com BIO MTA+. Considerando sua ótima adesão, o cimento enriquecido com cálcio (CEM) pode ser uma boa opção como um material de preenchimento em cavidades retrógradas no uso clínico.

Evaluation of microleakage and the degree of conversion of three composite resins polymerized at different power densities / Avaliação da microinfiltração e do grau de conversão de três resinas compostas polimerizadas em diferentes densidades de potência

Objectives: This study aims to evaluate the degree of conversion (DC) and microlekage scores of three different composite resins polymerized with a LED curing device in standard and extra-power mode. Material and Methods: One bulk-fill (Tetric EvoCeram Bulk-Fill ­ TECBF) and two conventional composite materials (Clearfil Majesty Posterior ­ CMP and Tetric EvoCeram ­ TEC) were evaluated. A total of 30 specimens were prepared for six groups (N = 5). These groups were polymerized with a LED curing device as follows: TECBF-6: 3200mW/cm2 for six seconds, TECBF-20: 1000mW/cm2 for 20 seconds, CMP-6: 3200mW/cm2 for six seconds, CMP-20: 1000mW/cm2 for 20 seconds, TEC-6: 3200mW/cm2 for six seconds, TEC - 20: 1000 mW/cm2 for 20 seconds. After 24 hours of water storage, DC was measured by Raman spectroscopy. Microleakage scores of the six groups were bonded to various adhesive systems (Clearfil SE Bond or Adhese Bond Universal) were also evaluated at Class II box cavities (N = 10). Results: While the highest DC was found at the top (TECBF-20= 79.92% and TECBF-6= 79.02%) and bottom surfaces (TECBF-20 = 68.94% and TECBF-6= 71.04%) for TECBF groups, TEC groups (TEC-20top = 59.06%, TEC-6top=49.66%, TEC-20bottom = 43.72% and TEC-6bottom= 40.68%) showed the lowest DC for the both surfaces (p < 0.05). Polymerization of materials in standard or extra-power mode was similar to DC (p > 0.05). Microleakage scores were found to be similar (p > 0.05). Conclusion: According to the results of the study, different power densities of LED curing light did not affect the DC of composite resins and microleakage values of restorations at small Class II cavities (AU)

Objetivo: este estudo tem como objetivo avaliar os graus de conversão (DC) e microinfiltração de três diferentes resinas compostas polimerizáveis com um dispositivo de luz por LED nos modos padrão e no modo de alta-potência. Material e métodos: uma resina bulk-fill (Tetric EvoCeram Bulk-Fill - TECBF) e dois materiais resinosos convencionais (Clearfil Majesty Posterior - CMP e Tetric EvoCeram - TEC) foram avaliados. Um total de 30 espécimes foram preparados e divididos em seis grupos (N = 5). Esses grupos foram polimerizados com um dispositivo de luz de LED da seguinte forma: TECBF-6: 3200mW / cm2 por seis segundos, TECBF-20: 1000mW / cm2 por 20 segundos, CMP-6: 3200mW / cm2 por seis segundos, CMP20: 1000mW / cm2 por 20 segundos, TEC-6: 3200mW / cm2 por seis segundos, TEC - 20: 1000 mW / cm2 por 20 segundos. Após 24 horas de armazenamento em água, a DC foi medida por espectroscopia Raman. Os escores de microinfiltração dos seis grupos dos vários sistemas adesivos (Clearfil SE Bond ou Adhese Bond Universal) também foram avaliados nas cavidades Classe II (N = 10). Resultados: embora a maior CD tenha sido encontrada nas partes superior (TECBF-20 = 79,92% e TECBF-6 = 79,02%) e inferiores (TECBF-20 = 68,94% e TECBF-6 = 71,04%) para grupos TECBF, os grupos TEC (TEC-20top = 59,06%, TEC-6top = 49,66%, TEC-20bottom = 43,72% e TEC-6bottom = 40,68%) apresentaram as menores CD para as ambas as partes (p < 0,05). A polimerização de materiais no modo padrão ou alta-potência foi semelhante à DC (p > 0,05). Os escores de microinfiltração foram semelhantes (p > 0,05). Conclusão: de acordo com os resultados do estudo, diferentes densidades de potência da luz de LED não afetaram as CD das resinas compostas e os valores de microinfiltração das restaurações em pequenas cavidades da Classe II. (AU)

Granulomatous hepatitis after intravesical BCG treatment for bladder cancer.

Intravesical bacillus Calmette-Guerin (BCG) is used in patients with urinary bladder carcinoma. Although it is generally well tolerated, granulomatous hepatitis is a rare but serious complication. We report a 42-year-old man and a 56-year-old man who developed granulomatous hepatitis following intravesical BCG. One of them was treated successfully with antitubercular therapy; the other died because of BCG sepsis and multi-organ failure.