Influence of preheating and post-curing on a novel fiber-reinforced composite post material

Abstract The aim of this study was to investigate the influence of preheating and post-curing methods on diametral tensile strength (DTS), flexural strength (FS), knoop microhardness (KHN), and degree of conversion (DC) of an experimental fiber-reinforced composite (FRC). Specimens (30 wt% of 3-mm-short E-glass fiber, 22.5 wt% of methacrylated-based resin and 47.5 wt% of filler particles) were subjected to: P - photocuring at 1500 mW/cm2 for 40 s (control); P/M - photocuring and microwave post-curing (540W/5 minutes); P/A - photocuring and autoclave post-curing (120°C/15 minutes); PH-P - preheating (60°C) and photocuring; PH-P/M - preheating, photocuring and microwave post-curing; and PH-P/A - preheating, photocuring and autoclave post-curing. Specimens for DTS (Ø 3 x 6 mm) and FS (25 x 2 x 2 mm) were tested at Instron 5965. KHN employed a 50g load for 30s. DC was measured using FTIR spectroscopy. Statistical analysis employed: factorial analysis, normality test, one-way ANOVA and Tukey's HSD test, independent T-test and the Dunnett test. Interaction between factors was not significant (P>0.05). Preheating promoted significantly higher values of FS and KHN (p = 0.0001). Post-curing promoted significantly higher values for KHN (p = 0.0001). For DTS (p = 0.066) and DC (p= 0.724) no statistical difference was found between groups. SEM images showed that preheating promoted better interaction between glass fibers and resin matrix. Preheating increased FS, KHN and DTS, and post-curing increased KHN. DC was not affected by both methods. Preheating and post-curing methods can be used to improve some mechanical properties of FRCs' but degree of conversion remains unaffected.

Minimally invasive approach in esthetic dentistry: composite resin versus ceramics veneers / Abordagem minimamente invasiva em odontologia estética: resina composta versus facetas cerâmicas

Unsatisfactory anatomical shape of anterior tooth promotes disharmony in the smile esthetics. The conservative dental esthetic reestablishment treatments has been improved and evaluated with the development of adhesive materials. The adhesive dentistry allowed minimally invasive preparation through direct treatments with composite resin and indirect ceramic laminates veneers. These two treatments methods present advantages and disadvantages. The aim of this manuscript is to describe two clinical reports and compare alternatives to rehabilitate the smile esthetic appearance by direct and indirect minimally invasive treatments. In the first case, a 24-years-old patient, female, complained of unsatisfactory anterior maxillary size and incisal wear. After the functional and esthetic planning, nanoparticle composite resin by free hand technique was indicated to rehabilitation. In the second case, a 24-years-old patient, male, reported dissatisfied with his anterior central incisive shape. On clinical examination, maxillary anterior conoid teeth were verified. Based on this evaluation, a conservative treatment using minimally invasive ceramic veneers in maxillary central and lateral incisor and ceramic fragments on canine was planed to the smile rehabilitation. It can be concluded that conservative treatment using direct composite resin restorations and minimum thickness ceramic veneers laminate, even with their specific limitations and advantages, provide satisfactory esthetic and functional treatment results, preserving the dental structure.

Dentes com formato anatômico insatisfatório podem causar desarmonia na estética do sorriso. Os tratamentos para restabelecer a estética do sorriso vêm evoluindo concomitantemente com o desenvolvimento dos materiais dentários. A odontologia estética permite um preparo minimamente invasivo através de resinas compostas e laminados cerâmicos. Estes dois métodos de tratamento apresentam algumas vantagens e desvantagens. O objetivo deste artigo é descrever dois relatos de casos clínicos e comparar alternativas para a reabilitação da estética do sorriso pelos tratamentos minimamente invasivos diretos e indiretos. No primeiro caso, paciente de 24 anos do gênero feminino, estava descontente com o tamanho e com o desgaste incisal dos dentes maxilares anteriores. Após o planejamento funcional e estético foi indicado restauração direta com uma resina nanopartículada pela técnica da mão livre. No segundo caso, paciente de 24 anos do gênero masculino relatou insatisfação com a forma dos incisivos centrais superiores. No exame clínico foi observado incisivos conoídes. Baseado no exame clínico foi planejado um tratamento conservador com laminados cerâmicos nos incisivos centrais e laterais, e fragmentos cerâmicos nos caninos. Pode-se concluir que os tratamentos conservadores utilizando resina composta e laminados cerâmicos, mesmo com suas limitações, promove uma estética satisfatória e resultados funcionais preservando a estrutura dental.

Reabilitação funcional e estética do sorriso û relato de caso / Functional and aesthetic rehabilitation of smile û case report

A constante busca por tratamentos odontológicos estéticos e por um sorriso bonito e harmônico é o que a maioria das pessoas almeja, o que contribui para a realização de procedimentos restauradores que possibilitem mimetização do natural para atingir as expectativas e necessidades dos pacientes. A presença de diastemas pode resultar em problemas funcionais e estéticos. Sendo assim, o presente caso clínico relata reabilitação de um extenso diastema entre os incisivos centrais superiores, após intervenção cirúrgica para remoção do freio labial e clareamento dental. Foram realizadas restaurações diretas minimamente invasivas nos dentes anteriores, com resina composta nanoparticulada. O acabamento e polimento foram realizados de forma a evidenciar anatomia e textura de superfície dos dentes. Em conclusão, o tratamento realizado utilizou materiais com comportamento biomecânico favorável, estabelecendo função, harmonia do sorriso e resultado estético satisfatório...

The constant search for dental aesthetic treatments in order to achieve a nice and harmonic smile has contributed to the development of restorative procedures enabling mimicry of natural teeth to meet expectations and needs of patients. The presence of diastemas can result in functional and aesthetic problems. Therefore, the present clinical case reports rehabilitation of a large diastema between the maxillary central incisors, after surgery for removal of labial frenum and tooth bleaching. Minimally invasive direct restorations were performed in anterior teeth with nanofilled composite resin. Finishing and polishing were done in order to demonstrate anatomy and surface texture of the teeth. In conclusion, the treatment used materials with biomechanical behavior, setting function, harmony of the smile and satisfactory aesthetic result...

Harmonização do sorriso com facetas diretas em resina composta: relato de caso / Smile harmonization with direct composite resin: a case report

Atualmente é possível ter maior previsibilidade do tratamento reabilitador com utilização de materiais com propriedades que biomimetizam os tecidos dentários perdidos. Este trabalho objetiva relatar o caso clínico de um paciente jovem insatisfeito com o aspecto de seu sorriso, o qual apresentava comprometimento do formato e da coloração dos dentes anterossuperiores. Para a reabilitação foram realizados planejamento reverso, com protocolo fotográfico, wax-up e mock-up, clareamento dental externo pela técnica de consultório e reanatomização dentária com facetas diretas em resina composta nos dentes 13 ao 23, pela técnica de estratificação. Em conclusão, esta reabilitação funcional e estética proporcionou ao paciente harmonia em seu sorriso, autoestima e satisfação com o resultado final alcançado...

Currently it is possible to have greater predictability of the rehabilitation treatment, through the use of materials with properties that resemble the lost dental tissue. This work aims to report the case of a young patient unsatisfied with the appearance of her smile, with format change and discoloration of the anterior teeth. For the rehabilitation, a reverse planning was carried out, through the use of a photographic protocol, wax-up and mock-up, external tooth bleaching and direct restorations on teeth #13 to #23, by a layering technique. In conclusion, this functional and aesthetic rehabilitation provided the patient’s smile harmony, self-esteem and satisfaction with the final result achieved...

Transformação do sorriso por meio de fechamento de diastema utilizando resina composta nanoparticulada - relato de caso / Smile transformation through diastema closure using composite nanofilled - case report

A presença de diastema entre os dentes anteriores pode gerar desarmonia do sorriso e comprometer a estética do paciente. Com a evolução dos materiais e das técnicas restauradoras, o fechamento de diastema empregando resinas compostas tornou-se alternativa viável para resolução da maioria dos casos clínicos. Este tratamento permite restabelecer a função, possibilitando os contatos interproximais, bem como restabelecimento da estética, proporcionando um sorriso mais harmônico e agradável. Este artigo tem como objetivo relatar um caso clínico de correção de diastemas nos dentes anteriores superiores, utilizando resina composta nanoparticulada pela técnica direta para restabelecimento funcional e estético. O caso foi acompanhado por quatro anos, sendo realizados alguns reparos ao longo desse tempo, demonstrando que o fechamento de diastema com resina composta ‚ uma técnica viável e confiável, além de apresentar boa longevidade

The presence of anterior diastema can result on smile disharmony and compromise the patient’s aesthetic. The evolution of dental materials and techniques has made the use of composite resin for diastema closure a viable option treatment for most clinical cases. It restores function allowing the interproximal contacts, as well as harmony, reestablishing of the smile’s aesthetic. This clinical report aims at demonstrating the clinical correction of an anterior diastema restoring the functional anatomy and especially aesthetic through nanofilled composite resin restorations. The case was followed for 4-years and some repairs were carried out over this time, demonstrating the reliability and viability of the technique, with good longevity of the treatment