Effect of time and dental substrate on the bond strength of a universal adhesive system: in vitro study / Efeito do tempo e do substrato dental na resistência de união de um sistema adesivo universal: estudo in vitro

Introduction: Dentin adhesives provide union between the dental substrate and composite resin, but this union can be influenced by the cleaning agent. Objective: Evaluate the use of ozonated water as a cavity cleaning solution. Material and method: 40 bovine dental crowns were selected, divided into four groups: AD (dentin cleaning with distilled water) and AO (dentin cleaning with ozonized distilled water). Each group was divided into two storage periods (24h and 30 days) kept at 37 °C. The selected universal system adhesive was employed according to the manufacturer's instructions and light cured for 20 seconds. At that time, three cylinders were made (Tygon matrix with an internal diameter of 2 mm and a height of 2 mm) of composite resin in the crowns in the cervical, médium, and incisal regions and light cured for 30 seconds. After storage, the bonding strength was tested by micro-shear, and fracture type analysis was performed. The data were submitted to statistical analysis using the Shapiro-Wilk test with a significance level of 95%, ANOVA, and Turkey. Result: There was a statistically significant difference between the bond strength values, only in the intergroup analysis for the time of 24 hours, between the middle third of the groups (LDAO24 = 2.70 (± 2.39); LDAO30 = 3.82 (± 2.31)). The predominant fracture type for both groups was an adhesive fracture, except in the medium and incisal thirds of the AD, which was a cohesive dentin fracture. Conclusion: The utilization of ozone did not change the bond strength adhesive.

Introdução: Os adesivos dentinários proporcionam união entre o substrato dental e resina composta, porém esta união pode ser influenciada pelo agente de limpeza. Objetivo: Avaliar a influência na resistência de união (RU) de um sistema adesivo universal associado à da água ozonizada como solução de limpeza cavitária. Material e método: Foram selecionadas 40 coroas de dentes anteriores bovinos divididos em 4 grupos: AD (limpeza dentinária com água destilada) e AO (limpeza dentinária com água destilada ozonizada). Cada grupo foi subdividido em outros dois grupos de acordo com o tempo de armazenamento (24h e 30 dias) armazenados a 37ºC. A limpeza dentinária foi realizada por meio de uma seringa de 60mL de cada solução e fricção por 10 segundos. O sistema adesivo universal selecionado foi aplicado de acordo com as instruções do fabricante e fotoativado por 20 segundos. Em seguida, foram confeccionados 3 cilindros (matriz Tygon com um diâmetro interno de 2 mm e 2 mm de altura) de resina composta nas coroas nas regiões cervical, média e incisal e fotoativados por 30 segundos. Após o armazenamento foi realizado o teste de RU por microcisalhamento e análise do tipo de fratura. Os dados coletados foram submetidos a análise estatística através do teste de Shapiro Wilk com nível de significância de 95%, ANOVA e Tukey. Resultado: Houve diferença estatística significativa entre os valores de RU apenas na análise intergrupos para o tempo de 24 horas, entre o terço médio dos grupos (LDAO24 = 2,70 (± 2,39); LDAO30 = 3,82 (± 2,31)). O tipo de fratura predominante para ambos os grupos em todos os tempos foi de fratura adesiva, com exceção ao terço médio e incisal do AD, que foi fratura coesiva de dentina. Conclusão: A utilização do ozônio não alterou a resistência de união adesiva.

In vitro evaluation of the antibacterial behavior of a self-etch adhesive associated with chlorhexidine / Avaliação in vitro da ação anti-bacteriana de um adesivo auto-condicionante acrescido de clorexidina

Abstract Introduction Adhesive technology has been developed quickly since its introduction about fifty years ago. Its goal is to produce a close contact within enamel and dentin. Failures in this process could result in microleakage, and allow the infiltration of bacteria, fluids and ions. Recent studies have been shown the use of chlorhexidine associated with adhesive systems can be able to inhibit the bacteria action. Objective The aim of this study was to evaluate the addiction of different percentages of chlorhexidine to a self-etch adhesive. Methodology The solution of digluconatechlorhexidine was increased to the primer of the two pass self etch adhesive to create a 0.5%, 1.0% and 2.0% chlorhexidine primer solution and after they were distributed in four groups (G1, G2, G3 and G4). Saliva samples (N=10) were used to test bacteria activity. Result They were spread in a blood medium with filter paper disks containing the different treatments. After the incubation, the inhibitions halos formation were evaluated. Conclusion This study demonstrated that, in vitro, the addition of different percentages of chlorhexidine digluconate to the self-etch adhesive induced inhibited halos at bacteria of saliva samples, independent from their concentration.

Resumo Introdução A tecnologia adesiva vem se desenvolvendo rapidamente desde que foi introduzida há mais de 50 anos. O principal objetivo da adesão é alcançar um íntimo contato entre a estrutura dental e o material restaurador e fornecer adequada união entre o esmalte e a dentina. Objetivo A proposta deste estudo foi avaliar o efeito antibacteriano de um adesivo auto-condicionante de dois passos associado a diferentes concentrações de solução de digluconato de clorexidina (DCHX). Metodologia A solução de digluconato de clorexidina a 20% foi adicionada ao primer do sistema adesivo nas concentrações de 0,5, 1,0 e 2,0% e distribuídas em quatro grupos (G1, G2, G3 e G4). Para o teste de atividade antibacteriana foram utilizadas amostras de saliva (N=10) semeadas em meio de ágar sangue e discos de papel filtro contendo os diferentes grupos. Após incubação, as amostras foram inspecionadas quanto à formação de halo de inibição dos microrganismos através da utilização do paquímetro digital de precisão (0,0001mm) (Mitutoyou Sul Americana Ltda/ Starret Tools ®). Resultado Halos de inibição foram encontrados ao redor de todos os discos de filtro em que foram aplicados o primer acrescido de clorexidina mais o adesivo, bem como ao redor dos discos do controle positivo. Ao redor dos discos do controle negativo e dos discos com primer e adesivo não modificado não foram observados halos de inibição. Conclusão Este trabalho demonstrou que, in vitro, a adição de diferentes concentrações de digluconato de clorexidina ao sistema adesivo produziu halo de inibição dos microrganismos presentes nas amostras de saliva, independente da concentração utilizada.

The influence of three photoactivation techniques on the sorption and solubility of different composite resins / A influência de três técnicas de fotoativação na sorção e solubilidade de diferentes resinas compostas

Introduction: There is a growing demand for aesthetic restorations and the polymerized composite resins are the most used material in these procedures. In order to achieve greater resistance to solubilization proper polymerization is required. Objective: Evaluate the influence of three photoactivation techniques, on sorption and solubility of three composite resins. Materials and methods: 90 test samples measuring 8 mm diameter and 1 mm thick were made and divided into 9 groups (n=10) of resins -Filtek Z350 XT, Tetric N-Ceram and IPS Empress Direct, each of them was polymerized with LED Bluephase, using the techniques: Conventional, Soft-Start (SS) and Pulse Delay (PD). Afterwards they were placed in desiccator with silica gel at 98.6 F and weighed daily until obtaining a constant mass (m1). Then they were immersed in deionized water for seven days and weighed again (m2). The test sample reconditioning was performed using the m1 procedure, until a constant mass (m3 ) was obtained. The sorption and solubility values were calculated and subjected to ANOVA test (two-way), followed by Tukey post hoc, p<0.05. Result: There were no statistically significant differences in sorption and solubility among the studied resins when photoactivation techniques were compared. For solubility analysis, statistically significant differences were observed among the materials. The results for composite resin Filtek Z350 XT presented higher statistical hybridization values than those of the other evaluated resins. Conclusion: The different forms of photoactivation had no influence on the sorption and solubility of the tested composite resins.

Introdução: Há uma crescente demanda por restaurações estéticas, sendo as resinas compostas polimerizadas o material mais utilizados nesses procedimentos. Visando uma maior resistência à solubilização, uma polimerização adequada é necessária. Objetivo: Avaliar a influência de três técnicas de fotoativação na sorção e na solubilidade de três resinas compostas. Material e método: Foram confeccionados 90 corpos-de-prova, com 8 mm de diâmetro e 1 mm de espessura, divididos em 9 grupos (n = 10) de resinas - Filtek Z350 XT, Tetric N-Ceram e IPS Empress Direct, cada uma elas polimerizada com LED Bluephase, utilizando as técnicas: Convencional, Soft-Start (SS) e Pulse Delay (PD). Posteriormente foram colocadas em dessecador com sílica gel a 98,6 F e pesadas diariamente até obtenção de massa constante (m1). Depois foram imersos em água desionizada durante sete dias e pesados ​​novamente (m2). O recondicionamento da amostra de teste foi realizado utilizando o procedimento m1, até que uma massa constante (m3) fosse obtida. Os valores de sorção e solubilidade foram calculados e submetidos ao teste ANOVA (two-way), seguido por Tukey post hoc, p <0,05. Resultado: Não houve diferenças estatisticamente significantes para sorção e solubilidade nas resinas estudadas quanto as técnicas de fotoativação. Para análise de solubilidade, foram observadas diferenças estatisticamente significantes entre os materiais. Os resultados para resina compostaFiltek Z350 XT apresentaram valores de hibridação estatísticos superiores aos das outras resinas compostas avaliadas. Conclusão: As diferentes formas de fotoativação não influenciaram a sorção e solubilidade das resinas compostas testadas.

Restaurações cerâmicas multicamadas e monolíticas: uma revisão de literatura / Multilayered and monolithic ceramic restorations: a literature review

Objetivo: realizar uma revisão de literatura sobre materiais, técnicas de confecção, vantagens, desvantagens e limitações das restaurações cerâmicas multicamadas e monolíticas. Revisão de literatura: embora as cerâmicas odontológicas sejam utilizadas para confecção de restaurações dentárias indiretas, porque têm excelentes propriedades mecânicas e estéticas, são materiais susceptíveis à fratura sob forças oclusais. Para compensar essa fragilidade, restaurações multicamadas são confeccionadas associando um material mais resistente para a infraestrutura e a posterior aplicação de cerâmica para recobrimento estético. Porém, as restaurações multicamadas apresentam como desvantagem o possível lascamento da cerâmica de recobrimento. Essas falhas comprometem a restauração funcional e a estética, exigindo a substituição da peça protética em muitos casos. Sendo assim, devido à evolução de sistemas cerâmicos e técnicas de processamento, surgiram as restaurações cerâmicas monolíticas fabricadas com um único material, a fim de superar tal limitação. Nesse sentido, diferentes materiais e técnicas são apresentados na literatura para a confecção de restaurações cerâmicas monolíticas. Considerações finais: as restaurações multicamadas têm bom resultado estético, porém podem apresentar lascamento da cerâmica de recobrimento. Essa limitação é superada pelo uso de um único material para as restaurações monolíticas, mas o resultado estético pode ser limitado. De um modo geral, a literatura demonstra um bom comportamento clínico para as restaurações cerâmicas multicamadas e monolíticas, quando a técnica de confecção e o sistema cerâmico são bem indicados. (AU)

Objective: the aim of this study was to conduct a literature review about the materials, techniques, advantages, disadvantages and limitations of multilayer and monolitic ceramic restorations. Literature review: although dental ceramics have been used for fabrication of dental restorations due to its good esthetic and mechanical properties, it is a material prone to fracture under oclusal loading. To surpass such fragility, multilayer restorations are fabricated using a resistant framework material associated to esthetic veneering ceramic. However, multilayer restorations present risk to chipping of veneering ceramic. Those failures represent a functional and esthetic problem, leading to restoration replacement. So, the evolution of ceramic systems and techniques generated monolitic restorations using a single material. Several materials and techniques are presented in the literature for fabrication of monolitic ceramic restorations. Final considerations: multilayer restorations present good esthetic result but delamination of veneering ceramic can occur. Such limitation is solved using a single material in monolitic restorations, but esthetic result is limited. In general, literature shows appropriate clinical performance for both multilayer and monolitic ceramic restorations when technique and materials are well indicated. (AU)

Influência da solução de irrigação sobre a resistência adesiva de um cimento resinoso de dupla polimerização / Influence of solution of irrigation on the resistance of and adhesive resin cement double polymerization

Objetivo: Avaliar a influência de diferentes soluções de irrigação cavitária sobre a resistência de união de um cimento resinoso de dupla polimerização. Material e Método: A partir de incisivos bovinos, foram obtidos 4 grupos (n=15), divididos aleatoriamente de acordo com a solução irrigadora empregada na limpeza cavitária, sendo: G0 - soro fisiológico + condicionamento ácido; G1 ­ EDTA + condicionamento ácido; G2 - Clorexidina 2% + condicionamento ácido + clorexidina 2% e G3 - soro fisiológico + condicionamento ácido + clorexidina 2%. Foram confeccionados cilindros de cimento resinoso para cada coroa, utilizando-se uma matriz de Tygon com diâmetro interno de 1 mm e altura de 2 mm. O teste de resistência adesiva por microcisalhamento foi realizado após 3 meses de armazenamento dos espécimes em soro fisiológico a 37ºC. Os dados foram submetidos ao teste de Kruskall-Wallis, seguido do teste de Dunn (p<0,05). Resultados: Os grupos G0, G1 e G3 não apresentaram diferenças significativas entre si (p>0,05). Os menores valores foram observados no grupo G2 (p<0,05). Conclusões: As soluções irrigadoras EDTA e soro fisiológico utilizadas previamente ao condicionamento ácido da dentina não interferiram, significativamente, na resistência de união, porém, a solução de clorexidina utilizada após o condicionamento ácido influenciou negativamente nos valores de resistência de união.

Objectives: This study aimed to evaluate the influence of different cavity irrigation solutions on the bond strength of a dual-curing resin cement. Methods: From bovine incisors, 4 groups (n=15), were randomly divided according to the irrigating solution for cavity cleaning: G0 ­ saline + acid etching; G1 ­ EDTA + acid etching; G2: Chlorhexidine 2% + acid etching + Chlorhexidine 2%; and G3 ­ Saline + acid etching + Chlorhexidine 2%. Resin cement cylinders were made for each crown, using a Tygon matrix with internal diameter of 1 mm and height of 2 mm. The specimens were stored for 3 months at 37oC, and then subjected to microshear tests. Data were statistically analyzed by Kruskal-Wallis test followed by Dunn (p<0.05). Results: There were no statistically significant differences between G0, G1 and G3 groups (p>0.05). The lowest values were observed in G2 group (p<0.05). Conclusion: The irrigation solutions EDTA and saline used before to the acid etching of dentin did not interfere, significantly, in the bond strength, however, the solution of chlorhexidine used after the acid etching influenced negatively.

Avaliação da influência da solução de irrigação na resistência adesiva de um cimento resinoso / Evaluation of influence of irrigation solution in strength adhesive of a resin cement

Introdução: A contaminação do substrato dentinário pode interferir na qualidade de união entre materiais adesivos e o dente. Objetivo: Investigar a influência de diferentes soluções de irrigação na resistência de união de um cimento resinoso. Material e Método: Foram selecionadas 40 coroas dentais bovinas, divididas em quatro grupos: G0 = soro; G1 = clorexidina; G2 = EDTA; G3 = clorexidina 0,12%, após condicionamento ácido. Em seguida, foram confeccionados cilindros de cimento resinoso utilizando-se uma matriz de Tygon com diâmetro interno de 1 mm e 2 mm de altura. A fotoativação foi realizada por aparelho de luz LED com 900 mW/cm² por 40 segundos. Foram confeccionados quatro cilindros de cimento resinoso para cada coroa bovina, totalizando 40 corpos de prova de cimento resinoso para cada grupo avaliado. O teste de resistência adesiva por microcisalhamento foi realizado após 24 horas. Decorrido esse período, os cilindros de cimento resinoso foram testados em uma máquina universal de ensaios (EMIC). Os dados obtidos foram submetidos à análise estatística pelos testes ANOVA e Tukey (p = 0,001). Resultado: Não houve diferenças estatisticamente significativas entre os grupos estudados, com exceção para o G3, que apresentou de forma significativa os menores valores de resistência adesiva. Conclusão: As diferentes soluções irrigadoras utilizadas previamente ao condicionamento ácido na dentina não interferem na resistência de união por microcisalhamento.

Introduction: The contamination of dentin can interfere with the quality of union between adhesives and tooth. Objective: Was to investigate the influence of different irrigation solutions on bond strength of a resin cement. Material and Method: Were selected 40 dental bovine crowns divided into four groups: G0= physiologic serum, G1= chlorhexidine, G2= EDTA, G3= 0.12% chlorhexidine after acid etching. Then the cylinders were fabricated resin cement using a matrix of Tygon with an internal diameter of 1mm and 2mm in height. The polymerization was carried out by LED light unit with 900 mW/cm² for 40 seconds. 4 cylinders were made of resin cement for each bovine crown, totaling 40 body-of-proof resin cement for each group evaluated. The test microshear bond strength was performed after 24 hours. After this period, the resin cement cylinders were tested in a universal testing machine (EMIC). Data were statistically analyzed by ANOVA and Tukey (p = 0.001). Result: There were no statistically significant differences between groups, except for the G3 which showed significantly lower values of bond strength. Conclusion: The different irrigating solutions used prior to etching dentin not interfere in the bond strength microshear.

Desensitizing treatments for dentin hypersensitivity: a randomized, split-mouth clinical trial

The aim of this randomized, controlled, split-mouth, clinical study was to differentiate and clinically qualify the effectiveness of different desensitizing agents in the treatment of painful symptoms caused by cervical dentin hypersensitivity (CDH). Two hundred-and-fifty-two teeth of 42 patients were distributed into seven groups (n = 36): G1 - placebo; G2, G3, G4 and G6 - fluoride varnishes; G5 - sodium fluoride; G7 - potassium oxalate. Three applications were made one week apart. A three-score system (Alfa = 0, Bravo = 2, and Charlie = 3, respectively for no sensitivity, slight sensitivity and high sensitivity) was used to assess CDH after each application and after 30 days. The data were subjected to statistical analysis using the Kruskall-Wallis and Dun tests. After the second week, statistically significant differences were observed for all materials compared with the baseline. After 30 days, Group G7 had presented a significant gradual reduction along all the evaluated time intervals. It was concluded that all the desensitizing agents were capable of reducing dentin hypersensitivity, with the exception of the placebo and the sodium fluoride groups.

Avaliação da sorção e solubilidade de uma resina composta em diferentes meios líquidos / Sorption and solubility assessment of a resin composite in different liquids

Este trabalho avaliou a sorção e a solubilidade de uma resina composta nanoparticulada em três meios líquidos diferentes: água destilada, Coca-Cola® e etanol/água a 75%, em função de dois períodos de armazenamentos: 7 e 15 dias. Foram confeccionados 30 espécimes, acondicionados em sílica gel azul, desidratada a 37°C, por 24 horas. Em seguida, foram pesados em balança analítica de precisão, repetindo-se até que se obtivesse massa constante (m1). Com a obtenção da m1, os espécimes foram subdivididos em 6 grupos e armazenados na solução. Três grupos permaneceram por 7 dias, e os outros três, por 15 dias. Após o período de armazenamento, os espécimes foram removidos, lavados, secos, pesados para a obtenção de uma segunda medida de massa, denominada m2. Os espécimes foram, então, recondicionados em estufa a 37°C. Mensurações de massa foram realizadas durante a desidratação, a cada 24 horas, obtendo-se a m3. Os dados de sorção e solubilidade foram calculados e submetidos à análise estatística. A resina nanoparticulada mostrou-se resistente à degradação química em meio ácido e em meio aquoso, mas foi suscetível à degradação, quando imerso em solução de etanol/água a 75%, apresentando solubilidade, sem diferença estatística entre os períodos de armazenamento.

This study evaluated the sorption and solubility of resin composite nanoparticle in three different liquid : distilled water, Coca-Cola ® and ethanol / water at 75%, according two periods of stores: 7 and 15 days. We prepared 30 specimens, packed in plastic container containing silica gel blue dehydrated and taken to an incubator at 37 ° C for 24 hours. Following, we weighed in analytical balance, and repeated until achieving constant mass (m1) on every 24 hour period. By getting the m1, the specimens were been divided into six groups and stored separately in 5 mL of each solution. Three groups were been maintained for 7 days and the other three for 15 days. After the storage period, the specimens were removed, washed, dried, weighed to obtain a second measure of mass, called m2. The specimens was reconditioned at 37 ° C. Mass measurements were performed during dehydration, every 24 hours, getting the dough reconditioned, with constant value of mass, called m3. The Data from sorption and solubility, we calculated and subjected to statistical analysis. The composite resin Filtek Z350 was found to be resistant to chemical degradation in acid and aqueous, but was susceptible to degradation when immersed in a solution of ethanol / water at 75%, with solubility, no statistical difference between the periods of storage.

Planejamento estético do sorriso: relato de caso clínico / Planning the esthetic smile: a case report

A beleza e a harmonia das restaurações odontológicas estão controladas por alguns fatores que servem de parâmetros e auxiliam na reconstrução de um sorriso, a estes fatores chamamos de princípios estéticos. O objetivo deste trabalho foi descrever um caso clínico elucidando os principais princípios estéticos e ao mesmo tempo observando que estãotodos interligados para a obtenção de um resultado estético satisfatório. Foi possível concluir com este relato de caso clínico, a devolução da harmonia do sorriso sobre o ponto de vista estético e funcional.

The beauty and harmony of dental restorations are controlled by several factors that serve as parameters and help in the reconstruction of a smile, and these factors are called esthetic principles. The aim of this study was to describe a clinical case elucidating the main esthetic principles, and at the same time, observe that they are all interconnected in order to obtain a satisfactory esthetic result. Through this Clinical Case Report it was possible to conclude restoration of the harmony of the smile from the esthetic and functional points of view.

Aspectos clínicos da técnica de preparo e restauração onlay de porcelana em dentes posteriores / Clinical aspects of the technique for porcelain onlay preparation and restoration in posterior teeth

Este trabalho é uma revisão bibliográfica sobre as características dos preparos e restaurações do tipo onlay de porcelana em dentes posteriores. Tem por intenção relatar as indicações, contraindicações, vantagens e desvantagens das restaurações onlay de porcelana e dos preparos onlay para porcelana - com suas respectivas configurações e técnica de preparo, todos baseados em princípios biomecânicos -, para promover um melhor diagnóstico e indicação dessa técnica pelos cirurgiões-dentistas. O aspecto estético do tratamento dentário torna-se cada vez mais importante para o paciente, o dentista deve estar consciente das aplicações e limitações das restaurações estéticas adesivas onlay de porcelana disponíveis para dentes posteriores para obter sucesso clínico a curto, médio e longo prazo. O aparecimento de novos e melhores materiais restauradores que atendem à demanda estética, mecânica e biológica cada vez mais supera limitações dos materiais antecessores. Esse é o caso das porcelanas, que, com o passar do tempo, têm sofrido alterações na sua composição a fim de melhorar suas propriedades e, dessa maneira, superar suas eventuais desvantagens. Assim, é possível prever para o futuro materiais que superem as presentes limitações e contraindicações daqueles atualmente disponíveis, ampliando ainda mais a indicação e sucesso clínico das restaurações onlay de porcelana para dentes posteriores.

Influência da luz de cura Diferentes Unidades de Resistência de União de restaurações de resina Composta indireta

O Objetivo Deste estudo da UM Foi avaliar Influência de Diferentes fontes de luz Sobre a Resistência adesiva de resina Composta de restaurações indiretas cimentadas com cimento resinoso dual hum . A dentina superficial de Terceiros molares Humanos Foi exposto e ácido - Gravado e hum Sistema Adesivo Foi aplicado (Single Bond 2 ). Quatro mm de espessura de resina Composta de restaurações indiretas ( GRADIA ) foram confeccionadas e cimentadas com cimento resinoso UM dual (Rely X). Quatro fontes de luz Foram utilizados Parágrafo polimerizar o cimento : QTH - Optilux 401; LED1 - LEDemetron 1; LED2 - Optilight CL e LED3 - Ultralume 5. Os dentes Por armazenados Foram 24 horas e seccionados , produzindo espécimes em forma de n com Bastão grupo CADA área aderida de 1,0 mm ². Os espécimes Foram então testados em Uma Máquina Universal de Ensaios , a Uma Velocidade de 1 mm / min. Os Dados Foram analisados Usando ANOVA. Bond Força Os valores médios foram: QTH : 22,5 (± 8,4 ); LED1 : 22,7 (± 9,4 ); LED2 : 21,4 (± 10,2 ) e 27,3 LED3: (± 13,8 ). Não Houve diferença estatisticamente significativa Entre os Grupos experimentais . A resistência de União Valores QUANDO o cimento com Diferentes Foi Luzes LED polimerizada Foram equivalentes EAo QUANDO valores de Uma luz QTH Foi Utilizada . Pode-se concluir Que A variedade de fontes de luz Não Utilizadas presente estudo , Não influenciou Uma Resistência de União de resina Composta de restaurações indiretas cimentadas com cimento resinoso dual Zumbido

Influence of different light curing units on the bond strength of indirect resin composite restorations

The aim of this study was to evaluate the influence of different light sources on the bond strength of indirect resin composite restorations cemented with a dual-cure resin cement. The superficial dentin of human third molars was exposed and acid-etched and an adhesive system was applied (Single Bond 2). Four-mm-thick indirect resin composite restorations (Gradia) were fabricated and cemented using a dual-cure resin cement (Rely X). Four light sources were used to polymerize the cement: QTH - Optilux 401; LED1 - L.E.Demetron 1; LED2 - Optilight CL; and LED3 - Ultralume 5. The teeth were stored for 24 h and then sectioned, yielding stick-shaped specimens for each group with a bonded area of 1.0 mm². The specimens were then tested in a universal testing machine, at a crosshead speed of 1 mm/min. Data were analyzed using ANOVA. Bond strength mean values were: QTH: 22.5 (± 8.4); LED1: 22.7 (± 9.4); LED2: 21.4 (± 10.2); and LED3: 27.3 (± 13.8). No statistically significant difference was observed among the experimental groups. The bond strength values when the cement was polymerized using different LED lights were equivalent to the values when the QTH light was used. It can be concluded that the variety of light sources used in the present study did not influence the bond strength of indirect resin composite restorations cemented with a dual-cure resin cement.