RESUMEN
Abstract Regular use of toothpaste with fluoride (F) concentrations of ≥ 1000 ppm has been shown to contribute to reducing caries increment. However, when used by children during the period of dental development, it can lead to dental fluorosis. Objective: In this study, we aimed to evaluate the in vitro effect of a toothpaste formulation with reduced fluoride (F) concentration (200 ppm) supplemented with sodium trimetaphosphate (TMP: 0.2%), Xylitol (X:16%), and Erythritol (E: 4%) on dental enamel demineralization. Methodology: Bovine enamel blocks were selected according to initial surface hardness (SHi) and then divided into seven experimental toothpaste groups (n=12). These groups included 1) no F-TMP-X-E (Placebo); 2) 16% Xylitol and 4% Erythritol (X-E); 3) 16% Xylitol, 4% Erythritol and 0.2%TMP (X-E-TMP); 4) 200 ppm F (no X-E-TMP: (200F)); 5) 200 ppm F and 0.2% TMP (200F-TMP); 200 ppm F, 16% Xylitol, 4% Erythritol, and 0.2% TMP (200F-X-E-TMP); and 7) 1,100 ppm F (1100F). Blocks were individually treated 2×/day with slurries of toothpastes and subjected to a pH cycling regimen for five days (DES: 6 hours and RE: 18 hours). Then, the percentage of surface hardness loss (%SH), integrated loss of subsurface hardness (ΔKHN), fluoride (F), calcium (Ca), and phosphorus (P) in enamel were determined. The data were analyzed by ANOVA (1-criterion) and the Student-Newman-Keuls test (p<0.001). Results: We found that the 200F-X-E-TMP treatment reduced %SH by 43% compared to the 1100F treatments (p<0.001). The ΔKHN was ~ 65% higher with 200F-X-E-TMP compared to 1100F (p<0.001). The highest concentration of F in enamel was observed on the 1100F treatment (p<0.001). The 200F-X-E-TMP treatment promote higher increase of Ca and P concentration in the enamel (p<0.001). Conclusion: The association of 200F-X-E-TMP led to a significant increase of the protective effect on enamel demineralization compared to the 1100F toothpaste.
RESUMEN
Abstract Dental applications based on the unique characteristics of amorphous calcium phosphate stabilized by casein phosphopeptides (CPP-ACP) have been proposed, as well as the improvement of its properties. Objectives: The objective of this study was to determine the ability of topically applied CPP-ACP from a commercial product to remineralize subsurface lesions when applied for extended periods of time (3 h and 8 h). Material and Methods: Artificially induced carious lesions were produced in 50 bovine enamel blocks previously selected by surface hardness. After treatments with gel without F and CPP-ACP applied for 1 minute (Placebo); 2% NaF neutral gel applied for 1 minute (Fluoride 1 min); CPP-ACP applied for 3 min (ACP 3 min); and CPP-ACP applied for 3 h (ACP 3 h) and for 8 h (ACP 8 h), the enamel blocks were submitted to the remineralization pH-cycling. Surface hardness and synchrotron micro-tomography were used to determine the percentage of surface hardness recovery (%SHR) and to calculate mineral concentration (gHAp.cm−3), respectively. The data were submitted to ANOVA followed by the Student-Newman-Keuls test (p<0.05). Results: Fluoride gel presented higher %SHR followed by ACP 3 min (p<0.001). No difference (p = 0.148) was found for Placebo, ACP 3 h and ACP 8 h groups for %SHR. Fluoride gel showed greater mineral concentration (p<0.001) when compared with the other groups. ACP 3 min demonstrated a significant difference (p<0.001) from ACP 3 h and ACP 8 h. The ACP 3 h and 8 h presented a subsurface lesion with development of laminations in all blocks. Conclusion: In this in vitro study the use of CPP-ACP for extended periods of time did not produce an additive effect in the remineralization process.