Effects of air-polishing powders on color stability of composite resins

OBJECTIVES: The purpose of this study was to investigate the effect of different air-polishing powders on the color stability of different types of composite resin restorative materials. MATERIAL AND METHODS: Thirty cylindrical specimens (15×2 mm) were prepared for each of 7 composite resin restorative materials. All specimens were polished with a series of aluminum oxide polishing discs (Sof-Lex). The prepared specimens of each composite resin were randomly divided into 3 groups of 10 specimens each, for control (Group-C) and two air-powder applications (Group-CP: Cavitron Prophy-Jet; Group-PS: Sirona ProSmile prophylaxis powder). A standard air-polishing unit (ProSmile Handly) was used. All specimens were air-powdered for 10 s at 4-bar pressure. The distance of the spray nosel from the specimens was approximately 10 mm and angulation of the nosel was 90°. Specimens were stored in 100 mL of coffee (Nescafe Classic) for 24 h at 37°C. Color measurement of all specimens was recorded before and after exposure to staining agent with a colorimeter (Minolta CR-300). Color differences (∆E*) between the 2 color measurements (baseline and after 24 h storage) were calculated. The data were analyzed with a 2-way ANOVA test, and mean values were compared by the Tukey HSD test (p<0.05). RESULTS: According to the 2-way ANOVA results, composite resin restorative materials, air-polishing powders, and their interaction were statistically significant (p<0.05) For Aelite Aesthetic Enemal, Filtek Z250, Grandio, CeramX Mono, and Quixfil composite resin restorative materials, no significant difference was observed between Group-PS and Group-CP (p>.05) and these groups demonstrated the highest ∆E* values. For Filtek Silorane and IntenS, the highest ∆E* values were observed in Group-PS. The lowest ∆E* values for all composite resin groups were observed in Group-C. When comparing the 7 composite resin restorative materials, Aelite Aesthetic Enemal demonstrated significantly less ∆E* values than the other composite resins tested. The highest ∆E* values were observed in Quixfil. CONCLUSION: Except for Quixfil, all control groups of composite resins that were polished Sof-Lex exhibited clinically acceptable ∆E values (<3.7). Air-polishing applications increased the color change for all composite resin restorative materials tested. Composite restorations may require re-polishing after air-polishing.

Effects of different polishing techniques on the surface roughness of dental porcelains

OBJECTIVE: The purpose of this study was to evaluate the effects of different polishing techniques on the surface roughness of dental porcelains. MATERIAL AND METHODS: Fifty-five cylindirical specimens (15x2 mm) were prepared for each feldspathic (Vita VMK 95, Ceramco III) and low-fusing dental porcelain (Matchmaker). Fifty-five specimens of machinable feldspathic porcelain blocks (Vitablocs Mark II), (12x14x18 mm) were cut into 2-mm-thick slices (12x14 mm) with low speed saw. The prepared specimens were divided into 11 groups (n=5) representing different polishing techniques including control ((C) no surface treatment), glaze (G) and other 9 groups that were finished and polished with polishing discs (Sof-Lex) (Sl), two porcelain polishing kits (NTI (Pk), Dialite II (Di)), a diamond polishing paste (Sparkle) (Sp), a zirconium silicate based cleaning and polishing prophy paste (Zircate) (Zr), an aluminum oxide polishing paste (Prisma Gloss) (Pg), and combinations of them. The surface roughness of all groups was measured with a profilometer. The data were analyzed with a 2-way analysis of variance, and the mean values were compared by the Tukey Honestly Significant Difference test (a=0.05). RESULTS: For all porcelain material groups, the lowest Ra values were observed in Group Gl, Group Sl, Group Pk, and Group Di, which were not significantly different from each other (p>0.05).When comparing the 4 different porcelain materials, the machinable feldspathic porcelain block group (Mark II) demonstrated statistically significantly less Ra values than the other porcelain materials tested (p<0.05). No significant difference was observed between the VMK 95 and Ceramco III porcelain groups (p=0.919), also these groups demonstrated the highest Ra values. CONCLUSION: Subjected to surface roughness, the surfaces obtained with polishing and/or cleaning-prophy paste materials used alone were rougher compared to the surfaces finished using Sof-lex, Dialite, ...

Effects of polishing procedures on color stability of composite resins

The purpose of this study was to investigate the effect of different polishing methods on color stability of posterior, universal and nanohybrid composite resin restorative materials upon exposure to a staining agent. Twenty-five specimens were prepared for each of 5 different composite resins (Filtek Z250, Filtek P60, Quadrant LC, Grandio and Filtek Supreme). Specimens were divided into 5 groups and different polishing procedures, including polishing discs (Pd), polishing discs then diamond polishing paste (PdP), polishing discs then a liquid polishing system (Biscover) (PdB), and combinations of these (PdPB) were used. Unpolished specimens served as the control (C). The specimens were stored for 48 h in a coffee solution. The color of all specimens was measured before and after exposure with a colorimeter, and total color change (DE*) were calculated. The data were analyzed with a two-way ANOVA and the means were compared by Tukey HSD test (a=0.05). The lowest color difference was observed in the groups PdP and C, while the highest color difference was observed in PdPB, and PdB. When comparing the five different restorative materials, no significant difference was observed between FiltekP60 and FiltekZ250, and these materials demonstrated significantly less color change than Quadrant LC and the nanohybrid materials (Grandio, Filtek Supreme). The posterior (Filtek P60) and universal (Filtek Z250) composite resin restorative materials, which do not contain tetraethyleneglycol dimethacrylate (TEGDMA), were found to be less stainable than the nanohybrid (Grandio, Filtek Supreme) and universal (Quadrant LC) composite resins, which contain TEGDMA. The use of diamond polishing paste after polishing with polishing discs significantly decreased staining when compared to the groups that used polishing discs alone, for all restorative materials tested. The highest color change values were obtained for the specimens that were polished with the...