RESUMEN
This study aimed to investigate whether pre-curing the universal adhesives affect the resin bonding to zirconia ceramic. Two commercial universal adhesives (All-Bond Universal, ABU; Single Bond Universal Adhesive, SBU) were tested in comparison with a conventional zirconia primer (Z-Prime Plus, ZPP). Air-abraded zirconia specimens were divided into six groups, to which different priming agents were applied with or without photo-polymerization. After resin cylinders were built on the primed zirconia surface using a resin cement (Duo-Link), all bonded specimens were stored in water at 37℃ for 24 hours and half of them (n = 12) were additionally thermocycled 5,000 times. A shear bond strength test was performed at a crosshead speed of 0.5 mm/minute and failure modes were assessed using an optical microscope at 25× magnification. Before thermocycling, the light-cured specimens of ABU and SBU showed higher bond strengths than the uncured ones of the materials (p 0.05). After thermal aging, there were significant decreases in the bond strength for all specimens treated with the universal adhesives (p 0.05) and attained higher bond strength values for both the pre-cured and uncured specimens when compared to the two universal adhesives (p<0.05). Adhesive failures were predominant in all test groups and thermocycling resulted in the higher incidences of adhesive failures for the uncured groups, which was not shown in the pre-cured groups.