RESUMEN
Objective: Ceramic inlays are bonded to tooth structure with resin cements. During the resin cement setting, shrinkage stress develops at the interfaces. During tooth preparation, the undercut areas formed due to the different patterns of caries progression can either be blocked out before taking impression with suitable cement such as glass ionomer cement, or before making the final restoration in the laboratory. Then, the relieved space will be filled with luting cement in clinic. The aim of this study was to compare these two methods of undercut filling in term of stress distribution in the ceramic inlay. Materials and Methods: An axisymmetric finite element analysis was performed to study the stress distribution during inlay cementing. The solid model was generated from a longitudinal section of maxillary premolar in which a class I cavity with 60 degree undercut at the preparation wall and 20 degree divergence of the vertical walls was prepared. A thermal model was used to simulate the polymerization shrinkage of the resin cement. Finite element analysis was carried out in ANSYS environment. Results: Filling the undercut by glass ionomer cement decreased the stress concentration at the ceramic/cement interface. The dominant normal stress at the tooth cement interface in absence of glass ionomer cement was tensile with maximum of 30 Mpa. Using glass ionomer, cement developed stresses with different compressive and tensile signs. With increasing the thickness of resin cement (100 μm, 150 μm, 200 μm), the stress increased. Conclusion: Cements with minimum shrinkage and as thin layer as possible should be used. Filling the undercut with glass ionomer cement decreases the stress. Other experimental and clinical studies must follow this research.